Liquid metal induced embrittlement as a case of stress corrosion cracking?

Wolski K.

Advances in Materials Science

2007

Vol. 7, nr 1(11)

93-99

Lmie (liquid metal indueed embrittlement) was studied on two model-systems: ni-bi at 700°c and cu-bi at 500°c. Lmie has been split in two independent steps, namely intergranular penetration at high temperature in absence of any external stress and room temperature embrittlement. Both systems exhibit rapid intergranular penetration with parabolic kinetics and subsequent room-temperature brittleness due to the intergranular diffusion of bismuth. The concentration profile of bismuth in grain boundaries bas been obtained by quantitative auger electron spectroscopy. For both systems an approximately one hundred microns transition zone between unaffected and embrittled part of grain boundary bas been shown, as opposed to Some nanometres transition length typical of the wetting phenomena. A major implication of these results is that the modelling of intergranular penetration and liquid metal embrittlement have to be based on a diffusionnal mechanism operating at a very tip of the penetration profile and in this sense lme (but not lmie) can be considered as a case of stress corrosion cracking.

Deformation Behaviour of Channel-Die Compressed Al Bicrystals with {100}<001>/{110}<011> Orientation

Paul H., Driver J. H.

Archives of Metallurgy and Materials

2005

Vol. 50, iss. 1

209--218

The formation of band-like heterogeneities in deformed grains and the evolution of their microtexture components during large plastic deformations is examined in Al bicrystals. The study has focussed on bands developed by plane strain compression in {100}< 001 >/}110}< 011> (soft/hard)-oriented high purity aluminium bicrystals with the boundary plane situated parallel to the compression plane. The character of the bands was determined by systematic local orientation measurements using EBSD in SEM-FEG scanning electron microscope and also by transmission electron microscopy (TEM/CBED) at specific locations. The bicrystal deformation analysis shows that the microtexture evolution in each crystallite is quite dierent. Very strong deformation banding in the ‘cube’ grain is initiated by strain incompatibilities and giving initial rotations about transveres direction. At very high strains where the flow is inhomogeneous, clearly defined rotations about a <112> axis are observed, suggesting localized single {111}<110> slip in areas of the band. The ‘hard’ {110}<011>-oriented grains are more stable under plane strain conditions except for the zone near the grain boundary where strong micro-textural/structural disturbances are observed.

W pracy analizowano problem formowania się pasmowych niejednorodności odkształcenia oraz ich wpływ na ewolucję mikrostruktury i tekstury stanu odkształconego. Analiza bazuje na pasmach formujacych się w bikryształach aluminium o układzie orientacji ziaren {100}<001>/{110}<011>, z granicą pomiędzy krystalitami usytuowaną równolegle do płaszczyzny ściskania, poddanych nieswobodnemu ściskaniu. Identyfikacje mechanizmów odpowiedzialnych za obserwowane tendencje rotacji sieci krystalicznej przeprowadzono z użyciem transmisyjnej (TEM) i skaningowej (SEM) mikroskopii elektronowej, wykorzystujących techniki pomiaru orientacji lokalnych. Zachowanie umocnieniowe oraz ewolucja początkowej orientacji obydwu krystalitów formujących bikryształ są całkowicie odmienne. Ziarna o orientacji {100}<001> wykazują silną tendencję do formowania pasm odkształcenia. Z krystalograficznego punktu widzenia proces przejścia od orientacji osnowy do orientacji pasma, stowarzyszony jest z rotacją sieci krystalicznej dookoła osi <112> sugerującej aktywacje pojedynczego poślizgu typu {111}<110>. Krystality o orientacji {110}<110>, w badanym zakresie deformacji są bardziej stabilne, za wyjątkiem obszarów bezpośrednio przylegających do granicy ziaren gdzie obserwowano wystąpienie silnych zaburzeń sieci krystalicznej.