Low-temperature powder paint modified with graphene oxide

Pojnar Katarzyna, Pilch-Pitera Barbara, Roś Natalia, Florczak Łukasz

Ochrona przed Korozją

|

2024

|

nr 2

30--39

EN

The aim of this study was to obtain low temperature polyurethane powder paint based on a thermosetting acrylic resin modified with graphene oxide (GO) and to investigate the protective properties of the coatings. The acrylic resin was synthesised by the radical copolymerisation reaction of 2-hydroxyethyl methacrylate (HEMA), methyl methacrylate (MMA) and n-butyl acrylate (BA). Graphene oxide was added to the resin at the synthesis stage in appropriate amounts by weight (so-called in situ method). An optimal amount of added graphene oxide of 0.5 wt% had a significant effect on the final result. Thanks to the use of a commercial crosslinker (VESTANAT B 1358/100), the coatings cured at a relatively low temperature (160°C). The curing process of the coatings was studied by differential scanning calorimetry (DSC). The cross-linked coatings were examined for appearance, physical and chemical properties, and resistance to corrosive media by electrochemical impedance spectroscopy (EIS). The presence of a modifier in the form of graphene oxide increased the hardness, scratch resistance, ductility, contact angle and resistance to corrosive media of the coatings obtained.

PL

Celem badań opisanych w artykule było otrzymanie niskotemperaturowych poliuretanowych powłok proszkowych na bazie termoutwardzalnej żywicy akrylowej modyfikowanej tlenkiem grafenu (GO) oraz określenie właściwości ochronnych powłok. Żywica akrylowa została zsyntezowana w reakcji kopolimeryzacji wolnorodnikowej metakrylanu 2-hydroksyetylu (HEMA), metakrylanu metylu (MMA) i akrylanu n-butylu (BA). Tlenek grafenu został dodany do żywicy na etapie syntezy w odpowiednich ilościach wagowych (metodą in situ). Istotny wpływ na wynik końcowy miała optymalna ilość dodanego tlenku grafenu – na poziomie 0,5% wag. Dzięki zastosowaniu komercyjnego środka sieciującego VESTANAT B 1358/100 powłoki utwardzały się w stosunkowo niskiej temperaturze (160°C). Przebieg procesu utwardzania powłok badano za pomocą różnicowej kalorymetrii skaningowej (DSC). Usieciowane powłoki analizowano pod kątem wyglądu, właściwości fizykochemicznych oraz odporności na media korozyjne, wykonując pomiar metodą elektrochemicznej spektroskopii impedancyjnej (EIS). Obecność modyfikatora w postaci tlenku grafenu zwiększyła twardość, odporność na zarysowanie, tłoczność, kąt zwilżania oraz odporność na media korozyjne otrzymanych powłok.

2

Ocena właściwości antykorozyjnych powłok konwersyjnych wytworzonych na magnezie i jego stopach w procesie elektrolitycznego utleniania plazmowego– przegląd

Florczak Łukasz

Ochrona przed Korozją

|

2021

|

nr 10

320--331

PL

W pracy wskazano na wciąż duże zainteresowanie magnezem i jego stopami z Al, Zn, Mn, Zr oraz pierwiastkami ziem rzadkich oraz krótko opisano kierunki aktualnych badań dotyczących metody elektrolitycznego utleniania plazmowego (PEO) jako metody zwiększającej odporność antykorozyjną stopów magnezu. Zaprezentowano metody pomiarowe służące do oceny właściwości antykorozyjnych powłok konwersyjnych wytworzonych w procesie PEO na magnezie i jego stopach. Opisano zalety i wady metod nieelektrochemicznych i elektrochemicznych, w tym: test w komorze solnej, test zanurzeniowy (ocena wyglądu, ubytek masy, zbieranie wodoru) oraz pomiary potencjału obwodu otwartego (OCP), polaryzacji potencjodynamicznej (PDP), analizę Motty-Schottky’ego oraz elektrochemiczną spektroskopię impedancyjną (EIS). Wykazano przewagę techniki EIS nad niszczącymi pomiarami elektrochemicznymi, która pozwala na prowadzenie nieniszczących pomiarów długoterminowych wytworzonych powłok ochronnych. Dokonano przeglądu roztworów korozyjnych, najczęściej stosowanych do oceny właściwości antykorozyjnych powłok konwersyjnych oraz wskazano rozcieńczony roztwór Harrisona (DHS), jako odpowiednie medium do badań cienkich powłok (~10 μm) wytworzonych metodą PEO na stopach magnezu przeznaczonych do zastosowań w warunkach przemysłowych. Zwrócono uwagę na konieczność właściwego doboru czasu trwania pomiarów korozyjnych w zależności od właściwości powłoki oraz jej potencjalnego zastosowania.

EN

The paper shows the unfailing interest in magnesium and its alloys with Al, Zn, Mn, Zr and rare earth elements, and briefly describes the directions of current research on the method of plasma electrolytic oxidation (PEO) as a method of increasing the corrosion resistance of magnesium alloys. The measurement methods for the assessment of anti-corrosion properties of conversion coatings produced in the PEO process on magnesium and its alloys are presented. Described are the advantages and disadvantages of non-electrochemical and electrochemical methods, including: salt spray test, immersion test (assessment of appearance, weight loss, hydrogen collection) and measurements of the open circuit potential (OCP), potentiodynamic polarization (PDP), Motta-Schottky analysis and electrochemical impedance spectroscopy (EIS). The advantage of the EIS technique over destructive electrochemical measurements has been demonstrated, which allows for non-destructive long-term measurements of the produced protective coatings. The most common corrosive solutions used to assess the anti-corrosive properties of conversion coatings were reviewed and the diluted Harrison solution (DHS) was indicated as a suitable medium for testing thin coatings (~10 μm) produced by the PEO method on magnesium alloys intended for use in industrial conditions. The necessity of proper selection of the duration of corrosion measurements depending on the properties of the coating and its potential application has been pointed out.

