1

Enhancement of mechanical properties of concrete using microwave cured bamboo composites

Adeniyi Ajayi Joseph, Gana James, Adanikin Ariyo, Ogedengbe Kola, Idowu Abundance

Archives of Civil Engineering

|

2022

|

Vol. 68, nr 3

553--567

EN

Microwave curing of bamboo fiber increases the physical and mechanical qualities of cement concrete, according to previous studies. However, there are limited research on their endurance when used as an additive in concrete manufacturing to increase strength. The impact of bamboo fiber and Styrene Butadiene Rubber (SBR) on the mechanical and microstructure of the resulting concrete is investigated in this study. With the inclusion of bamboo fiber ranging from 0-1.5%, a mix ratio of 1:1.5:3 was used. To make the samples, 10% SBR by weight of cement was dissolved in the mixing water. The batching was done by weight, with a water cement ratio of 0.6. Compressive strength, water absorption, swelling, modulus of elasticity, and modulus of rupture were all studied as mechanical properties. Various characterization tests such as SEM, EDS, FTIR, XRD, and TGA were performed on the microstructure, crystalline nature, and mineral composition of certain samples. According to the FTIR study’s findings, peak levels were detected in the O-H stretching, C-H fiber and CH2 functional groups, carbonyl group, C-O and C-C functional groups. As the temperature climbed, TGA measurements showed a drop in weight. The XRD test revealed peak levels of 6.611, 4.255, and 3.855 for sanidine, quartz, and calcite, respectively. After 28 days, the inclusion of bamboo fibers as an additive in concrete shows some promising outcomes in compressive strength, with samples containing 1% and 1.5% bamboo fiber cured at 80°C having a higher compressive strength value.

2

Microbiological and Chemical Analysis of Bamboo Textile Materials and Leathers Modified with Bamboo Extract at the Tanning Stage

Ławińska Katarzyna, Serweta Wioleta, Popovych Nataliia, Decka Sebastian, Woźnicki Dominik, Ogrodowczyk Dominika, Rostocki Andrzej, Sprynskyy Miroslaw

Fibres & Textiles in Eastern Europe

|

2021

|

Vol. 29, no. 3 (147)

33--39

EN

In this paper, microbiological and chemical analysis were carried out in the case of bamboo textile materials and leathers modified by bamboo extract at the tanning stage. Microbiological resistance was examined for some fungi, i.e.: Aspergillus niger, Trichophyton mentagrophytes and Candida albicans and some bacteria strains: Escherichia coli, Salmonella enteritidis and Pseudomonas aeruginosa. In parallel, a safety analysis was conducted through the determination of heavy metals, certain aromatic amines and dimethyl fumarate. The main goal of the above-mentioned research was a comprehensive examination of materials which will be used as footwear components i.e.: linings, uppers and insoles. These issues are very important from the footwear manufacture point of view because of the opportunity to find new solutions in the field of hygienic and healthy materials which can be applied as footwear elements. The anti-microbial and anti-fungal resistance of materials are features important for the reduction of the probability of dermatosis. For this reason, they should be taken into account when the improvement of hygienic properties is pursued.

PL

W ramach prac przeprowadzono analizy mikrobiologiczne skórzanych i tekstylnych materiałów, w których w procesie produkcji zastosowano włókna oraz ekstrakt bambusa. Dokonano oceny odporności wybranych materiałów, przeznaczonych na asortyment obuwniczy, na działanie mikrogrzybów tj. Aspergillus niger, Trichophyton mentagrophytes, Candida albicans oraz określono ich aktywność antybakteryjną względem szczepów Escherichia coli, Salmonella enteritidis, Pseudomonas aeruginosa. Równoległym kierunkiem badań było określenie aspektu bezpieczeństwa stosowania poprzez oznaczenie zawartości metali ciężkich, amin aromatycznych i fumaranu dimetylu. Celem przedstawionych badań była kompleksowa diagnostyka możliwości zastosowania tekstyliów na bazie włókien bambusowych i skór modyfikowanych roztworem ekstraktu z bambusa w roli materiałów obuwniczych takich, jak: cholewki, wyściółki, podszewki oraz wkładki. Tematyka ta została podjęta ze względu na potrzebę ciągłego poszukiwania przez producentów możliwości poprawy właściwości higienicznych materiałów obuwniczych. Uzyskanie efektu bakterio – i grzybostatycznego jest jedną z istotnych funkcji tych materiałów, co z kolei prowadzi do redukcji prawdopodobieństwa występowania schorzeń dermatologicznych stóp. Aspekt ten jest jednym z najważniejszych, który należy wziąć pod uwagę przy projektowaniu obuwia o zoptymalizowanych właściwościach higienicznych.

