Wyniki wyszukiwania - BazTech

1

Structure and properties of Ni-P/PTFE composite coatings produced by chemical reduction method

Trzaska M., Cieślak G., Mazurek A.

Composites Theory and Practice

|

2016

|

R. 16, nr 3

174--179

EN

The paper presents the results of investigations on Ni-P/PTFE alloy composite coatingsproduced by the electroless method. Ni-P coatings were deposited from two baths differing in composition and pH (acidic and alkaline). PTFE powders with a nanometric size of particles was used as the dispersion phase. The coatings were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), optical microscopy, roughness measurements and Vickers microhardness measurements. Abrasive wear testing of the Ni-P/PTFE coatings was carried out by friction of the ball at a constant pressure on the sample using a Calotest apparatus. Images of the surface morphology, cross section of the coatings and sample surfaces after wear tests are presented. The coatings are compact and have good adhesion to the steel substrate. Incorporation of the PTFE powder particles in the nickel-phosphorus matrix increases the degree of surface development and hardness of the coating material and increases the wear resistance.

PL

W pracy przedstawiono wyniki badań stopowych powłok kompozytowych Ni-P/PTFE wytwarzanych metodą bezprądową. Powłoki Ni-P osadzano z dwóch kąpieli różniących się składem oraz pH (kwaśna oraz zasadowa) na stali. Jako fazę dyspersyjną stosowano proszek politetrafluoroetylenu (PTFE). Powłoki były badane za pomocą następujących technik badawczych: skaningowej mikroskopii elektronowej (SEM), dyfrakcji promieniowania rentgenowskiego (XRD), mikroskopii optycznej, pomiarów mikrotwardości metodą Vickersa, pomiarów parametrów chropowatości powierzchni. Badania zużycia ściernego powłok Ni-P/PTFE realizowano za pomocą kulotestera przy stałym nacisku kulki na badaną próbkę. Przedstawiono obrazy morfologii powierzchni, przekrojów poprzecznych powłok i powierzchni po badaniach zużycia ściernego. Wytworzone powłoki charakteryzują się zwartą budową i dobrą przyczepnością do stalowego podłoża. Wbudowanie cząstek proszku PTFE w niklowo-fosforową osnowę wpływa na zwiększenie stopnia rozwinięcia powierzchni, twardości materiału powłok oraz zwiększenie odporności na zużycie ścierne.

2

Corrosion properties of Ni-P and Ni-B alloy coatings produced by chemical method

Trzaska M., Cieślak G., Mazurek A.

Ochrona przed Korozją

|

2015

|

nr 11

426--429

EN

The paper presents results of investigations reported to Ni-P and Ni-B alloy coatings produced by electroless deposition in chemical reduction process on S235JR carbon steel substrate. The coatings were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), optical microscopy, Vickers microhardness measurements and electrochemical corrosion tests. Images of the surface morphology, cross-sections of the coatings and corrosion damages are presented. The results of corrosion tests for investigated coatings are presented in the forms of potentiodynamic polarization curves j = f (E) and values of corrosion potentials and currents. The results showed a compact and a good adhesion of the alloy coatings to the substrate and their good corrosion resistance in studied corrosive environments.

PL

W pracy przedstawiono wyniki badań powłok stopowych Ni-P oraz Ni-B wytworzonych na podłożu ze stali węglowej S235JR metodą bezprądową w wyniku procesu redukcji chemicznej. Powłoki scharakteryzowano za pomocą: dyfrakcji promieniowania rentgenowskiego (XRD), skaningowej mikroskopii elektronowej (SEM), mikroskopii optycznej. Przeprowadzono badania mikrotwardości metodą Vickersa, oraz badania odporności korozyjnej metodą potencjodynamiczną. Przedstawiono obrazy morfologii powierzchni, przekrojów poprzecznych powłok oraz zniszczeń korozyjnych. Wyniki badań korozyjnych powłok zostały przedstawione w postaci potencjodynamicznych krzywych polaryzacji j = f(E) oraz wartości potencjałów i prądów korozyjnych. Wyniki badań wskazują na zwartą budowę oraz dobre połączenie wytworzonych powłok do stalowego podłoża oraz dobrą odporność korozyjną w badanym środowisku korozyjnym.

