Wyniki wyszukiwania - BazTech

1

Application of Natural and Artificial Ageing on Multiply Remelted AlSi9Cu3 Alloy

Matejka M., Bolibruchova D.

Archives of Foundry Engineering

|

2019

|

iss. 2

60--66

EN

This article focuses on the study of the influence of remelting and subsequent natural and artificial ageing on the structure of recycled AlSi9Cu3 alloy with increased iron content. The assessed changes in eutectic silicon and iron-based intermetallic phases were carried out using optical and scanning electron microscopy. The degradation of the eutectic silicon morphology due to remelting occurred only at the highest numbers of remelting. The effect of remelting the investigated alloy, which is accompanied by a gradual increase in wt. % Fe, began to manifest significantly through a change in the length of the ferric phases after the fourth remelting. As expected, the artificial ageing process has proven to be more effective than natural ageing. It has led to a change in the eutectic silicon morphology and has been beneficial in reducing the lengths of adverse ferric phases. The use of alloys with higher numbers of remelting, or with greater “contamination”, for the manufacture of shape-challenging castings is possible when using a suitable method of eliminating the negative factors of the remelting process. The results of our investigation show a suitable method of the above elimination the application of heat treatment T5 – via artificial ageing.

2

Odporność tynków polimerowych na wzrost glonów jako cecha ich trwałości

Wiejak A.

Materiały Budowlane

|

2016

|

nr 9

21--22

3

Zmiana właściwości dachówek ceramicznych i cementowych podczas eksploatacji pokryć dachowych

Francke B.

Materiały Budowlane

|

2015

|

nr 6

20--21

PL

W artykule omówiono wyniki badań przyspieszonego starzenia wykonane w ITB dla dachówek ceramicznych i cementowych. Uzyskane wyniki badań laboratoryjnych porównano z wynikami badań dachówek sezonowanych równolegle na daszkach próbnych, w warunkach naturalnych.

EN

The article discusses the results of artificial aging tests made by ITB for clay and concrete roofing tiles. The results of these tests were compared with the research results obtained for tiles exposed to weathering in service conditions.

4

Thermal Conductivity Coefficient of PUR Insulation Material from Pre-Insulated Pipes After Real Operation in District Heating Networks and After Artificial Ageing Process in Heat Chamber

Kręcielewska E., Menard D.

Ciepłownictwo, Ogrzewnictwo, Wentylacja

|

2015

|

T. 46, nr 2

46--52

EN

Pre-insulated pipelines, because of foam polyurethane (PUR) lifetime, are designed for 30 years of operation. During operation insulation foam is subject to natural process of ageing, resulting in changing of its basic thermal and mechanical properties. As a result of ageing, an increase (worsening) of insulation thermal conductivity coefficient follows. The Research Laboratory in Heat-Tech Center (LB HTC) from Veolia Energy Warsaw has started a research project, which aim is to determine actual values of thermal conductivity coefficient of pipe insulations, changing over time, under real operating conditions of the district heating network. The Laboratory also performs in parallel studies on insulation of preinsulated pipes after artificial ageing process according to the norm EN 253. The publication presents the results of the tests of thermal conductivity of PUR foam insulation of the pre-insulated pipe ageing in natural and artificial environments.

PL

Ze względu na żywotność pianki PUR rurociągi preizolowane projektowane są na 30 lat eksploatacji. Podczas pracy izolacja ulega procesowi naturalnego starzenia, zmieniają się jej podstawowe właściwości termiczne i mechaniczne. W wyniku starzenia się izolacji następuje wzrost (pogorszenie) współczynnika przewodzenia ciepła. Laboratorium Badawcze Heat-Tech Center (LB HTC) Veolii Energia Warszawa rozpoczęło projekt badawczy, którego celem jest określenie zmian wartości współczynnika przewodzenia w czasie, w rzeczywistych warunkach pracy sieci ciepłowniczej. Równolegle Laboratorium prowadzi badania izolacji z rur preizolowanych po procesie przyspieszonego starzenia zgodnie z normą EN253. Przedstawiono wyniki badań współczynnika przewodzenia ciepła izolacji z pianki PUR z rur preizolowanych starzonych w środowisku naturalnym i sztucznym. Artykuł był przedstawiony na konferencji w Sztokholmie.

