Wyniki wyszukiwania - BazTech

1

The Influence of Chosen Abrasive Wear Parameters on Fault-free Operation Time of the Cylinder-Piston System

Piątkowski J., Mesjasz A.

Archives of Foundry Engineering

|

2015

|

Vol. 15, iss. 3 spec.

69--72

EN

In the paper the method of data modeling for damages, that has values higher than zero, is being shown. With the use of Weibull distribution, with prior regression and correlation analysis, the chosen parameters, that define durability and break down level of two populations of AlSi17Cu5Mg, were set. The calculation sheet that is shown for reliability allows the creation of so called survival chart, and on the basis of durability data the average warrantee time can be defined at the pre-exploitation stage.

2

Data Simulation with the Use of Weibull Analysis for Evaluation of Reliability of Chosen Assortment

Piątkowski J., Mesjasz A.

Archives of Foundry Engineering

|

2015

|

Vol. 15, iss. 3

47--50

EN

In the dissertation the data modeling has been shown for the data that regards the damages, which value is above zero. With the use of Weibull distribution, with prior regression and correlation analysis chosen parameters that defines the life time and failure level of two populations of AlSi17Cu5 were defined. The calculation sheet of reliability allows to create so called survival diagram, and on the basis of durability data the average warrantee can be determined, on the pre-exploitation period.

3

Effect of vortex runner gating system on the mechanical strength of Al-12SI alloy castings

Ahmad R., Hashim M. Y.

Archives of Metallurgy and Materials

|

2011

|

Vol. 56, iss. 4

991-991

EN

Gating system design is an essential element in casting process which affects significantly the molten metal flow behavior, heat transfer and solidification of the melt. Optimum gating design will lead to a good quality of casting product. One of the major components in gating system is runner. This study was conducted to determine the effect of vortex runner diameter gating system on the mechanical strength of Al-12Si alloy casting. Simulation was conducted to study the behavior of the fluid flow and the results obtained showed close agreement with the results obtained from the experiment. Experimental results showed that the casting product with bigger vortex runner diameter gating system led to the improvement of average bending strength.

PL

Układ wlewowy to podstawowy element w procesie odlewania, który znacząco wpływa na płynięcie ciekłego metalu, transport ciepła oraz krzepnięcie metalu. Optymalny układ wlewowy gwarantuje dobra jakość odlanego produktu. Jednym z głównych elementów układu wlewowego jest kanał wlewowy. Celem pracy było zbadanie wpływu średnicy kanału układu wlewowego na wytrzymałosc mechaniczna odlewów ze stopu Al-12Si. Celem zbadania zachowania przecieczy przeprowadzono symulacje i otrzymane wyniki wykazują dobrą zgodność z wynikami otrzymanymi doświadczalnie. Wyniki doswiadczeń pokazały, że zastosowanie większej srednicy kanału układu wlewowego prowadzi do poprawy średniej wytrzymałości odlewów na zginanie.

4

Determination of weibull analysis of the hypereutectic silumins reliability in failure time respect

Szymszal J., Piątkowski J., Mikuszewski T., Maliński M.

Archives of Foundry Engineering

|

2009

|

Vol. 9, iss. 3

195-200

EN

The results of dynamic evaluation of the reliability of hypereutectic AlSi17Cu3NiMg silumin under the effect of symmetrical cyclic tensile-compressive stresses were presented. Studies were carried out on a normal-running fatigue testing machine, which was the mechanically driven resonant pulsator. For the needs of quantitative reliability evaluation and the time-to-failure evaluation, the procedures used in survival analysis, adapted to the analysis of failure-free operation with two- and three-parametric Weibull distributions, were applied. The values of the parameters were estimated using the method of maximum reliability and a rank-based non-parametric method. The results of the evaluation of the reliability and damage intensity are an important element in the determination of casting quality and enable a reliable estimation of the operational suitability time.

5

Mechanical properties of Fe-3Mn-0.8C sintered steel based on sponge and atomised iron powders; Comparison and probabilistic failure prediction

Faryj K., Ciaś A.