3

Bezprądowe nakładanie wielowarstwowych powłok Zn/Ni-P/Ni-P-SiC na stopach magnezu AZ91D

Rudnik E., Gdula M.

Rudy i Metale Nieżelazne Recykling

|

2014

|

R. 59, nr 4

164--172

PL

Przeprowadzono próby otrzymywania powłok kompozytowych Ni-P/SiC na stopach magnezu AZ91D. Jako warstwy pośrednie naniesiono: powłokę cynkową metodą cementacyjną oraz powłokę Ni-P w procesie autokatalitycznym. Powłoki scharakteryzowano pod względem składu i morfologii. Określono mikrotwardość poszczególnych warstw oraz przeprowadzono testy szczelności układu wielowarstwowego.

EN

Ni-P/SiC composite coatings were deposited on AZ91D magnesium alloys. Two interlayers were used: zinc was deposited by cementation, while Ni-P layer was obtained by electroless deposition. Zinc and nickel plating solutions should contain fluoride ions in order to protect the alloy against corrosion due to the formation of a sparingly soluble magnesium fluoride. Composition and morphology of the individual layers were described. The presence of SiC significantly increased the microhardness of the alloy surface, but porosity of the coatings and large potentials differences between the individual layers and the alloy substrate lead to the galvanic corrosion of magnesium.

4

Otrzymywanie nanometrycznych ziaren srebra jako katalizatora autokatalitycznego osadzania miedzi

Rudnik E.

Rudy i Metale Nieżelazne

|

2013

|

R. 58, nr 8

442-446

PL

Przedstawiono przegląd literatury dotyczący metod otrzymywania zarodków katalitycznych Ag. Zaprezentowano także wyniki badań własnych dotyczących syntezy ziaren Ag na szkle. Stosowano uczulanie w SnCl2 i aktywację w roztworach AgNO3 z dodatkiem substancji kompleksujących (NH3, C7H6O2, EDTA). Określono wpływ czasu poszczególnych etapów na morfologię, wielkość i gęstość rozkładu ziaren metalicznych. Oceniono „efektywność” katalizatora w procesie autokatalitycznego osadzania miedzi.

EN

A review of the literature data on the Ag activator is presented. The results of the studies on the Ag particles synthesis are also reported. Sensitization of the substrate in SnCl2 was followed by the activation in AgNO3 solution with complexing agents (NH3, C7H6O2, EDTA). The influence of the time on the morphology, size and distribution density of the metal particles was investigated. “Efficiency” of the catalyst was determined during electroless deposition of copper.

5

Bezprądowe osadzanie mikrocząstek cyny na podłożu niemetalicznym

Rudnik E., Wcisło K.

Rudy i Metale Nieżelazne

|

2013

|

R. 58, nr 5

254-259

PL

Przedstawiono sposób syntezy mikrocząstek cynowych na podłożu niemetalicznym metodą bezprądową. Zaproponowano następujący sposób otrzymywania: (I) synteza zarodków katalizatora Pd, (II) bezprądowe osadzanie miedzi z roztworu alkalicznego z zastosowaniem formaldehydu jako reduktora, (III) wytwarzanie ziaren cynowych na drodze cementacji cyny(II) miedzią w roztworze kwaśnym, (IV) osadzanie cyny z roztworu silnie alkalicznego na drodze dysproporcjonacji Sn(II). Średnia wielkość poszczególnych ziaren metalicznych wynosiła: 0,7 nm Pt, 2 [mi]m Cu, 10 [mi]m Sn (cementacyjnie) i 4 [mi]m Sn (autokatalitycznie). Przeprowadzono także dodatkowe pomiary elektrochemiczne z zastosowaniem różnych typów elektrod.

