Wyniki wyszukiwania - BazTech

1

The bactericidal effect of extracts from Humulus lupulus l marynka variety on selected bacteria

Rył Bartosz, Sporek Monika, Krzyśko-Łupicka Teresa

Ecological Chemistry and Engineering. A

|

2020

|

Vol. 27, nr 1-2

1--11

EN

The aim of the research was to obtain extracts of Humulus lupulus L hop cones of the Marynka variety and to evaluate their antibacterial properties against three strains of gram-negative bacteria (Escherichia coli ATCC 10536, E. coli IPS and Pseudomonas aeruginosa ATCC 27853) and against two strains of gram-positive bacteria (Enterococcus hirae ATCC 10541 and Bacillus cereus ATCC 12826). The research material consisted of dried Marynka variety hop cones, from which extracts in the form essential oil (EO), infusion and decoction were obtained. EO was obtained in the process of hydrodistillation. The antibacterial activity of the extracts was evaluated by the plate-cylinder diffusion method against the tested gram-negative and gram-positive bacteria. Diverse antibacterial activity of water extracts of H. lupulus L hop cones of the Marynka variety (essential oil, infusion and decoction) on the tested bacteria was demonstrated, with higher sensitivity of gram-positive than gram-negative bacteria. The highest resistance to hop extracts was demonstrated by P. aeruginosa ATCC 27853. The best antibacterial properties were demonstrated by the essential oil at a concentration of 2.0 %. In the group of gram-positive bacteria, E. hirae ATCC 10541 was more sensitive to EO, and E. coli IPS in the group of gram-negative bacteria. In the case of B. cereus ATCC 12826, the sensitivity to infusions and decoctions of hop cones requires further investigation, as the obtained large zones of growth inhibition were unstable.

2

Bioactive Membranes from Cellulose with a Graphene Oxide Admixture

Machnicka A., Fryczkowska B.

Journal of Ecological Engineering

|

2018

|

Vol. 19, nr 6

231--240

EN

The paper presents the results of microbiological tests of composite membranes made of cellulose (CEL) with graphene oxide (GO) admixture. At the beginning, the antibacterial properties of the GO in aqueous solutions of various concentrations (0.001; 0.01; 0.1% w/w) were studied, and the obtained results allowed to use GO as an additive to cellulose membranes. The solution used to prepare the membranes was a 5% cellulose solution (CEL) in 1-ethyl-3-methylimidazolium acetate (EMIMAc), into which various amounts of graphene oxide (GO) dispersed in N,N-dimethylformamide (DMF) were added (0.5÷28.6% of GO). From this solution, composite membranes were formed using phase inversion method. It was observed that the GO addition influences the process of membrane formation and their physicochemical properties. The obtained membranes were subjected to microbiological tests using the Gram-negative bacteria (Escherichia coli), Gram-positive bacteria (Staphylococcuc aureus) and fungi (Candida albicans). It was observed that the GO addition to the cellulose membrane (GO/CEL) inhibited the growth of bacteria and fungi, and the biological activity as dependent on the type of living organism and the size of GO particles.

3

Biomateriały implantacyjne dotowane srebrem – próby wstępne. Cz.1 – Materiały gipsowe

Jaegermann Z., Michałowski S., Ciołek L., Wiśniewski Z.

Prace Instytutu Ceramiki i Materiałów Budowlanych

|

2015

|

R. 8, nr 22

23--33

PL

Celem prac nad implantacyjnymi biomateriałami dotowanymi srebrem było opracowanie wstępnych założeń otrzymywania materiałów gipsowych i kalcytowych wykazujących działanie bakteriobójcze. Opis wyników prowadzonych prac podzielono na dwie części, które ukażą się w kolejnych numerach czasopisma. Istotą zadania opisanego w niniejszym artykule było dobranie sposobu dotowania materiałów gipsowych nanocząstkami srebra i przeprowadzenie badań skuteczności przeciwbakteryjnej otrzymanych materiałów. Do przygotowania materiałów gipsowych wykorzystano półwodny siarczan wapnia odmiany α oraz roztwory koloidalne srebra. Przygotowano pięć rodzajów próbek gipsowych i przeprowadzono badania ich właściwości fizycznych. Badania skuteczności przeciwbakteryjnej dla wybranych próbek przeprowadzono metodą rozcieńczeń z wykorzystaniem pałeczki ropy błękitnej Pseudomonas aeruginosa i gronkowca złocistego Staphylococcus aureus. Wyniki przeprowadzonych wstępnych badań wykazały, że zastosowana metoda otrzymywania materiałów gipsowych zawierających srebro daje szansę na uzyskanie materiałów wykazujących działanie przeciwbakteryjne w stosunku do użytych mikroorganizmów. Udowodniono również, że działanie przeciwbakteryjne badanych próbek zależy zarówno od ich składu chemicznego, jak i od rodzaju użytych bakterii.

EN

The aim of the work on implant biomaterials containing silver was to develop initial assumptions on the production of gypsum and calcite materials showing bactericidal effect. The description of results was divided into two parts, which will appear in consecutive issues of the magazine. The essence of the research described in this article consisted in choosing the method of adding of silver nanoparticles to gypsum material, as well as in testing antimicrobial efficacy of the materials obtained. Calcium sulfate hemihydrate and colloidal silver solutions were used for the preparation of gypsum implants. Five types of gypsum samples were prepared and their physical properties were tested. Antimicrobial activity studies of selected samples were performed by dilution method using Pseudomonas aeruginosa and Staphylococcus aureus. The results of preliminary studies have shown that the method of silver doping of gypsum materials is a way of obtaining implants with antibacterial activity, in the case of microorganisms used in the research. It was also shown that the antibacterial effect of test samples depended on both the chemical composition and the type of bacteria applied.

