A Comparative Study on Ballistic Behaviour of MWCNT / Graphene Reinforced AL6061 Surface Composites Fabricated Via Friction Stir Processing

Magarajan U., Suresh Kumar S.

Archives of Metallurgy and Materials

2023

Vol. 68, iss. 2

541--550

In this work, a comparative study on the ballistic behaviour of friction stir processed AL6061 targets had been made. Base Metal AL6061 (BM) plates with 25 mm thickness were friction stir processed by adding Multi Walled Carbon Nano Tubes (MWCNT) and Graphene (G), producing AL6061-MWCNT and AL6061-G surface composites. Optical microscopy and microhardness test on BM, AL6061-MWCNT and AL6061-G samples were performed as per the standard procedure. It was noticed that uniform dispersion of ceramic particles and refined grains were obtained for the friction stir processed surface composites. From the microhardness test, it was perceived that friction stir processing had induced strengthening of surface composites, hence increasing the microhardness of AL6061-MWCNT and AL6061-G by ~60.3% and ~73.6% respectively. Also, ballistic experiments were conducted at 680±10 m/s by impacting Ø7.62×51 mm projectiles. AL6063 backing plates were placed to compare the ballistic behaviours AL6061-MWCNT and AL6061-G targets by depth of penetration. It was noted that the depth of penetration of AL6061-MWCNT and AL6061-G targets were 37.81% and 65.84% lesser than the BM target. Further, from the results of Post ballistic microscopy it was observed that the microstructure near and away from the penetration channel edge looks unchanged in BM target. However, the AL6061-MWCNT and AL6061-G targets showed considerable change in their morphology, by forming Adiabatic Shear Bands.

Estimation of the Propagation of the Impact Wave Phenomenon as a Result of a Bullet Impact in PACVD-Modified Textiles

Struszczyk Marcin H., Łandwijt Marcin, Wilbik-Hałgas Bożena, Cichecka Magdalena, Urbaniak–Domagała Wiesława, Puszkarz Adam K., Krucińska Izabella

Fibres & Textiles in Eastern Europe

2019

Vol. 27, no. 2 (134)

68-73

This complex study was performed using Plasma Assisted Chemical Vapour Deposition (PACVD) modification of ultrahigh molecular weight polyethylene (UHMWPE) fibrous composites and pararamid fabrics with deposition of a fluoro- or silane-like-polymer onto their surface. Research on the phenomenon of the propagation of the shockwave resulting from a bullet hit in an insert model system was performed on the basis of the PN-V-87000:2011 Standard, with the use of 7,62x25 TT 5,5 ± 0,1g bullets. To assess the phenomenon of propagation of the shockwave resulting from a bullet hit in the insert model system, an ultrahigh-speed digital camera was used. The behaviour of the shockwave resulting from the hit of a bullet on the surface of the model insert systems studied depended greatly on the type of textiles introduced to the system. Modification with low-temperature plasma in the presence of vapours of low-molecular-weight fluorinated or silanegenic substrates positively affected the stability of ballistic properties during accelerated aging of woven fabrics and unwoven sheets.

Wykonano kompleksowe badania elastycznych kompozytów włóknistych na bazie UHMWPE i tkanin para-aramidowych poddanych z zastosowaniem modyfikacji plazmą z chemicznym osadzaniem na ich powierzchni z fazy gazowej polimeru fluoro- lub silanopodobnego. Badania odporności na odłamki standardowe wykonano w oparciu o własną procedurę badawczą opracowaną na podstawie STANAG 2920 edycja 2 Ballistic Test Method for Personal Armour Materials and Combat Clothing. Układy modelowe wykonane ze zmodyfikowanych lub niemodyfikowanych arkuszy na bazie UHMWPE wykazywały znacząco odmienny trend zmian odłamkoodporności, w przypadku jako czynniki starzenia zastosowano temperaturę i wilgotność. W układach wykonanych ze zmodyfikowanych nietkanych arkuszy zaobserwowano wzrost wartości V50, podczas gdy V50 układów wykonanych ze niezmodyfikowanych arkuszy zmniejszył się wraz z wydłużeniem procesu przyspieszonego starzenia. Modyfikacja plazmą niskotemperaturową w obecności oparów o niskiej masie cząsteczkowej substratów fluorowych lub silanowych zmieniła właściwości tkanin i włóknin. Wpłynęło to korzystnie na stabilność właściwości balistycznych podczas przyspieszonego starzenia.