The article presents the results of research of thermophysical peculiarities obtaining volumetric amorphous structures in metals and alloys. This technology differs mainly the realization internal heat removal by means of local heat sink (inoculator). A mathematical model of melting inoculator in melts for optimizing the process of obtaining massive amorphous structures, which allows to reduce time of experimental research and material resources to create massive amorphous structures. Mathematical modeling of processes heat and mass transfer inoculator in melts allows you to identify peculiarities of the technological process, and establish influence inoculator on the degree of amorphization melt. The results provide an effective assessment of the intensity of heat transfer during the casting process, which makes it possible to estimate and predict the ability of alloys to the amorphization of the structure.
2
Dostęp do pełnego tekstu na zewnętrznej witrynie WWW
The article presents the results of research of thermophysical peculiarities obtaining volumetric amorphous structures in metals and alloys. This technology differs mainly the realization internal heat removal by means of local heat sink (inoculator). A mathematical model of melting inoculator in melts for optimizing the process of obtaining massive amorphous structures, which allows to reduce time of experimental research and material resources to create massive amorphous structures. Mathematical modeling of processes heat and mass transfer inoculator in melts allows you to identify peculiarities of the technological process, and establish influence inoculator on the degree of amorphization melt. The results provide an effective assessment of the intensity of heat transfer during the casting process, which makes it possible to estimate and predict the ability of alloys to the amorphization of the structure.
The article presents the results of an experimental study of energy-resource saving technologies of formation of massive amorphous structure. Considered are the methods of mathematical modeling and optimization of process production of massive amorphous structures, which can reduce experimental studies and material resources to create a highly efficient production of amorphous alloys. The results of physical experiments are compared with the results of the calculation. Received results can be used to analyze the physical regularities and justified choice of technological modes of formation of amorphous structures.
The aim of this paper was to investigate the corrosion resistance of Mg66Zn30Ca4 and Mg68Zn28Ca4 metallic glasses and evaluate the ability of this amorphous alloy use for medical applications as biodegradable medical implants. Taking into account the amount of Mg, Zn, Ca elements dissolved in multielectrolyte physiological fluid (MPF) from Mg66+xZn30-xCa4 (x=0.2) alloys the daily dose of evolved ions from alloys components was determined. Additional goal of the paper was determination of corrosion rate (Vcorr) and amount of hydrogen evolved from amorphous magnesium alloys in simulated environment of human body fluids during 24h immersion and during electrochemical tests. Corrosion studies were done in the multielectrolyte physiological fluid (MPF) at 37°C. The amount of hydrogen evolved [ml/cm2] and corrosion rate Vcorr [mm/year] of amorphous Mg66Zn30Ca4 and Mg68Zn28Ca4 alloys were compared. The work also presents characterization of Mg-based bulk metallic glasses structure in the form of 2 mm thickness plates. Samples structure was analyzed by means of X-ray diffraction. Fracture and surface morphology of magnesium alloy samples were identified using scanning electron microscopy.
W pracy przedstawiono przykładowe wyniki badań właściwości magnetycznych oraz struktury kompozytów zbudowanych z żywicy epoksydowej Epidian 100 oraz amorficznego wypełniacza o właściwościach magnetycznych magnetycznie miękkich. Na podstawie analizy badań struktury wykonanych za pomocą dyfraktometru rentgenowskiego można stwierdzić, że badane kompozyty posiadały strukturę amorficzną, co w rezultacie jest potwierdzeniem amorficzności metalicznego wypełniacza. Podstawowe parametry opisujące materiał magnetycznie miękkie, tj. magnetyczna polaryzacja oraz pole koercji w badanych kompozytach zmieniają się w zależności od ilości diamagnetycznego lepiszcza lub frakcji stosowanego wypełniacza. W przypadku kompozytów magnetycznych już niewielka ilość diamagnetycznej żywicy epoksydowej Epidian 100 jest powodem gwałtownego pogorszenia parametrów magnetycznie miękkich.
EN
The paper presents an example of the results of the magnetic properties and structure of composites made of epoxy resin Epidian 100 and amorphous filler with magnetically soft magnetic properties. From the structure analysis made using the X-ray diffractometer can be concluded, that the examined composites had an amorphous structure, which in turn confirms the amorphous content of the filler metal. The basic parameters describing the soft magnetic material, i.e. magnetic polarization and the coercive field in the studied composites vary depending on the amount of binder or on diamagnetic fraction of the filler used. In the case of magnetic composites even a small quantity of Epidian 100 diamagnetic epoxy resin causes rapid deterioration of soft magnetic parameters.