4

Deposition of Zinc Oxide on the Materials Used in Medicine. Preliminary Results

Teterycz H, Suchorska-Woźniak P, Fiedot M, Karbownik I

Fibres & Textiles in Eastern Europe

|

2014

|

Vol. 22, no. 3 (105)

126--132

EN

This paper presents preliminary results of the direct deposition of nano- and microstructures of zinc oxide on materials used in medicine. The coatings were deposited on cotton gauze and polyamide fabric. During the research the biological activity of these materials was defined. Performed were also tests of doping the ZnO structures with silver obtained. The research has proved that there is a growth of zinc oxide structures both on the gauze and polyamide fabric. The nanostructures deposited on it did not become detached from the surface, even though the material was subjected to ultrasonic rinsing. In addition, good biocidal properties of both of the textile materials modified were found. Furthermore a complex surface analysis of catheters: vascular and urological was made. ZnO was deposited on catheters, but they were characterised by low adhesion.

PL

W artykule przedstawiono wstępne wyniki badań bezpośredniego osadzania nano- i mikrostruktur tlenku cynku na materiałach stosowanych w medycynie. Warstwy osadzono na gazie opatrunkowej, tkaninie poliamidowej oraz cewnikach wykonanych z politetrafluoroetylenu. Podczas badań określono aktywność biologiczną czystej oraz pokrytej ZnO gazy opatrunkowej i tkaniny poliamidowej. Wykonano również próby domieszkowania otrzymywanych struktur ZnO srebrem. Badania wykazały, że na analizowanych materiałach zachodzi wzrost struktur tlenku cynku. Stwierdzono dobre właściwości biobójcze zmodyfikowanych materiałów włókienniczych. Ponadto przeprowadzono kompleksową analizę powierzchni cewników naczyniowych i urologicznych. Na ich powierzchni również tworzyły się warstwy tlenku cynku, lecz charakteryzowały się niską adhezją .

5

Poly(lactide-co-glycolide) composites containing antibacterial silver nanoparticles : in vitro preliminary study

Ziąbka M., Mertas A., Król W.

Composites Theory and Practice

|

2014

|

R. 14, nr 3

155--162

EN

This work concerns the biological and morphological assessment of poly(lactide-co-glycolide)/silver nanoparticle (nAg) composites prepared by the slip-casting method. Due to the significance of the bactericidal properties of such materials, antibacterial activity against Gram-positive - Staphylococcus aureusand Gram-negative - Escherichia coliwas evaluated by means of the surface deposition method. By inductively coupled plasma mass spectrometry (ICP-MS), it was possible to evaluate the amount of released silver ions and to determine their impact on the surrounding environment of bacteria. The material microstructure and dispersion of the modifier phase were estimated by using electron scanning microscopy with elemental analysis in micro-areas (SEM+EDS). The roughness and Theta angle measurements allowed us to define the surface character of the investigated materials. The tests of antibacterial efficacy proved that nanosilver-modified composites have bactericidal activity against the tested bacteria. The antibacterial efficacy of the tested materials depends on the amount of modifier phase (nAg). Along with an increasing volume fraction of modification phase, a different degree of the homogenization process was observed as well as a reduction in composite homogenization, a roughness increase and Theta angle decrease. At the same time, the composites showed higher wettability. Spectrometric analysis showed that the amount of released silver ions depends on the amount of nanoparticles present in the polymer matrix.

PL

W pracy przedstawiono ocenę morfologiczną i biologiczną kompozytów polilaktyd-ko-glikolid/nanocząstki srebra (nAg) otrzymanych w procesie odlewania folii. Materiały kompozytowe oraz polimer w czystej postaci poddane zostały testom oceny aktywności przeciwbakteryjnej. Skuteczność bakteriobójcza została oceniona wobec wzorcowych szczepów Gram-dodatnich bakterii Staphylococcus aureus oraz Gram-ujemnych bakterii Escherichia coli, wykorzystując w tym celu technikę osadzania powierzchniowego. Za pomocą techniki elektronowej mikroskopii skaningowej (SEM) oraz spektroskopii z dyspersją energii (EDS) przeprowadzono ocenę mikrostruktury oraz stopnia dyspersji fazy modyfikującej w matrycy polimerowej. Dzięki przeprowadzonym pomiarom profilometrycznym oraz kąta zwilżania określono charakter powierzchni badanych materiałów. Ilość uwolnionych jonów srebra oznaczono techniką spektrometrii mas ze wzbudzeniem w plazmie indukcyjnie sprzężonej (ICP-MS). Antybakteryjne działanie materiałów korelowano z ilością uwolnionych do otoczenia jonów srebra. Na podstawie wyników przeprowadzonych testów i obserwacji wykazano, że kompozyty polimerowe modyfikowane nanosrebrem wykazują działanie bakteriobójcze wobec wzorcowych szczepów Gram-dodatnich bakterii Staphylococcus aureus oraz Gram-ujemnych bakterii Escherichia coli. Skuteczność przeciwbakteryjnego działania badanych materiałów kompozytowych uzależniona była od ilości dodatku antybakteryjnego (nAg). Wraz z rosnącym udziałem fazy modyfikującej obserwowano niższy stopień homogenizacji kompozytów, wzrost chropowatości i spadek kąta zwilżania, ale tym samym kompozyty wykazywały wyższą zwilżalność. Największą skutecznością działania przeciwbakteryjnego wobec bakterii Gram-dodatnich i Gram-ujemnych wykazywały się kompozyty z dodatkiem trzech procent wagowych nanosrebra.