5

Starzenie powłok malarskich

Pałasz A.

Materiały Budowlane

|

2014

|

nr 12

24--25

6

Współczynnik przewodzenia ciepła izolacji w rurach preizolowanych po naturalnym i sztucznym starzeniu

Kręcielewska E., Menard D.

Instal

|

2014

|

nr 11

14--20

PL

Ze względu na żywotność pianki PUR rurociągi preizolowane projektowane są na 30 lat eksploatacji. Podczas pracy izolacja ulega procesowi naturalnego starzenia, zmieniają się jej podstawowe właściwości termiczne i mechaniczne. W wyniku starzenia się izolacji następuje wzrost (pogorszenie) współczynnika przewodzenia ciepła. Laboratorium Badawcze Heat-Tech Center (LB HTC) Dalkii Warszawa rozpoczęło projekt badawczy, którego celem jest określenie zmian wartości współczynnika przewodzenia w czasie, w rzeczywistych warunkach pracy sieci ciepłowniczej. Równolegle Laboratorium prowadzi badania izolacji z rur preizolowanych po procesie przyspieszonego starzenia zgodnie z normą EN253. Publikacja przedstawia wyniki badań współczynnika przewodzenia ciepła izolacji z pianki PUR z rur preizolowanych starzonych w środowisku naturalnym i sztucznym.

EN

Preinsulated pipelines, because of foam polyurethane (PUR) lifetime, are designed for 30 years of operation. During operation insulation foam is subject to natural process of ageing, resulting in changing of its basic thermal and mechanical properties. As a result of ageing, an increase (worsening) of insulation thermal conductivity coefficient follows. The Research Laboratory in Heat-Tech Center (LB HTC) from Dalkia Warsaw has started a research project, which aim is to determine actual values of thermal conductivity coefficient of pipe insulations, changing over time, under real operating conditions. Laboratory also performs in parallel studies on insulation of preinsulated pipes after artificial ageing process according to norm EN 253. The publication presents the results of the tests of thermal conductivity of PUR foam insulation of the pre-insulated pipe ageing in natural and artificial environments.

7

Poprawa logistyki i bezpieczeństwa przesyłu prądu elektrycznego w przewodach napowietrznych, poprzez zwrócenie uwagi na obróbkę cieplną oraz odporność reologiczną drutów ze stopu AlMgSi

Korzeń K., Knych T., Smyrak B.

Logistyka

|

2013

|

nr 4

PL

Łańcuchem wiążącym wytwórcę prądu elektrycznego, a jego odbiorców są napowietrzne przewody elektroenergetyczne. To jak efektywny będzie przesył energii elektrycznej decydować będzie przede wszystkim materiał oraz konstrukcja przewodów. Problem ten jest ściśle powiązany z zadaniami logistycznymi operatorów sieci elektroenergetycznych na całym świecie, którzy muszą spełniać obecne i przyszłe wymagania konsumentów na ilość dostarczanej energii elektrycznej. Dane statystyczne ostatnich lat wykazują bowiem permanentny wzrost zapotrzebowania na energię elektryczną z poziomu 904,57 kWh (1960 rok) do 3783,08 kWh (2010 rok) na osobę w Polsce. Przy obecnym założeniu, iż średni czas eksploatacji linii elektroenergetycznych powinien być na poziomie 30–35 lat, okazuje się, iż polski system sieci w ponad 70% jest przestarzały, co za tym idzie, jest nie wydajny. Konieczne są, zatem, natychmiastowe działania logistyczne mające na celu poprawę efektywności, intensywności, a także bezpieczeństwa przesyłu prądu elektrycznego. W tym celu należy zwrócić uwagę przede wszystkim na materiał, z jakiego wykonane są przewody elektroenergetyczne, aby charakteryzował się on wysokimi własnościami mechanicznymi, elektrycznymi, a także eksploatacyjnymi (odporność cieplna, reologiczna i zmęczeniowa). Zaprojektowanie i przebadanie drutów z takiego materiału, który później mógłby być wykorzystany w przewodach elektroenergetycznych jest głównym celem niniejszej pracy.

