Large strain deformation substructures and local crystallography in {100}<001>/{110}<001> aluminium bicrystals

Paul H., Driver J. H., Maurice C., Bijak M.

Archives of Metallurgy and Materials

|

2006

|

Vol. 51, iss. 1

43-53

EN

Symmetrically oriented bicrystals of pure Al(99.998%) have been deformed in channel-die compression up to strains of 1.5 to correlate the dislocation substructures and the slip system distributions. The study has focused on structure development in f100g<001>/f110g<001> (cube/Goss) – oriented bicrystals with the grain boundary situated parallel to the compression plane. Both orientations have the same nominal Taylor factor and deform macroscopically by the same amount but have stable (Goss) and unstable (cube) micro-deformation behavior. The character of the deformation substructure was determined by systematic local orientation measurements using high resolution EBSD in a SEM-FEG scanning electron microscope and also by transmission electron microscopy (TEM) and the CBED technique at specific locations. The bicrystal deformation analysis shows that the microtexture evolution within neighboring grains is quite different. Very strong deformation banding is observed within crystallites with the unstable orientation, i.e. cube-oriented grain forms classical deformation bands of slightly and strongly dislocated areas. The Goss-oriented grains within bicrystals are more stable under plane strain conditions and do not show any tendency to strain inhomogeneties except for the zone near the grain boundary.

PL

W pracy analizowano umocnieniowe zachowanie się bikryształów Al(99.998%) o orientacji krystalitów {100}<001>/ {110}<001>, odkształcanych w próbie nieswobodnego ściskania do zakresu odkształceń ∼1.5. Granica rozdziału pomiędzy ziarnami usytuowana była równolegle do płaszczyzny ściskania. Obydwa krystality formujące bikryształ scharakteryzowane są tą samą wartością współczynnika Taylora. Jednakże ich zachowanie umocnieniowe jest odmienne, tj. orientacja {110}<001> pozostaje stabilna podczas gdy {100}<001> jest silnie niestabilna. W oparciu o pomiary orientacji lokalnych w TEM a także z wykorzystaniem techniki EBSD w SEM wyposażonym w działo o emisji polowej dokonano charakterystyki mikrostrukturalnej i tekturowej. W krystalicie o orientacji {100}<001> obserwowano formowanie się pasm odkształcenia złożonych z obszarów o wysokiej i niskiej gęstości dyslokacji. Orientacja G{110}<001> pozostawała stabilna nie przejawiając tendencji do formowania pasmowych niejednorodności odkształcenia za wyjątkiem wąskich obszarów w pobliżu granicy pomiędzy ziarnami.

2

In-situ SEM studies of microtextural changes during recrystallization of cold deformed Al bicrystal

Paul H., Lens A., Driver J.H.

Inżynieria Materiałowa

|

2004

|

R. XXV, nr 3

411-414

EN

The evolutions of the components of the deformation microtexture and new grains orientation at early stages of recrystallization have been investigated in great detail. The analysis based on deformation process developed by plane strain compression in pure aluminium bicrystals with {100}<011>/{110}<001> orientation and with the grain boundary situated parallel to the compression plane. Progress in understanding of the new grains orientations formation was possible thanks to combination of the sample heating with systematic local orientation measurements within selected areas, using scanning electron microscopy (SEM) and electron backscattered diffraction (EBSD). SEM/EBSD orientation maps allowed investigation of the new grains occurrence, their growth, and as a result, the changes of the crystallographic orientations at early stages of recrystallization. Within step by step recrystallized samples the grain boundary migration connected with the 'consumption' of the as-deformed areas is realized by their movement along crystallographic corresponding to traces of the {111}<110>-type slip systems. No significant orientation changes within as-deformed areas far from the recrystallization front (with increasing of the recrystallization time) were observed.

PL

W pracy analizowano ewolucję składowych mikrotekstury stanu odkształconego oraz zmiany orientacji, jakie następują w początkowych stadiach procesu rekrystalizacji. Przeprowadzoną analizę oparto o proces nieswobodnego ściskania (channel-die test) próbek bikryształów aluminium o układzie orientacji {100}<011>/ {110}<001>, z granicą pomiędzy ziarnami, usytuowaną równolegle do płaszczyzny ściskania. W badaniach dokonano połączenia techniki pomiaru orientacji lokalnych w SEM z obserwacjami 'in-situ' wzrostu nowych ziaren w procesie rekrystalizacji. Sukcesywnie wykonywane mapy orientacji umożliwiły dokładną analizę krystalograficznych aspektów wzrostu nowych ziaren a tym samym mechanizmów rządzących procesem przemiany tekstury. Wykazano, że proces 'konsumpcji' obszarów stanu zdeformowanego jest realizowany poprzez migrację frontu rekrystalizacji wzdłuż kierunków krystalograficznych odpowiadających usytuowaniu śladów poślizgu typu {111}<110>. Ze wzrostem czasu wyżarzania nie obserwowano istotnych zmian orientacji w obszarach stanu odkształconego, znacznie oddalonych od czoła frontu rekrystalizacji.

3

Crystal lattice rotation in channel-die deformed al bicrystals with {100}<001>/{100}<011> AND {100}<001>/{110}<001> orientations

Paul H., Litwora A., Bijak M.

Inżynieria Materiałowa

|

2004

|

R. XXV, nr 3

540-544

EN

The issues of band-like inhomogeneties of deformed structure and the evolution of their microtexture components are addressed. The analysis is based on bands development by plane strain compression in {100}<001>/{100}<011> and {100}<001>/{110}<001> oriented high purity aluminium bicrystals with boundary planes situated nearly perpendicular to the compression plane. Substantial progress in understanding the character of these bands was possible due to systematic local orientation measurements using scanning electron microscopy (SEM) equipped with field emission gun (FEG). Goss {110}<001> oriented grains are stable within the range of applied deformations whereas the 'cube' {100}<001> and 'shear' {100}<011> grain orientations are very unstable under plane strain conditions and develop band-like inhomogeneities of deformation.

PL

W pracy analizowano formowanie się niejednorodności odkształcenia oraz ewolucję ich wewnętrznej mikrotekstury. Badania prowadzono na bikryształach aluminium o układzie orientacji {100}<001>/{100}<011> i {100}<001>/{110} <001> z granicą ziaren usytuowaną równolegle do płaszczyzny ściskania. Opisu dominujących systemów poślizgu odpowiedzialnych za obserwowane tendencje rotacji sieci krystalicznej dokonano w oparciu systematyczne pomiary orientacji w mikroskopie skaningowym wyposażonym w działo o emisji polowej. Ziarna o orientacji 'goss'{110}<001>są stabilne w szerokim zakresie odkształceń podczas gdy krystality o orientacjach 'cube'{100}<001> oraz 'shear' {100}<011>są silnie niestabilne w próbie nieswobodnego ściskania i sprzyjają rozwojowi pasmowych niejednorodności odkształcenia.