Archives of Metallurgy and Materials

|

2008

|

Vol. 53, iss. 3

817-826

EN

This paper presents a systematic approach to study the effect of manufacturing variables on the mechanical properties of sintered Fe-3Mn-0.8C steel. Tensile and 3 point bending tests have been performed on specimens madę of three different iron powders with variations of sintering conditions. Ferro-manganese and graphite powders were admixed to Hoganas sponge, NC100 24, and water atomised, ABC 100.30 and ASC 100.29, iron powders - to produce three variants of Fe-3Mn-0.8C mixtures. The powders were pressed into specimens at 660 MPa, sintered in semi-closed containers for 1 h in dry nitrogen or hydrogen at 1120 or 1250°C, and cooled at 64°C/min. Green and sintered densities were expectedly highest for ABC 100.30 powder at ~7.1 g/cm3. They were >0.2 g/cm3 higher than for the sponge powder based specimens. Similarly, Young's modulus in the former materiał attained ~130 GPa, being ~117 GPa in the latter. Yield strengths were higher for the atomised powder based alloys and for 1250°C and nitrogen sintering. Tensile and bend strengths were somewhat higher for specimens sintered in nitrogen and, generally by ~10%, higher for specimens pressed from sponge iron powder, resulting in ~730 MPa tensile strength for sintering in nitrogen at 1250°C. The strongest ABC 100.30 powder based specimens attained tensile strength ~650 MPa. The higher plasticity of the sponge powder based steel and hence strengths are associated with the increased surface area available to the Mn vapour for alloying. This ensures also cleaner, morę cohesive prior powder particie boundaries, the favoured microcracking paths. The study of fracture stress is based on a statistical strength theory suggested by Weibull. lt enables fracture probability to be calculated as a function of applied stress. The paper shows that Weibull distribution is morę applicable to the strength evaluation and failure statistics of PM steels than the morę commonly used normal distribution.

PL

W artykule zaprezentowano systematyczne badania wpływu warunków wytwarzania na własności mechaniczne spiekanych stali Fe-3%Mn-0,8%C. Badania wytrzymałości na rozciąganie i zginanie trójpunktowe przeprowadzono przy użyciu próbek spiekanych w różnych warunkach, wykonanych z trzech różnych proszków żelaza. W celu otrzymania próbek Fe-3%Mn-0,8%C, do redukowanego, gąbczastego proszku żelaza gatunku Hoganas NC 100.24, oraz do rozpylanych proszków żelaza gatunków Hoganas ABC 100.30 i ASC 100.29, wprowadzono mangan w ilości 3%, w postaci proszku żelazomanganu niskowęglowego, oraz grafit w ilości 0,8%. Z proszków sprasowano pod ciśnieniem 660 MPa próbki, które poddano następnie spiekaniu w półhermetycznym pojemniku, w czasie 1 h, w suchym azocie lub wodorze, w temperaturze 1120 lub 1250°C; próbki chłodzono z prędkością 64<,C/min. Zgodnie z oczekiwaniami, gęstość tak wyprasek, jak i spiekanych stali była najwyższa w przypadku próbek wytworzonych z proszku ABC 100.30 i wynosiła ~7.1 g/cm3. Była ona o ponad 0,2 g/cm3 wyższa, niż gęstość spieków wykonanych z proszku gąbczastego. Podobnie moduł Younga, który osiągał w przypadku pierwszej stali ~130 GPa, podczas gdy w przypadku drugiej ~117GPa. Wartości umownej granicy plastyczności były wyższe w przypadku spieków otrzymanych z rozpylanego proszku żelaza - oraz dla próbek spieczonych w azocie - i próbek spieczonych w temperaturze 1250°C. Wytrzymałość na rozciąganie i zginanie trójpunktowe próbek spieczonych w azocie była wyższa, średnio o ~10%, niż próbek otrzymanych z gąbczastego proszku żelaza, osiągając ~730 MPa w przypadku wytrzymałości na rozciąganie próbek spieczonych w azocie, w temperaturze 1250°C, podczas gdy najmocniejsze próbki wykonane z proszku ABC 100.30 osiągały ~650 MPa. Wyższa plastyczność stali wykonanej z proszku gąbczastego i wyższe jej wytrzymałości związana jest z powiększoną, dostępną dla par manganu, powierzchnią cząstek proszku, co ułatwia wnikanie do nich tego pierwiastka stopowego. Zapewnia to także czyste, bardziej spoiste pierwotne granice cząstek proszku, będące zazwyczaj uprzywilejowanymi ścieżkami mikropęknięć. Badania wytrzymałości oparto na teorii statystycznej zaproponowanej przez Weibulla. Umożliwia ona obliczenie prawdopodobieństwa powstania przełomu w funkcji występującego naprężenia. W artykule wykazano, że do szacowania wytrzymałości stali wytworzonych techniką metalurgii proszków - i do statystycznego opisu tej wytrzymałości -rozkład Weibulla jest bardziej odpowiedni niż, stosowany powszechnie, rozkład normalny.