Ferritic ductile cast iron was quench-hardened with the isothermal transformation in the range of temperatures 400÷300 °C, in the range of time 7,5÷240 min. Soaking before the transformation was gradual. Nominal austenitizing temperature t = 950 °C, and then there appeared cooling to t[gamma] = 850 or 800 °C. Heat treatment was performed with the usage of specimens for the impact strength test, and after that hardness was measured and microstructure analyzed. Test results were used to elaborate mathematical equations and to make threedimensional charts with the usage of STATISTICA and EXCEL software. It was stated, that austenitizing temperature and conditions of the isothermal transformation influence on hardness and impact strength of ADI. On the base of hardness and impact strength it can be stated that as a result of gradual austenitizing of specimens there was obtained ADI corresponding to grades of ASTM 897 (850/550/10) Grade 1, (1050/700/7) Grade 2 and (1200/850/4) Grade 3.
JavaScript jest wyłączony w Twojej przeglądarce internetowej. Włącz go, a następnie odśwież stronę, aby móc w pełni z niej korzystać.