The Effect of Powder Particle Biencapsulation with Ni-P Layer on Local Corrosion of Bonded Nd-(Fe,Co)-B Magnetic Material

Klimecka-Tatar D., Pawłowska G., Sozańska M.

Archives of Metallurgy and Materials

|

2015

|

Vol. 60, iss. 1

153--157

EN

Effect of the Nd-(Fe,Co)-B powder particle biencapsulation with Ni-P layer on bonded magnetic materials corrosion behaviour has been investigated. Bonded magnets were prepared from single-phase, nanocrystalline magnetic Nd11 Fe77 Co5 B6 powder. Powder particles before consolidation were preliminary etched and then coated with bilayer (powder biencapsulation). The powder surface was coated as a first with autocatalytic applied Ni-P layer during 5, 15 and 30 minutes in Ni(II) containing bath and the second layer was thermosetting epoxy-resin. Impact of the used biencapsulation process was rated on the basis of polarization curves recorded in phosphate environment with addition of chloric ions. It has been established that the used biencapsulation method satisfactorily isolate individual particles of the powder and consequently, significantly inhibits corrosion processes of the final material, especially in passivating environment containing Cl-.

PL

W pracy zaprezentowano wyniki badań nad wpływem bienkapsulacji cząstek proszku powłokami Ni-P/żywica epoksy-dowan na odporność korozyjną magnesów wiązanych. Materiały magnetyczne zostały przygotowane z jednofazowego, na-nokrystalicznego proszku Nd11 Fe77 Co5 B6. Cząstki proszku przed konsolidacją były wstępnie trawione, a następnie pokryte podwójną warstwą (bienkapsulacja proszku). Powierzchnia proszku w pierwszej kolejności została poddana 5 i 30 minutowemu autokatalitycznemu nanoszeniu warstw Ni-P. Drugą warstwę stanowił materiał spoiwa, czyli żywica epoksydowa. Dokonano oceny wpływu zastosowanej metody bienkapsulacji na odporność na korozję lokalną na podstawie krzywych polaryzacji zarejestrowanych w środowisku fosforanowym (0,5M, pH = 3) z dodatkiem jonów chlorowy. Stwierdzono, że zastosowane metody bienkapsulacji zadowalająco izolują pojedyncze cząstki proszku, a co za tym idzie, hamują proces korozji materiału końcowego, zwłaszcza w środowisku pasywującym zawierającym Cl- .

2

The effect of Nd-(Fe,Co)-B powder biencapsluation with Cu/epoxy resin coating on the corrosion behavior in sulphate solution of bonded magnets

Pawłowska G., Klimecka-Tatar D., Mazik A.

Ochrona przed Korozją

|

2013

|

nr 4

174--176

EN

In this paper the investigation under the effect of Nd-(Fe,Co)-B powder biencapsulation with Cu/epoxy resin coating on the bonded magnets corrosion behavior in acidified (pH = 1 and 3) sulphate solutions was carried out. The subject of this study was bonded magnetic material based on Nd12Fe77Co5B6 powder. The Authors have presented proposition of the preliminary chemical treatment of powder particles by etching their surface in oxalic acid solution and covering with protective bilayer. It has been found that the using of complex method of oxides removing and powder particles biencapsulation with Cu/epoxy resin coating before consolidation beneficially affect on the corrosion properties of magnetic composite.

PL

Przeprowadzano badania nad wpływem bienkapsulacji cząstek proszku Nd-(Fe,Co)-B, powłoką typu Cu/żywica epoksydowa na korozyjne zachowanie magnesów wiązanych w zakwaszonych (pH = 1 i 3) środowiskach siarczanowych. Przedmiotem badań były wiązane materiały magnetyczne na bazie proszku Nd12Co5Fe77B6. Autorzy przedstawili propozycję wstępnej obróbki chemicznej cząstek proszku, poprzez wytrawienie ich powierzchni w roztworze kwasu szczawiowego oraz pokrycie podwójną warstwą ochronną. Zauważono, że zastosowanie kompleksowej metody usuwania tlenków i bienkapsulacji cząstek proszku powłokami Cu/żywica epoksydowa korzystnie wpływa na odporność korozyjną kompozytu magnetycznego.

3

Effect of the Nd-(Fe,Co)-B powder biencapsulation with Ni-P/epoxy resin and phosphate/epoxy resin coatings on the potentiokinetic characteristic of bonded magnets in the phosphate solution

Klimecka-Tatar D., Pawłowska G., Radomska K.

Ochrona przed Korozją

|

2013

|

nr 5

187--190

EN

In this paper the effect of the Nd-(Fe,Co)-B powder particles biencapsulation process with double protective coatings (Ni-P/epoxy resin and phosphate/ epoxy resin) on the corrosion resistance of the magnets bonded in the phosphate environment was presented. The test material were composite magnets prepared from Nd-(Fe,Co)-B powder, which surface was preliminary coated with Ni-P layer during 5, 15 and 30 minutes of Ni(II) modyfication solution bath and with phosphate protective coating resulting from the powder exposure in aqueous phosphate solution acidified to pH = 3 and 7. Impact of the used biencapsulation process was rated on the basis of polarization curves recorded in phosphate environment (pH = 3) and assigned during electrochemical measurment polarization resistance. It is shown that the biencapsulation before the consolidation process has its beneficial effect on corrosion characteristics of the final magnet in passivating environment.