3

Tensile, Flexual, Impact and Water Absorption Properties of Natural Fibre Reinforced Polyester Hybrid Composites

Prasanna Venkatesh R., Ramanathan K., Srinivasa Raman V.

Fibres & Textiles in Eastern Europe

|

2016

|

Vol. 24, no. 3 (117)

90--94

EN

In this paper, tensile, flexural, impact properties and water absorption tests were carried out using sisal/unsaturated polyester composite material. Initially the optimum fibre length and weight percentage are estimated. To improve the tensile, flexural and impact properties, sisal fibre was hybridised with bamboo fibre. This work shows that the addition of bamboo fibre in sisal/ unsaturated polyester composites of up to 50% by weight results in increasing the mechanical properties and decreasing the moisture absorption property. In this research work, the effects of fibre treatment and concentration on the mechanical properties of a short natural fibre reinforced polyester hybrid composite are investigated. The fibres were subjected to 10% sodium hydroxide solution treatment for 24 h. The mechanical properties of composites with treated fibres are compared with untreated fibre composites. The fractured surface of the treated fibre composite specimen was studied using Scanning Electron Microscopy (SEM).The treated hybrid composite was compared with an untreated hybrid composite, with the former showing a 30% increase in tensile strength, 27.4% - in flexural strength, and 36.9% - in impact strength, along with an extreme decrease in moisture absorption behaviour.

PL

Badania przeprowadzono stosując kompozyty sizal/poliester i sizal/nienasyconą żywicę poliestrową. Początkowo określono optymalną długość włókien oraz udział procentowy masy w materiale kompozytowym. Dla polepszenia właściwości mechanicznych do włókien sizalowych dodawano włókna bambusowe aż do 50% wagowych. Stwierdzono polepszenie właściwości mechanicznych i, co jest bardzo ważne, zmniejszenie absorpcji wilgoci. Włókna poddawano działaniu 10% roztworu wodorotlenku sodu przez 24h. Badano kompozyty niemodyfikowane i modyfikowana zwracając szczególną uwagę na przełomy obserwowane za pomocą SEM. Stwierdzono polepszenie właściwości mechanicznych hybrydowych kompozytów poddanych modyfikacji, przy czym wytrzymałość na rozciąganie zwiększyła się o 30%, na zginanie 27,4% a wytrzymałość na uderzenia o 36,9%, a jednoczenie absorpcja wody zmniejszyła się znacznie

4

Investigation of Regenerated Bamboo Fibre and Yarn Characteristics

Erdumlu N., Ozipek E.

Fibres & Textiles in Eastern Europe

|

2008

|

Vol. 16, no. 4 (69)

43--47

EN

This article presents general characteristics and current applications of regenerated bamboo fibre in the textile industry. In the experimental part of the study, 100% regenerated bamboo yarns of six different counts (11.8, 14.8, 16.4, 19.7, 24.6 and 29.5 tex) were produced from bamboo fibre using ring yarn spinning technology. Subsequently, the physical parameters of related yarns produced in spinning mill conditions were tested, and the results were evaluated according to the parameters of 100% viscose rayon, as well as 100% carded and combed ring spun yarn in Uster statistics. In this way, the aim was to state the strength and weakness of bamboo fibre and to predict its future in the textile industry

PL

Przedstawiono ogólną charakterystykę regenerowanych włókien bambusowych oraz możliwości ich zastosowania w przemyśle tekstylnym. Część eksperymentalna przedstawionych badań dotyczyła regenerowanych włókien bambusowych o sześciu masach liniowych (11,8; 14,8; 16,4; 19,7; 24,6 i 29,5 tex). Włókna przędziono na przędzarce obrączkowej, a następnie włókna otrzymane w warunkach określonej przędzalni były badane a wyniki porównywano ze 100% wiskozową przędzą ciągłą oraz zgrzebloną i czesaną przędzą obrączkową, biorąc jako odniesienie charakterystyki Ustera. Badania pozwoliły na określenie zalet i wad włókien bambusowych i możliwości ich zastosowania w przemyśle włókienniczym.