Wyniki wyszukiwania - BazTech

1

Wpływ rozdrobnienia granulowanego żużla wielkopiecowego i współczynnika w/c na wytrzymałość cementów żużlowych

Ostrowski Mikołaj, Niziurska Małgorzata, Duszak Bogumiła, Tkocz Aleksandra

Materiały Budowlane

|

2019

|

nr 9

48--51

2

Analysis of the properties of expansive concrete with portland and blast furnace cement

Jackiewicz-Rek W., Kuziak J., Jaworska B.

Archives of Civil Engineering

|

2018

|

Vol. 64, nr 4/I

175--196

EN

The properties of expansive concretes made of two types of cement: Portland cement CEM I and blast furnace slag cement CEM III were tested. The expansion of the concrete was caused by using an expansive admixture containing aluminium powder added in an amount of 0.5; 1 and 1.5% of cement mass. It was found that the compressive strength of concrete with CEM I decreased after using an expansive admixture in the amount of more than 0.5% of the cement mass. The compressive strength of concrete with CEM III decrease after addition of admixture in the entire range of dosages used. On the basis of electrochemical measurements, it was found no influence of an expansive admixture on corrosion of reinforcing steel. The use of an expansive admixture causes a slight increase in the effective diffusion coefficient of chloride ions in concrete.

PL

W pracy przedstawiono wyniki badań właściwości betonów ekspansywnych o w/c = 0,37 wykonanych z dwóch rodzajów cementu: cementu portlandzkiego CEM I i cementu hutniczego CEM III. Ekspansję betonu wywołano domieszką ekspansywną zawierającą proszek aluminiowy dozowaną w ilości 0,5; 1 i 1,5% masy cementu. Dotychczas proszek aluminiowy był wykorzystywany w technologii betonu m.in. do napowietrzania betonu, produkcji betonu lekkiego, produkcji betonu komórkowego. Proszek aluminiowy w zasadowym środowisku mieszanki betonowej wchodzi w reakcje, w wyniku których wydziela się gazowy wodór. Pod wpływem ciśnienia wywieranego przez wytwarzający się gaz następuje wzrost objętości mieszanki betonowej. Z tego względu proszek aluminiowy może być wykorzystany do produkcji betonów ekspansywnych, do efektywnego wypełniania trudnodostępnych miejsc takich jak szczeliny czy ubytki, a także do produkcji betonów o ograniczonym skurczu w celu zapobiegania zarysowaniom. W pracy przedstawiono wyniki następujących badań: badanie konsystencji mieszanki betonowej metodą opadu stożka, badanie wytrzymałości na ściskanie betonu oraz badania zdolności ochronnych betonu dla stali zbrojeniowej w zakresie badań korozyjnych stali w wyciągach wodnych z betonów i dyfuzji jonów chlorkowych w betonie. Dodatkowo określono przyrost objętości betonu - ekspansję betonu w czasie do 1 godziny od wymieszania składników mieszanki betonowej.

3

Influence of the air-entraining agent in the concrete coating on the reinforcement corrosion process in case of simultaneous action of chlorides and frost

Raczkiewicz W.

Advances in Materials Science

|

2018

|

Vol. 18, nr 1(55)

13--19

EN

The paper presents the test results to evaluate the effect of air-entraining agent addition on the intensity of reinforcement corrosion in concrete with blast-furnace slag cement in the case of simultaneous action of chloride corrosion and frost. Two groups of reinforced concrete specimens were prepared for the study. The first group of specimens included air-entraining agent addition and the other group was prepared without air-entraining agent. The blast-furnace slag cement (CEM III/A) was used for the specimens. Two parallel reinforcing rods were placed in each specimen. The specimens were subjected to 120 cycles of freezing and thawing in 3% NaCl solution to induce corrosion on the reinforcement. To determine the occurrence of the reinforcement corrosion and estimate the corrosion activity the non-destructive electrochemical galvanostatic pulse method was used. On each specimen the corrosion current density of the reinforcement was measured as well as the reinforcement stationary potential and the concrete coating resistivity, i.e. values indicating the ongoing reinforcement corrosion. Measurements were made on all specimens in two steps: before freezing and thawing cycles in 3% NaCl solution and after the cycles. The analysis of the obtained results allowed to determine differences in corrosion processes intensity on the reinforced bars in the concrete specimens depending on whether or not the air-entraining agent was added. Based on the analysis it was found that in the case of simultaneous action of chloride corrosion and frost it is advisable to use both blast-furnace slag cement and air-entraining agent. The use of only blast-furnace slag cement (although it is a chloride resistant cement), without the addition of air-entraining agent is insufficient.

4

Ekologiczne materiały cementowe o podwyższonej odporności na działanie środowisk korozyjnych

Błaszczyński T., Król M.

Przegląd Budowlany

|

2017

|

R. 88, nr 10

56--59

PL

W pracy omówiono zagadnienie ekologiczności cementów. Przedstawiono dwa główne czynniki wpływające na fakt, czy dane spoiwo może być uznane za ekologiczne. Na podstawie badań trwałościowych związanych z odpornością korozyjną zapraw na bazie spoiw cementowych oraz geopolimerowych przedstawiono zalety i wady danych rozwiązań. W porównaniu zestawiono trzy rodzaje materiałów. Były to zaprawy na bazie dwóch cementów: CEM I oraz CEM IV a także wysoko wyspecjalizowanych zapraw na bazie modyfikowanego spoiwa cementowego oraz spoiwa geopolimerowego.

5

Zawartość chlorków w cemencie hutniczym a zdolności ochronne betonowej otuliny zbrojenia

Kuziak J., Woyciechowski P., Wcisło A.

Ochrona przed Korozją

|

2016

|

nr 6

196--199

PL

Przeprowadzono badania wpływu zawartości chlorków w cemencie hutniczym na właściwości ochronne otuliny betonowej. Stosowano cement zawierający od 0,085 do 0,5% jonów chlorkowych. Właściwości ochronne otuliny betonowej oceniono na podstawie anodowych krzywych polaryzacji stali w betonie po różnych czasach dojrzewania oraz po karbonatyzacji betonu. Stwierdzono brak wpływu zawartości chlorków w cemencie hutniczym, w badanym zakresie wartości, na korozję stalowego zbrojenia betonu. Otulina nieskarbonatyzowana, nawet przy najwyższej stosowanej zawartości chlorków, wykazała dobre właściwości ochronne w stosunku do zbrojenia. Zbrojenie w otulinie betonowej skarbonatyzowanej ulegało korozji aktywnej.

EN

The investigation of the effect of chloride content in blast furnace slag cement on the protective properties of concrete cover of steel was carried out. Cement containing from 0.085 to 0.5% chloride ion was used. The protective properties of the concreto cover were evaluated based on anodic polarization curves of steel in the concrete after different periods of concrete hardening and carbonation. No effect of chloride content in the cement, over a range of tested values, on the corrosion of steel reinforcement was found. Noncarbonated cover, even at the highest chloride content used, showed a good protection properties for reinforcement. The active corrosion of steel reinforcement in the carbonated concrete was observed.