Selected aspects of production and characterization of layered biopolymer composite bonded with a cellulose-based binder

Dasiewicz Julia, Kowaluk Grzegorz

Annals of Warsaw University of Life Sciences - SGGW. Forestry and Wood Technology

|

2022

|

No. 119

24--34

EN

Selected aspects of production and characterization of layered biopolymer composite bonded with a cellulose-based binder. This project aimed to study the possibility of using regenerated cellulose for gluing a layered composite. In the scope of research have been produced different variants of layered composite differ in wood species and pressing time. The produced composite has been characterized according to selected mechanical and physical properties. The prepared samples have been referred to as those bonded with industrial MUF resin. Obtained results proved that regenerated cellulose can be used as a bonding agent. Furthermore, the tests confirmed an improvement in mechanical and physical properties after the bonding of the regenerated cellulose.

PL

Wybrane aspekty wytwarzania i charakterystyka warstwowego kompozytu biopolimerowego wiązanego spoiwem na bazie celulozy. Celem badań było określenie możliwości wykorzystania regenerowanej celulozy do klejenia kompozytu warstwowego. W ramach badań wykonano różne warianty kompozytu warstwowego różniące się gatunkiem drewna i czasem prasowania. Wytworzony kompozyt scharakteryzowano zgodnie z wybranymi właściwościami mechanicznymi i fizycznymi. Uzyskane wyniki dowiodły, że regenerowana celuloza może być stosowana jako spoiwo. Ponadto badania potwierdziły poprawę właściwości mechanicznych i fizycznych po użyciu regenerowanej celulozy w kompozytach warstwowych.

2

Zestalanie zużytych płuczek wiertniczych – próba półprzemysłowa

Steliga T., Uliasz M., Jakubowicz P., Szajna A.

Nafta-Gaz

|

2018

|

R. 74, nr 11

821--827

PL

W artykule przedstawiono wyniki badań laboratoryjnych zestalania płuczek bentonitowych i beziłowych polimerowych pod kątem dobru rodzaju i optymalnej ilości środka wiążącego oraz badania otrzymanego zestalonego półproduktu. Przy zestalaniu płuczki ważny jest dobór środków wiążących, których zadaniem jest takie przekształcenie suspensji płuczki wiertniczej w ciało stałe o odpowiedniej wytrzymałości mechanicznej, aby w jak największym stopniu ograniczyć wymywanie się z niego substancji niebezpiecznych występujących w postaci związków rozpuszczalnych. W wyniku tych badań wytypowano zestaw środków stanowiących kompozycję na bazie cementu portlandzkiego CEM I 32,5 lub spoiwa hydraulicznego – Silment CQ-25 w ilości 20÷35% zawierającą 4÷5% szkła wodnego sodowego. O wyborze tych środków zdecydowały ich właściwości chemiczne i wpływ na właściwości mechaniczne ciała stałego powstałego po zestaleniu płuczki otworowej. W celu weryfikacji opracowanej technologii zestalania zużytych płuczek wiertniczych przeprowadzono próbę w skali półprzemysłowej. Zestalony półprodukt poddano badaniom pod kątem wytrzymałości na ściskanie – po 7 dniach wytrzymałość wynosiła 0,9 MPa, a po 14 dniach – 1,9 MPa. Przeprowadzone badania wymywalności substancji szkodliwych w odcieku z półproduktu wykazały następujące wartości oznaczeń: stałe związki rozpuszczone (TDS) – 58 424 mg/kg s.m., chlorki Cl− – 21 300 mg/kg s.m., siarczany – 1984 mg/kg s.m., ogólny węgiel organiczny (DOC) – 3200 mg O2/kg s.m., zawartość metali ciężkich – na niskim poziomie. Spośród wykonanych oznaczeń jedynie zawartość węgla organicznego (DOC) przekroczyła graniczne wartości wymywania (Dz.U. z 2015 r., poz. 1277, załącznik nr 5), co mogło być spowodowane obecnością polimerów organicznych zawartych w składach zestalonych płuczek oraz zanieczyszczających je substancji ropopochodnych. Ponadto wykonano badania toksykologiczne odcieku z zestalonego półproduktu z wykorzystaniem wytypowanych testów toksykologicznych. Toksyczność wyrażona w jednostkach toksyczności (TU) w wytypowanych do badań testach wynosiła: Microtox – 4,3; Daphtoxkit (48 h) – 9,9; Spirodela – 9,5. Odciek z półproduktu można zaliczyć do niskotoksycz- nych (II klasa toksyczności, TU < 10). Prezentowana technologia została objęta ochroną patentową nr P.418959 pt.: Sposób zestalania zużytych wodnodyspersyjnych płuczek wiertniczych typu bentonitowego i polimerowego.