EN

Overhead conductor lines connect the manufacturers of electric current with its customers. How the transmission of electricity will be effective will be decide primarily material and construction of wires. This problem is closely related to the tasks of logistics operators of power grids around the world, who must meet the current and future demands of consumers on the amount of supplied electricity. Statistical data for recent years show a permanent increase in the demand for electricity from 904.57 kWh (1960 years) to 3783.08 kWh (2010 years) per capita in Poland. With the current assumption that the average life of the power lines should be at the level of 30 - 35 years, it turns out that the Polish system of networks in more than 70% is outdated, hence, it is not efficient. It is necessary to immediate logistics operations to improve efficiency, intensity, and security of electricity transmission. For this purpose, it should be noted first of all the material they are made of the conductors that was characterized by a high mechanical properties, electrical and consumable (heat resistant, rheological and fatigue). Design and testing wires with such material, which later could be used in power lines is the main aim of this work.

8

Badania wpływu parametrów starzenia sztucznego walcówki z przewodowego stopu AlMgSi na kształtowanie się umacniania drutów w procesie ciągnienia

Smyrak B., Knych T., Osuch P., Nalborski Ł., Słaby P., Korzeń K.

Hutnik, Wiadomości Hutnicze

|

2011

|

Vol. 78, nr 1

127-129

PL

W artykule przedstawiono wyniki badań wpływu parametrów obróbki cieplnej drutów ze stopu AlMgSi gat. 6201 na ich finalne własności. Wyniki badań i ich analiza zostały podzielone na dwie części. Pierwsza dotyczy wpływu temperatury i czasu starzenia sztucznego na własności wytrzymałościowe walcówki wykonanej ze stopu AlMgSi (gat. 6201). Z kolei druga część, ukierunkowana jest na badania dotyczące kształtowania się umocnienia w procesie ciągnienia drutów AlMgSi wykonanych z tego samego gatunku stopu, po różnej obróbce cieplnej, której parametry zostały wyselekcjonowane po analizie wyników części pierwszej dotyczącej walcówki.

EN

The paper presents results of a study of the impact of artificial ageing parameters of 6201 grade AlMgSi alloy wires on their final properties. The study results are presented and discussed in two parts. The first part addresses the impact of artificial aging temperaturę and duration on the strength properties of AlMgSi alloy wire rod. The second part is focused on hardening development in the process of drawing of a AlMgSi wire made of the same alloy grade, subjected to different thermal treatments, the parameters of which have been selected based on analysis of the results of the first, wire-rod related, part of the study.

9

Badania wpływu czasu starzenia naturalnego walcówki z przewodowego stopu AlMgSi (seria 6xxx) na elektryczno-mechaniczne własności drutu osiągane w procesie końcowej obróbki cieplnej

Knych T., Mamala A., Smyrak B., Tarasek A.

Rudy i Metale Nieżelazne

|

2004

|

R. 49, nr 9

456-461

PL

Przedstawiono zagadnienie wpływu czasu starzenia naturalnego walcówki z przewodowego stopu AlMgSi gat. 6201 (wg PN-EN 515 stan T4) na zmianę własności mechanicznych i elektrycznych drutów w procesie końcowej obróbki cieplnej. Program obejmuje czternaście akcji badawczych prowadzonych systematycznie po określonym interwale czasu starzenia naturalnego walcówki. Stwierdzono zmienność własności wytrzymałościowych drutów starzonych sztucznie w analogicznych warunkach, lecz wytworzonych z walcówki po różnym czasie starzenia naturalnego. Wpływ starzenia naturalnego walcówki ujawnia się najmocniej w okresie pierwszego miesiąca oczekiwania materiału na ciągnienie. Uzyskane wyniki posiadają duże walory poznawcze i praktyczne umożliwiające lepsze zrozumienie zachowania się stopu AlMgSi podczas procesu przetwarzania na drut po stabilizacji własności walcówki oraz stabilizacji własności elektrycznych drutów ciągnionych z walcówki po długim czasie starzenia.

