1
Content available Study on mechanical properties and microstructure of 42CrMo4/NANOS-BA® high-strength clad plates after the process of hot rolling and two-stage heat treatment with isothermal transformation
Walnik Bartłomiej, Woźniak Dariusz, Nieszporek Aleksandra, Adamczyk Mariusz
Journal of Metallic Materials
|
2021
|
Vol. 73, no. 1
22--31
EN
The aim of the study was to develop a technology for welding non-weldable 42CrMo4 and NANOS-BA® steel grades in the process of hot rolling and two-stage heat treatment. As a result of physical experiments carried out in a line for semi-industrial simulation of the production of metals and their alloys (LPS) and additional heat treatment, a durable combination of 42CrMo4 and NANOS-BA® steels with high mechanical properties was obtained, including: Rp0.2 = 1036 MPa, Rm = 1504 MPa and A = 10.9%, without microscopically visible cracks and other discontinuities in the joined surface. The quality of the 42CrMo4/NANOS-BA® clad plates produced in this way was assessed on the basis of microstructure examination as well as bending, shear and tensile strength tests.
PL
Celem pracy było opracowanie technologii zgrzewania niespawalnych stali w gatunkach 42CrMo4 i NANOS-BA® w procesie walcowania na gorąco i dwuetapowej obróbki cieplnej. W wyniku fizycznych eksperymentów przeprowadzonych w linii do półprzemysłowej symulacji wytwarzania metali i ich stopów (LPS) i dodatkowej obróbki cieplnej uzyskano trwałe połączenie stali 42CrMo4 i NANOS-BA® o wysokich właściwościach mechanicznych m.in.: Rp0,2 = 1036 MPa, Rm =1504 MPa i A = 10,9%, bez widocznych mikroskopowo pęknięć i innych nieciągłości w płaszczyźnie zgrzewania. Ocenę jakości wykonanych tym sposobem połączeń płaskowników dwuwarstwowych 42CrMo4/NANOS-BA® dokonano w oparciu o badania mikrostruktury i próby wytrzymałości na zginanie, ścinanie i rozciąganie.
2
Content available remote Badania złącza doczołowego blachy stalowej platerowanej wybuchowo stopem niklu Inconel 625
Szmul M., Pocica A., Szulc Z.
Przegląd Spawalnictwa
|
2018
|
R. 90, nr 4
43--46
PL
W artykule przedstawiono porównanie dwóch technologii wykonania złącza doczołowego stali P355NH platerowanej wybuchowo stopem Inconel 625. Przedstawiono wpływ zastosowania prądu pulsującego na skład chemiczny ściegów wykonanych metodą 131. Opracowana technologia spawania zapewniła uzyskanie składu chemicznego zgodnie z wymaganiami norm ASME SECTION II, PART A oraz PN-EN 10095:2002.
EN
The article presents a comparison of two welding technologies of butt joints of explosively cladded P355NH - Inconel 625 plate. The influence of applying pulsing current on the chemical composition of stitches made by method 131 is presented. The applied welding technology ensure the chemical composition in accordance with the requirements of ASME SECTION II, PART A and PN-EN 10095:2002.
3
Content available remote Semi-continuous caster for plate
Haga T., Miyazaki K.
Journal of Achievements in Materials and Manufacturing Engineering
|
2017
|
Vol. 84, nr 2
58--67
EN
Purpose: Development of a semi-continuous caster that can cast a single plate and a clad plate of Al-40%Sn-1%Cu alloy used for sliding bearings. Design/methodology/approach: A semi-continuous caster to cast a single plate and a clad plate directly from molten metal was designed and assembled. The cast single plate has a thickness ranging from 10 mm to 30 mm, a width of 400 mm, and a length of 500 mm to 1,000 mm. The cast clad plate has a thickness ranging from 10 mm to 30 mm, a width of 50 mm, and a length of 300 mm. Findings: The semi-continuous caster successfully produced both a single plate and a clad plate of Al-40%Sn-1%Cu alloy. Influence of casting conditions on the properties of the plate, including the thickness, porosity, and surface quality were investigated in the single plate casting. The mixing and diffusion of the alloy elements at the interface was also investigated in the clad plate casting. Research limitations/implications: The cast Al-40%Sn-1%Cu alloy plate has not yet been tested as a sliding bearing material, so the efficacy of the material still requires investigation. Practical implications: The semi-continuous caster described in this paper enables the “small lot” production made from single and clad plates of aluminium alloy. Originality/value: Development of a semi-continuous caster that can cast both single and clad plates of aluminium alloy. Investigation of the relationship between the casting conditions and plate quality.
