Effect of artificial polymer film on biooxidation of arsenopiryte wastes

Jażdżyk E., Sadowski Z.

Physicochemical Problems of Mineral Processing

|

2003

|

Vol. 37

69-76

EN

The effect of polymer film on the biooxidation of arsenopyrite tailings was examined. Adsorption of a typical sugar polymer, dextrin, on the mineral particles was studied. The effect of pH on the adsorption at the biooxidation range was determined. The microelectrodes were used to measure the dissolved oxygen concentration in the polymer film. Based on these results, the oxygen diffusion coefficient has been calculated to be 1.6 10-5 cm2/s. The biooxidation results show that polymer film plays a key role in both the immobilization of microbial cells and oxygen diffusion. For effective biooxidation of arsenopyrite tailings the presence of polymer film onto the solid surface is indispensable

PL

Określono wpływ filmu utworzonego z dekstryny na proces bioutleniania odpadów arsenopirytowych. Zbadano proces adsorpcji typowego polimeru cukrowego, dekstryny, na powierzchni materiału mineralnego. Określono wartości odczynu pH dla procesu bioutleniania odpadów arsenopirytowych. Stosując mikroelektrodę tlenowa określono profile stężeń tlenu w filmie z polimeru. Korzystając z uzyskanych wyników obliczono współczynnik dyfuzji tlenu w warstwie utworzonego filmu. Współczynnik ten wyniósł 1.6 10-5 cm2/s. Wyniki uzyskane dla procesu bioutleniania wskazują na to, że film utworzony z polimeru odgrywa kluczową rolę zarówno w procesie unieruchomienia komórek bakteryjnych jak i w dyfuzji tlenu. W celu zintensyfikowania procesu bioutleniania odpadów arsenopirytowych niezbędna wydaje się być obecność filmu z polimeru na powierzchni ciała stałego.

2

Wpływ uziarnienia odpadów arsenopirytowych na kinetykę procesu bioutleniania

Jażdżyk E., Sadowski Z.

Inżynieria Chemiczna i Procesowa

|

2001

|

T. 22, z. 3C

561--566

PL

Procesu bioutleniania odpadów arsenowych przeprowadzono w biorotorze i w kolbach Erlenmayera z wykorzystaniem bakterii Thiobacillus ferrooxidans. Kinetykę procesu opisano za pomocą równania logistycznego.

EN

The kinetics of bacterial oxidation of arsenic bearing waste using Thiobacillus ferrooxidans cells was studied. The effects on the rate of biooxidation were determined for two solid fractions. The logistic equation was used to descried experimental data.

3

Biooxidation of mining tailings from Zloty Stok.

Sadowski Z., Jażdżyk E., Farbiszewska T.

Physicochemical Problems of Mineral Processing

|

2000

|

Vol. 34

47-56

EN

The biooxidation of gold-bearing arsenic concentrate from mining tailing was investigated. The strain of Thiobacillus ferrooxidans isolated from the Zloty Stok tailing heaps was used. The chemical and biooxidation processes were monitored by checking the ferrous, ferric and arsenic concentration in the leaching solution. Leaching experiments, were conducted using both coarse (-0.5 +0.125 mm) and fine (-0.045 mm) fractions. The samples were examined. by means of the specific surface area measurements and the X-ray diffraction analysis. The small differences were observed during the oxidation of coarse and fine fractions. The slow chemical dissolution of loellingite (AsFe2) a main arsenic-bearing mineral, was supported by X-ray diffraction anal. In the case of a fine fraction oxidation, the precipitation of ferric arsenate was responsible for the lower Fe and As readings. The production of new phase was also supported by the FTIR spectra. Obtained results suggest that the direct biooxidation mechanism was responsible for the arsenic-bearing concentrate biooxidation.

PL

Przeprowadzone wcześniej badania wykazują, że odpady górnicze zgromadzone na Hałdzie Jan koło Złotego Stoku stanowią potencjalny surowiec do otrzymania złota. Przedstawiona Praca zawiera wyniki badań nad procesem bioutleniania próbek mineralnych pobranych z hałdy Jan. W badaniach użyto homogenizowanych bakterii Thiobacillus ferrooxidations wcześniej wyselekcjonowanych z tego złoża. Próbom bioługowania poddano grubo i drobnoziarnistą frakcję surowca. Przebieg procesu bioutleniania analizowane przez kontrole zmian stężenia jonów Fe(II), Fe(III), As przez pH roztworu. Określono zmiany w powierzchni właściwej próbek mineralnych wywołane procesem bioutleniania. Zachowanie gruboziarnistej próbki mineralnej mało różni się od chemicznego i biologicznego utleniania materiału drobnoziarnistego. Badania rentgenowskie wskazują na łatwiejsze bioutleniania loellingitu w porównaniu z procesem chemicznym. Zmniejszenie stężenia jonów arsenu w roztworze w końcowym okresie chemicznego ługowania należy tłumaczyć wytrąceniem się arseninu żelaza. W przypadku zastosowania pożywki 9K do bioługowania stężenia arsenu w roztworze spadło do zera. Badania spektroskopowe potwierdzają powstanie arseninu żelaza w procesie bioutleniania drobnoziarnistej frakcji odpadów górniczych z hałdy Jan.