EN

The paper presents correlation natural ageing of AlMgSi conductor alloy rod and properties of material during artificial ageing of final wire. Satisfactory natural rod ageing process is fundamental due to quality of final wire. The problem is very important because natural ageing of rod is long-time element of making wire technology. Material for testing was classic continuously cast and rolled 9.5 mm diameter rod. After rolling process the rod was homogenized, supersaturated and naturally aged during different period of time. Next the rod was drawn in laboratory condition up to 3 mm diameter wire (as a standard and occasionally different diameters of wires), which was artificial aged up to eight hours at temperature about 160 degrees centigrade. The article shows the results of investigations on the influence of rod's natural ageing process on behaviours of wire during artificial ageing. It states significant effect on mechanical properties of wires and less significant effect on electric properties of wires during ageing. Dispensable time for maximal growth of tensile strength of aged wire decreases with increase natural ageing time of rod before drawing. Electrical resistance of wire during artificial ageing decreases continuously during rise period of ageing time. Essential influence of natural ageing time of wire during first month of rod ageing time is shown. In conclusion it should be minimal ageing time of rod in factory conditions.

10

Flexible plastic explosives with rubber NBR during artificial ageing

Chovancová M., Očko P., Lazar M., Lisý J., Lopúch J.

Problemy Techniki Uzbrojenia

|

2003

|

R. 32, z. 86

13--22

EN

This paper investigates chemical and thermal stability of flexible PBX's during their artificial ageing in term of their similar plastic binder. It was documented, they contain the rubber NBR and the similar base (RDX, PETN or RDX with PETN), but they don't have equivalent behaviour during the artificial ageing. It was discovered one from them is chemically unstable, because probably the rubber NBR is incompatible with RDX.

11

Wpływ obróbki cieplnej na własności laserowo spawanego stopu na bazie Al-Li.

Twardowska A., Kusiński J.

Inżynieria Materiałowa

|

1999

|

R. XX, nr 5

335-338

PL

Przeprowadzono statystyczną próbę wytrzymałości na rozciąganie stopu Al-Li-Cu-Mg-Zr spawanego laserem CO2 jak i nie spawanego, technologiczną próbę zginania spoin, pomiary mikrotwardości oraz badania mikrostruktury za pomocą mikroskopu optycznego, elektronowego skaningowego i elektronowego transmisyjnego. Pomimo, że materiał spawany charakteryzował się niższymi własnościami wytrzymałościowymi (Rm=268 MPa i A=3,7% ) niż materiał nie spawany (RM=487 MPa i A=17,48%), w próbie zginania (rozciągane lico spoiny) z łatwością osiągnięto kąt 180 stopni. Starzenie po spawaniu powodowało stopniowy spadek wytrzymałości na rozciąganie i wzrost plastyczności spawanego i nie spawanego materiału z czasem starzenia. Starzenie poprzedzone przesycaniem powodowało wyraźną poprawę wytrzymałości jak i plastyczności materiału spawanego, natomiast niewielki spadek wytrzymałości i wzrost plastyczności materiału osnowy.

EN

An Al-Li-Cu-Mg-Zr alloy was welded with CO2 laser to produce full-penetration, single pass butt welds. Initial YS of 487 MPa for unwelded material decreased to 268 MPa after laser welding as well as the measured elongation decreased from 17.48% to 3.7% respectively. The postweld heat treatment consisting of solutionizing at 550C for 2h and/or artificial ageing at 150C, 175C, 200C and 225C for 2h, 4h, 8h, 16h and 32h were performed to improve the properties of welded material. Studies by optical, scanning and transmission electron microscopies were provided in: as-welded, as-heat-treated, and as-deformed states to show the microstructural changes with postweld heat treatment.