4
Content available remote Steel clad plates hydrogen degradation evaluation using ultrasonic defectoscopy method
Szwed M., Lublińska K., Gloc M., Manaj W., Kurzydłowski K. J.
Advances in Manufacturing Science and Technology
|
2009
|
Vol. 33, nr 4
51-57
EN
This paper presents results of hydrogen degradation tests of steel clad plates by the ultrasonic defectoscopy. The subject of the tests were samples of low-alloy steel 12CrMo4-5 coated with austenitic steel X2CrNi19-11 using explosive cladding method. The samples were subjected to a thermocycling process within the temperature range from 25 to 450 degrees centigrade in the gaseous hydrogen atmosphere. Detailed microstructural and microanalytical tests of the areas indicated by the ultrasonic defectoscopy were carried out to verify the results of the ultrasonic tests. The structural observations were carried out by light microscopy, scanning electron microscopy (SEM). X-ray microanalysis of chemical composition (EDS) was also performed. The results show that with properly selected measurement settings, the ultrasonic defectoscopy allows to detect early stages of hydrogen degradation in clad plates.
PL
W pracy przedstawiono wyniki badań degradacji wodorowej blach platerowanych metodami defektoskopii ultradźwiękowej. Przedmiotem badań jest blacha ze stali niskostopowej 13CrMo4-5 platerowana metodą wybuchową austenityczną stalą X2CrNi19-11. Wykonano cykliczną obróbkę cieplną w zakresie temperatury od 25 do 450 stopni Celsjusza w atmosferze wodoru. Weryfikację wyników badań ultradźwiękowych dokonano przez obserwację mikrostruktury stali w obszarach wytypowanych za pomocą badań ultradźwiękowych. Stosowano metody mikroskopii świetlnej, elektronowej mikroskopii skaningowej oraz mikroanalizę rentgenowską (EDS). Stwierdzono, że dobór parametrów pomiarowych metodą defektoskopii ultradźwiękowej umożliwia wykrywanie wczesnych etapów degradacji wodorowej mikrostruktury stali blach platerowanych.
5
Content available remote Evaluation of steel clad plate weldability using ram tensile test method
Zatorski Z.
Engineering Transactions
|
2007
|
Vol. 55, iss. 3
229-238
EN
The weldability evaluation of steel clad plate is performed using the ram tensile test method. Numerical analysis of the considered problem is performed using the finite element method. The author introduces and verifies a critical ram tension strength R0 above the yield strength RIIe – as the criterion of the weldability evaluation of clad steel plate, where: RIIe =RIe < 0:707, RIIe, RIe – yield strengths of soft and hard materials.
6
Content available remote Wpływ walcowania platerów Al-Cu na ich właściwości plastyczne
Skoblik R.
Archiwum Technologii Maszyn i Automatyzacji
|
2000
|
Vol. 20, Nr 1
193-200
PL
Jedną z metod otrzymywania materiałów warstwowych jest ich łączenie przez wybuch. Na przykładzie plateru Al-Cu pokazano możliwości obróbki plastycznej na zimno przez walcowanie, spęczanie, gięcie i tłoczenie takich materiałów.
EN
One of the method to obtain laminated materials is the bonding of metal explosion. On the example bi-metal Al-Cu it has been shown the plastic cold working; for example rolling, upsetting, press forming.
7
Content available remote Spawanie blach platerowanych ASTM A387C/A240 + 450 na przykładzie modernizacji Reaktora na instalacji Kraking Katalityczny II w S.A. 'Petrochemia' Płock
Rodakowski T., Główka K., Nieradka G.
Przegląd Spawalnictwa
|
1999
|
R. 71, nr 5
15-18