Impact of reclaimed asphalt pavement (RAP) on low-temperature properties of asphalt concrete

Jaczewski Mariusz, Dołżycki Bohdan, Alenowicz Jacek, Jaskuła Piotr

Roads and Bridges - Drogi i Mosty

|

2019

|

Vol. 18, no. 4

303--315

EN

Hot mix recycling is a practice which enables reusing materials from old asphalt pavements. Current Polish regulations allow usage of RAP only for binder and base courses, and its amount is limited. Asphalt mixtures with RAP material have to fulfil requirements stated for typical asphalt mixtures. The research presents low-temperature properties of twelve different asphalt concretes with RAP material, determined using three-point bending test. Mixtures differed in: type (for wearing, binder or base courses), content of RAP (from 0% up to 60%), quality of RAP material and application of rejuvenator. For all mixtures, RAP content strongly influences mechanical properties – critical strain and flexural strength. Their values decreased with an increase in the used amount of RAP. The greatest decrease was observed for wearing and binder courses. The changes were much smaller for base course mixtures, even with higher amounts of RAP.

PL

Recykling mieszanek mineralno-asfaltowych na gorąco umożliwia powtórne wykorzystanie materiałów uzyskanych ze starych nawierzchni asfaltowych. Aktualne polskie przepisy pozwalają użyć granulat asfaltowy w ograniczonej ilości, tylko do zastosowania w przypadku warstw wiążących oraz podbudowy. Mieszanki mineralno-asfaltowe z udziałem granulatu asfaltowego muszą spełniać wymagania obowiązujące dla typowych mieszanek asfaltowych. W pracy określono niskotemperaturowe właściwości dwunastu różnych betonów asfaltowych z udziałem granulatu asfaltowego wyznaczone na podstawie trzypunktowego badania zginania. Mieszanki różniły się przeznaczeniem (do warstw ścieralnych, wiążących lub podbudowy), zawartością granulatu asfaltowego (od 0% do 60%), jego jakością i zastosowaniem środka odmładzającego lepiszcze. W przypadku wszystkich badanych mieszanek zawartość granulatu asfaltowego wywierała istotny wpływ na ich właściwości mechaniczne – odkształcenie graniczne i wytrzymałość na zginanie. Wartości tych parametrów zmniejszały się wraz ze wzrostem zastosowanej ilości granulatu asfaltowego. Największe spadki zanotowano w przypadku warstw ścieralnych i wiążących. W przypadku warstw podbudowy zmiany te były znacznie mniejsze, nawet gdy zwiększano w nich udział granulatu asfaltowego

2

Failure analysis of poly(phenylene sulphide)/short glass fibre composite in bending strength test

Ostapiuk M.

Inżynieria Materiałowa

|

2016

|

Vol. 37, nr 5

272--277

EN

Nowadays polymer composites are one of the most popular materials in the field of science and applying engineering. They combine various advantages, which are easy to manufacture, cost effectiveness and excellent performance. The great importance is choosing of an appropriate matrix for special composites elements working in different conditions. Very interesting technical material seems to be the thermoplastic resin poly (phenylene sulphide) (PPS) which can be used in automobiles, aircrafts and electro-/electronics technologies. Conventional thermoset composites have in recent years successfully found engineering applications but in contrast to PPS they have been limited for applying at higher temperature and difficulties in recycling. Regarding the lack of knowledge in terms of precise understanding on the failure basis, there has been not many publications on the degradation mechanisms of PPS with short glass fibres. In this article, the PPS/fibre fillers (containing 30% and 40% short glass fibers) has been introduced. It has been showed and discussed the phenomena and structure characterization after three point bending tests. It was carried out the macro- and microstructural observation. The plots of stress vs displacement indicate to brittle materials behaviour. All samples of the PPS 30% and PPS 40% composites subjected to 3-points bending test were destroyed in in the centre of the sample. It was confirmed that in short fibre composites, generally, the failure process is dictated by fibre/matrix separation which usually starts near the fibre ends. The scheme of cracking is similar regardless of fibre content. The bending stresses were higher in the composite with higher volume fraction of fibres.

PL

Istnieje niewiele doniesień w literaturze na temat zjawisk zachodzących w kompozytach termoplastycznych podczas badań wytrzymałościowych, a w szczególności dotyczy to kompozytów wzmacnianych krótkimi włóknami. Dlatego celem artykułu jest analiza zniszczenia i zmian w strukturze kompozytu o osnowie poli(siarczku fenylenu) (PPS) wzmacnianego krótkimi włóknami szklanymi w badaniach wytrzymałości 3-punktowego zginania.

3

Trwałość zmęczeniowa mosiądzu MO58 poddanego proporcjonalnemu cyklicznemu zginaniu ze skręcaniem

Kohut M.

Zeszyty Naukowe. Mechanika / Politechnika Opolska

|

2005

|

z. 85

31-38

PL

W pracy przedstawiono wyniki badań zmęczeniowych mosiądzu MO58 w zakresie cyklicznego czystego zginania, czystego skręcania i kombinacji zginania ze skręcaniem ?a= 0,5?a. Wyznaczono pasma rozrzutu dla poszczególnych badań zmęczeniowych ze współczynnikiem istotności =5%. W opisie trwałościowym jest to pasmo o współczynniku rozrzutu równym 2,2 dla zginania, 2,5 dla skręcania i 2,1 dla wybranej kombinacji zginania ze skręcaniem.

EN

The paper contains the fatigue test results for MO58 brass under pure bending, pure torsion and combined bending with torsion ?a= 0,5?a. The scatter bands with really factor equal to five percent for individual fatigue tests were determined. In fatigue life the scatter band amounts to 2.2 for pure bending, 2.5 for pure torsion and adequate 2.1 for combination bending with torsion.