3

Wpływ molibdenianów na właściwości antykorozyjne żywicy epoksydowej

Trela J., Scendo M., Leszczyńska A., Kania M., Kluska K., Czajkowski J., Pauli R.

Zeszyty Naukowe Politechniki Świętokrzyskiej. Nauki Techniczne

|

2014

|

Z. 18

282--290

PL

Zbadano wpływ stężenia kwasu molibdenowego(VI) (H2MoO4) oraz molibdenianu(VI) amonowego ((NH4)6Mo7O24) na właściwości antykorozyjne żywicy epoksydowej Epidian 115. Zawartość molibdenianów w żywicy wynosiła: 1, 5 i 10% wagowych. Środowiskokorozyjne stanowił 1,1 M roztwór chlorków. Do badań korozyjnych zastosowano stal węglową S355. Badania prowadzone były metodą grawimetryczną. Na podstawie otrzymanychwyników stwierdzono, że korozja próbek stali S355 przebiegała według złożonego,wieloetapowego mechanizmu z udziałem rozpuszczonego tlenu i jonów chlorkowych. Badania wykazały, że najbardziej odporne na działanie agresywnego środowiska elektrolitu okazały się powłoki zawierające w składzie żywicy 10% wag. kwasu(VI) molibdenowego.

EN

The effects of concentration of acid molybdenum(VI) (H2MoO4) and molybdate(VI) ammonium ((NH4)6Mo7O24) on the anticorrosion properties of an epoxy resin anticorrosive EPIDIAN 115 was studied. The concentration of molybdates in the resin were as follows: 1, 5 and 10% wt. Corrosive environment was a 1.1 M sodium chloride. To the corrosion tests were used carbon steel S355. Research was carried out by the gravimetric method. Based on the obtained results it was found that the corrosion samples S355 proceeded according to a complex, multi-step mechanism involving dissolved oxygen and chloride ions. Research showed that the most resistant to aggressive environments was layer composed of a resin containing 10% by weight of molybdenum(VI) acid.

4

Antykorozyjne powłoki lakierowe nowej generacji

Zubielewicz M., Gnot W.

Ochrona przed Korozją

|

2005

|

nr 4

98-100

PL

Omówiono nowe rozwiązanie w dziedzinie antykorozyjnych powłok lakierowych, z uwzględnieniem spoiw hybrydowych o bardzo dobrych właściwościach barierowych oraz nanotechnologii. Powłoki ochronne nowej generacji nie zawierają pigmentów antykorozyjnych a ich skuteczność ochronną zapewnia struktura, hamująca dostęp czynników agresywnych do podłoża.

EN

New solutions in the field of anticorrosion coatings including hybrid binders with excellent barrier properties and nanotechnologies have been described. The new generation of protective coatings does not contain anticorrosion pigments and their effectiveness is ensured by a structure, which impedes the penetration of aggressive agents into the substrate.

5

Impregnowanie warstw azotowanych zwiększających odporność na zużycie przez tarcie i korozję.

Senatorski J., Tacikowski J., Iwanow J.

Inżynieria Materiałowa

|

2000

|

R. XXI, nr 6

427-429

PL

W referacie omówiono cel, metodykę i wyniki badań własności tribologiczno-antykorozyjnych cienkich warstw azotowanych (12,5 mikrometra) otrzymywanych na stali 45 w procesie regulowanego azotowania gazowego (570 stopni Celsjusza, 4 h), impregnowanych preparatami olejowymi, zawierającymi inhibitor BS-43, modyfikowany dodatkami tribologicznymi opartmi na popiołowych związkach metaloorganicznych oraz bezpopiołowych związkach organicznych. Stwierdzono, że dodatki tribologiczne nie rzutują w istotny sposób na kształtowanie się odporności na korozję warstw azotowanych impregnowanych preparatami olejowymi, związane głównie z inhibitorem BS-43. Współdziałanie dodatku tribologicznego i inhibitora korozji wyraźnie zaznacza się natomiast w kształtowaniu się odporności na zużycie przez tarcie warstwy azotowanej. Charakter oddziaływania dodatków tribologicznych w skojarzeniu z inhibitorem korozji BS-43 wiąże się z ich rodzajem i w efekcie poprawieniem lub pogorszeniem się odporności warstw azotowanych na zużycie przez tarcie. Stąd o wyborze preparatu impregnującego, umożliwiającego spełnienie wymagań tribologiczno-antykorozyjnych, decyduje przede wszystkim dodatek tribologiczny.

EN

The aim, methodology and test results of tribological - anticorrosion properties of thin nitrided layer (12,5 micrometer), obtained on 45 steel grade in controlled gas-nitriding process (570 degrees centigrade, 4h), impregnated with oil-based formulations, containing corrosion inhibitor BS-43, modified with tribological additives based on ashen organometalic compounds as well as ash-free organic compounds are described in the work. It was stated, that tribological additives don't influence, the corrosion resistance of nitrided layers impregnated with oil-base formulations mainly connected with inhibitor BS-43. Synergy of tribological additives and corrosion inhibitor is however more visible in modelling the wear resistance of nitrided layer. The way of influence of tribological additives combined with corrosion inhibitor BS-43 is connected with their kind and one may obtain betterment or worsening of the wear resistance. Hence in choice of impregnated formulation, which would enable to accomplish of tribological - anticorrosion requirements, tribological additive plays the crucial role.