EN

The article presents results of laboratory tests of solidification of bentonite and non-clay polymeric muds to select a type and an optimum amount of a bonding agent and to examine the obtained solidified semi-finished product. When solidifying the fluid, it is important to select binding agents, the task of which is to convert the suspension of the drilling fluid into a solid body of sufficient mechanical strength in order to minimize the leaching of hazardous substances in the form of soluble compounds. As a result of these tests, a set of agents constituting a composition based on Portland cement CEM I 32.5 or hydraulic binder – CQ-25 Silment in the amount of 20÷35% containing 4÷5% sodium water glass was selected. The choice of these agents was determined by their chemical properties and their effect on the mechanical properties of the solid produced after the solidification of the borehole fluid. In order to verify the developed technology of solidification of used drilling fluids, a semi-industrial test was carried out. The semiproduct of solidification was tested for compressive strength – after 7 days it was 0.9 MPa, whereas after 14 days – 1.9 MPa. The test of leaching of harmful substances in the leachate from the semi-finished product, showed the following values of determinations: solid dissolved compounds (TDS) – 58 424 mg/kg d. m., Cl-chlorides – 21 300 mg/kg d. m., sulphates – 1984 mg/kg d. m., total organic carbon (DOC) – 3200 mg O2/kg d. m., heavy metal content, which was at a low level. Of the performed determinations, only organic carbon content (DOC) exceeded the leaching limit values (Journal of Laws of 2015, item 1277, Appendix no. 5), which may have been caused by the presence of organic polymers contained in solidified fluids and petroleum substances contaminating them. In addition, toxicological studies of leachate from the solidified semi-finished product were performed using selected toxicological tests. The toxicity expressed in TU units of the tests selected for the research was as follows: Microtox – 4.3; Daphtoxkit (48 h) – 9.9; Spirodela – 9.5. Leachate from the semi-finished product may be classified as low toxic (toxicity class II TU < 10). The presented technology has been granted patent protection No. P. 418959 under the title The method of solidification of used water dispersion bentonite and polymeric drilling fluids, which was awarded with a gold medal at the international exhibition of inventions in Geneva.

3

Magnesy Nd-Fe-B wiązane proszkiem cynku i tworzywem sztucznym

Leonowicz M., Kaszuwara W.

Archiwum Nauki o Materiałach

|

2002

|

T. 23, nr 4

269-281

PL

Wytworzono magnesy z proszku NdFeB wiązane cynkiem oraz żywicą epoksydową. Zbadano podstawowe parametry magnetyczne oraz wytrzymałość na ściskanie w funkcji temperatury wygrzewania, a także zawartości środka wiążącego. Dla magnesów wiązanych cynkiem zbadano skład fazowy. Po wygrzewaniu stwierdzono powstanie dodatkowej fazy NdZn5, co z kolei prowadzi do utworzenia kryształów wolnego żelaza. Porównanie magnesów wiązanych cynkiem i żywicą wykazuje, że większą koercję mają magnesy wiązane żywicą, natomiast magnesy wiązane cynkiem charakteryzują się wyższą remanencją. Za parametry optymalne dla wiązania cynkiem uznano 15% wag. Zn w temperaturze 370 stopni Celsjusza. Dla wiązania żywicą optymalną ilość określono na poziomie 7-10% wag.

EN

Zinc and resin bonded NdFeB magnets were processed. Basic magnetic parameters as well as compressive strength were evaluated versus annealing temperature and volume fraction of the bonding agent. For the zinc bonded magnets phase composition was investigated. The additional NdZn5 phase was found in the Zn bonded magnets after annealing. Comparison of the Zn and resin bonded magnets reveals higher remanence for the former and higher coercivity for the latter. For the Zn and resin bonded magnets, 15 wt.% Zn/370 degrees centigrade and 7-10 wt.% resin were chosen as the optimal processing parameters.