PL

W artykule przedstawiono wpływ procesu bienkapsulacji cząstek proszku Nd-(Fe,Co)-B, podwójnymi powłokami ochronnymi (powłokami Ni-P/żywica epoksydowa oraz fosforan/żywica epoksydowa) na odporność korozyjną magnesów wiązanych w środowisku fosforanowym. Do badań posłużono się wiązanymi materiałami magnetycznymi na bazie proszku Nd12Co5Fe77B6, którego powierzchnia została pokryta powłoką Ni-P/ żywica epoksydowa (w czasie 5, 15 i 30-minutowej kąpieli w modyfikującym roztworze soli Ni(II)), oraz powłoką ochronną fosforan/żywica epoksydowa w roztworze fosforanowym (pH = 3 i 7). Wpływ procesu bienkapsulacji oceniono na podstawie badań elektrochemicznych w środowisku fosforanowym (pH = 3). Stwierdzono się, że zastosowanie metody bienkapsulacji przed procesem konsolidacji proszku ma korzystny wpływ na odporność korozyjną finalnego materiału magnetycznego.

4

Wpływ bienkapsulacji proszków Nd(Fe,Co)B powłokami Ni-P na odporność korozyjną wiązanych magnesów w środowisku sztucznej śliny i roztworze Ringera

Klimecka-Tatar D., Pawłowska G., Szymura S., Radomska K.

Ochrona przed Korozją

|

2012

|

nr 11

505-508

PL

Przeprowadzono badania nad wpływem bienkapsulacji cząstek proszku Nd(Fe,Co)B powłokami NiP/żywica epoksydowa na zachowanie korozyjne uzyskiwanych w ten sposób magnesów wiązanych w środowisku płynów ustrojowych/ fizjologicznych. Materiałem do badań były magnesy kompozytowe wykonane z proszku Nd(Fe,Co)B, którego powierzchnia została pokryta warstwą Ni-P w czasie 5, 15 i 30-minutowej kąpieli w modyfikującym roztworze soli Ni(II). Dla oceny odporności korozyjnej materiału wiązanego wykonano potencjokinetyczne krzywe polaryzacji w środowisku sztucznej śliny i roztworze Ringera. Badania korozyjne wykazały, że zastosowanie bienkapsulacji przed procesem spajania ma korzystny wpływ na charakterystyki korozyjne materiału finalnego.

EN

Investigations under the effect of the powder particles biencapsulation with NiP/epoxy resin coating on corrosion characteristics of the final bonded magnetic material have been carried out. As corrosion environments the physiological body fluids have been applied. The test material were composite magnets prepared from Nd(Fe,Co)B powder, which surface was coated with NiP layer during 5, 15 and 30 minutes of Ni(II) modyfication solution bath. To evaluate corrosion behaviour of the bonded material the Potentiokinetic polarization curves in artificial saliva and Ringer solution have been compared. It is shown that the biencapsulation before the consolidation process has its beneficial effect on corrosion behaviour of the final magnet.

5

Bienkapsulacja proszków RE-M-B powłokami NiP/żywica epoksydowa jako metoda poprawy odporności korozyjnej

Klimecka-Tatar D., Pawłowska G.

Ochrona przed Korozją

|

2012

|

nr 5

212-215

PL

Przedstawiono przeglądową oceny ocenę wpływu enkapsulacji cząstek proszku Nd12Fe77Co5B6 powłokami NiP na ograniczenie powierzchniowego utleniania składników stopu. Omówiono również korozyjne zachowanie magnesów kompozytowych, wykonanych z proszków po bienkapsulacji powłokami NiP/żywica epoksydowa, w roztworach o różnym zakwaszeniu. Ocenę odporności korozyjnej magnesów wiązanych przedstawiono na podstawie pomiarów krzywych polaryzacji w zakwaszonych roztworach siarczanowych (pH = 1 i 3). Stwierdzono, że pokrycie cząstek proszku warstwą NiP przed procesem spajania skutecznie spowalnia procesy utleniania powierzchni cząstek oraz ogranicza szybkość korozji magnesów wiązanych.

EN

The effect of the encapsulation of Nd12Fe77Co5B6 powder particles with NiP coating on the surface oxidation rate has been evaluated. The behavior of the composite magnet made of powder after biencapsulation with NiP/epoxyresin layers in solutions with different acidification was also discussed. Evaluation of corrosion resistance of bonded magnets from polarization curves measurements in acidic sulphate solutions (pH = 1 and 3) was carried out. The study showed that the coating of powder particles of NiP layer effectively inhibits the oxidation process of basic alloying elements and reduces the corrosion rate of the final bonded magnets.