EN

The paper presents electroless deposition of tin microparticles on non-metallic substrate. The following method was proposed: (I) synthesis of Pd catalytic nuclei for copper electroless deposition, (II) electroless deposition of copper from an alkaline solution using formaldehyde as a reducing agent, (III) cementation tin by copper nuclei in an acid solution, (IV) tin electroless deposition in a strong alkaline solution. Average grain sizes were: 0,7 nm Pt, 2 [mi]m Cu, 10 [mi]m Sn (cemented) i 4 [mi]m Sn (autocatalytic). Electrochemical studies were also performed using various electrode substrate.

6

Warstwy Ni-P z proszkami ceramicznymi jako faza dyspersyjna

Miazga A., Konopka K., Trzaska M., Biedunkiewicz A.

Materiały Ceramiczne

|

2012

|

T. 64, nr 1

94-97

PL

W pracy przedstawiono wyniki badań struktury i niektórych właściwości niklowych warstw kompozytowych z fazą dyspersyjną w postaci proszków ceramicznych otrzymanych metodą zol-żel. Wykorzystane zostały dwa rodzaje proszków: nanometryczny węglik tytanu oraz wielofazowa mieszanina węglików i borków, w skład której wchodziły min. TiB2, B4C i TiC, także o rozmiarach nanometrycznych. Warstwy wytwarzane były metodą redukcji chemicznej na stali St3S. W celach porównawczych na tym samym podłożu wytworzona została także warstwa Ni-P. Osadzanie warstw przeprowadzano z wykorzystaniem zasadowej kąpieli do niklowania chemicznego z dodatkiem 1 g/dm3, 5 g/dm3 i 10 g/dm3 ceramicznej fazy dyspersyjnej. Na podstawie przyrostu masy określona została szybkość narastania warstw pozwalająca ocenić efektywność procesu bezprądowego osadzania. Topografia otrzymanych warstw oraz struktura warstw na przekroju charakteryzowane były z użyciem skaningowego mikroskopu elektronowego z przystawką EDS. Wykonana została komputerowa analiza obrazu pozwalająca określić zawartość fazy ceramicznej w warstwie. Charakterystyka morfologii powierzchni warstw wykonana została z użyciem profilometru optycznego. Określone zostały także parametry chropowatości oraz mikrotwardość. Stwierdzono, że obecność proszku TiC w kąpieli zwiększa szybkość procesu osadzania warstw, natomiast proszek wielofazowy spowalnia ten proces oraz jest on mniej efektywny pod względem ilości wbudowanej w warstwę fazy ceramicznej. Stwierdzono także, że warstwy kompozytowe charakteryzowały się znacznie większą chropowatością powierzchni oraz wyższą mikrotwardością w porównaniu do warstwy Ni-P.

EN

The paper presents the results of studies of the structure and some properties of composite nickel layers with the dispersion phase as ceramic powders obtained by the sol-gel method. Two types of powders were used: nanometric titanium carbide and mixture of carbides and borides, which contained e.g. TiB2, B4C and TiC, also of a nanometric size. The layers were deposited by chemical reduction on St3S steel. For comparison, on the same substrate, Ni-phosphorus coatings were obtained. The coatings were deposited from alkaline bath. The electroless deposition processes were performed with different contents of ceramic powders: 1 g/dm3, 5 g/dm3 and 10 g/dm3. Basing on the mass increase, a rate of layer rise was determined, which allowed the effectiveness of the process to be evaluated. The topography of the obtained layers and their cross-sectional structure were characterized by using scanning electron microscopy with EDS attachment. Computer image analysis was applied to determine the content of the dispersed ceramic phase in the composite material. Characteristics of the surface morphology of the layers was performed by using an optical profilometer. The roughness and microhardness values were determined. It was found that the presence of TiC powder in the bath increases the speed of the deposition process while multiphase powders slows the process, and it is less efficient in terms of the ceramic phase content built in the layer. It was also found that the composite layers showed much higher surface roughness and higher microhardness than the Ni-P layer.

7

Powłoki cyny immersyjnej - badanie właściwości korozyjnych

Araźna A., Bieliński J., Królikowski A.

Ochrona przed Korozją

|

2009

|

nr 11

468-469

PL

Warstwy cyny immersyjnej o różnej grubości osadzono na folię miedzianą z roztworu metanosulfonianowego. Odporność na korozję osadzanych warstw określono w roztworze 0,5 M NaCl metodą potencjodynamiczną. Powłoki Sn badane były w stanie dostawy i po starzeniu. Zaobserwowano, że odporność korozyjna warstw o grubości 0,3 žm wzrasta po starzeniu, natomiast grubsze warstwy Sn w niewielkim stopniu zmieniają swoje właściwości korozyjne. Porównując te wyniki z uzyskanymi dla powłok Sn osadzanych z roztworu chlorkowego stwierdzono, że warstwy Sn immersyjnej o różnych cechach morfologicznych mają odmienne właściwości korozyjne po starzeniu.

EN

Immersion tin coatings of different thickness were deposited on copper foil from methanolulfonic bath. Their corrosion behavior in 0.5 M NaCl solution was determined using potentiodynamic polarization method. The Sn coatings were investigated as received and after ageing. It was observed, that corrosion resistance of 0.3 žm thick Sn layers increased after ageing, whereas the corrosion resistance of thicker layers was changed slightly. These results were compared with those for Sn layers obtained from hydrochloric bath. It was found, that immersion tin coating with various morphology showed different corrosion characteristic after ageing.

8

Bezprądowe osadzanie Ni-P z roztworów z dwoma związkami buforująco-kompleksującymi

Bieliński J., Gajewska-Miziołek A., Jaworska A., Bielińska A., Kuziak J.

Inżynieria Powierzchni

|

2007

|

nr 4

29-35

PL

Przedmiotem pracy jest przedstawienie roli związków buforujących i kompleksujących (ZBK), stosowanych w roztworach do bezprądowego osadzania warstw stopowych Ni-P, zawierających układy dwóch ZBK. W części literaturowej dokonano przeglądu najważniejszych opisów osadzania Ni-P dla roztworów z dwoma ZBK oraz przeanalizowano możliwe mechanizmy współudziału związków w procesie. W części doświadczalnej porównano procesy osadzania Ni-P z roztworów kwaśnych (pH = 3 - 6) i alkalicznych (pH = 7,5 - 9,5), zawierających siarczan niklu, podfosforyn sodu oraz dodatki wybranych ZBK. Główną uwagę poświecono roztworom z cytrynianami lub z glicyną, z dodatkami wybranych związków buforujących, organicznych i nieorganicznych. Stwierdzono, że w przypadku roztworów na osnowie cytrynianu, szybkość metalizacji, przy dodatku drugiego ZBK, była określana prze zawartość cytrynianu. Dodatki nieorganiczne przyspieszały osadzanie. Natomiast w roztworach na osnowie glicyny o rodzaju zmian szybkości metalizacji decydowała wartość pil roztworu. Otrzymywano powłoki Ni-P o wysokiej zawartości P (ponad 10%), jedynie dodatek glicyny w roztworach alkalicznych zmniejszał zawartość fosforu nawet do 2%.

EN

The subject of the paper is an analysis of the role of the buffering and complexing compounds (BCC) applied in electroless Ni-P deposition baths, with two BCC additives. The process behaviour and the mechanism of action for the most important baths with two BCC additives are reviewed in the introduction part of the paper. The experimental part of paper presents the investigation of electroless Ni-P deposition from acidic (pH = 3 - 6) and alkaline baths (pH = 7,5 - 9,5), containing nickel sulphate and sodium hypophosphite, with added some BCC. Special attention was paid to citrate and glycine as main BCC. It was concluded that the Ni-P deposition rate was mainly influenced by citrate content or by pH in glycine-containing baths. Inorganic additives increased deposition rate in citrate baths. The deposited Ni-P coatings contained over 10% of P, glycine as BCC decreased this content up to 2%.