W pracy przedstawiono wyniki badań kompozytów składających z ferromagnetyka Fe61Co10Y8W1B20 wykazującego miękkie właściwości magnetyczne związanego polimerem (Epidian 100) w proporcjach 2%, 3% i 4% wag. Przeprowadzono badania struktury wykorzystując dyfrakcje promieni rentgenowskich. Na podstawie tych badań wykazano że proces mielenia jak i utwardzania Epidianu w nie wpływa na strukturę badanych kompozytów powodując jej krystalizację. W kolejnym etapie przeprowadzono badania magnetyczne wykorzystując magnetometr wibracyjny (VSM). Pokazano, że można sterować właściwościami poprzez odpowiednie dobranie zawartości osnowy polimerowej.
EN
This paper presents results of research on the composites consisting of ferromagnetic Fe61Co10Y8W1B20 alloy exhibiting soft magnetic properties of bonded polymer (Epidian 100) in the proportion of 2%, 3% and 4% by weight. Structure study was carried out using X-ray diffraction. This research have shown that the process of grinding and Epidianu hardening does not affect the structure of the composites causing its crystallization. In a next step were studied by using a vibrating sample magnetometer (VSM). It is shown that the properties can be controlled through appropriate selection of the content of the polymer matrix.
7
Dostęp do pełnego tekstu na zewnętrznej witrynie WWW
Celem pracy jest zbadanie odporności na korozję elektrochemiczną szkła metalicznego Mg36,6Cu36,2Ca27,2 w stanie bezpośrednio po odlaniu oraz po wygrzewaniu. W ramach pracy przeprowadzono badania struktury analizowanych próbek za pomocą badań rentgenowskich i mikroskopowych. W celu określenia szybkości roztwarzania badanego stopu Mg36,6Cu36,2Ca27,2 oraz jego przydatności do potencjalnych zastosowań biomedycznych przeprowadzono badania immersyjne i potencjodynamiczne odporności na korozję elektrochemiczną w płynie fizjologicznym (wieloelektrolitowym). Stwierdzono, że stop Mg36,6Cu36,2Ca27,2 o strukturze amorficznej charakteryzuje się znacznie wyższą odpornością korozyjną od stopu Mg36,6Cu36,2Ca27,2 o strukturze krystalicznej.
EN
The aim of this paper is to investigate the electrochemical corrosion resistance of metallic glass Mg36,6Cu36,2Ca27,2 in as-cast state and after annealing. In the work was carried out studies of the structure of the analyzed samples using X-ray diffraction and microscopic observation. In order to determine the dissolution rate of the tested alloy Mg36,6Cu36,2Ca27,2 and potential suitability for biomedical applications were carried out immersion test and potentiodynamic test electrochemical corrosion in a physiological fluid (electrolyte solution). It was found that Mg36,6Cu36,2Ca27,2 alloy with amorphous structure has a much higher corrosion resistance than the same alloy with crystalline structure.
8
Dostęp do pełnego tekstu na zewnętrznej witrynie WWW
In this work, 20 % aqueous suspensions of three commercial high performance inulin powders were prepared and subsequently heated, to study the effect of temperature on the rheological properties of obtained gels. Apparent viscosity, flow curves and frequency sweeps were measured. Moreover, the analysis of texture was carried out, where hardness (Fig. 1), adhesiveness (Fig. 2) and cohesiveness (Fig. 3) of the inulin gels were estimated. All the analysed samples had higher values of storage modulus (G') then loss modulus (G”) (Table 1, Fig. 4). Rotational rheometry showed that the examined gels revealed thixotropic (Fig. 6) and shear thinning behaviour (Fig. 5). Rheological properties of inulin gels were influenced by the structure properties of inulin powders and the preparation temperature. An increase in temperature caused a significant (p ? 0.05) drop in storage and loss moduli as well as a decrease in apparent viscosity values for the gels formed from inulin with amorphic structure. Inulin with crystalline structure was able to form stable gels only at high temperature.
PL
Z trzech handlowo dostępnych rodzajów wysokoprzetworzonej inuliny sporządzono 20-proc. zawiesiny w wodzie, po czym ogrzewano je i badano wpływ temperatury na właściwości reologiczne powstałych żeli. Analiza cech termoplastycznych wykazała, że wartości modułu zachowawczego (G‘) wszystkich badanych próbek żeli były większe niż wartości modułu stratności (G”). Za pomocą reometru rotacyjnego wykazano, że badane żele to układy rozrzedzane ścinaniem, o właściwościach tiksotropowych. Właściwości reologiczne żeli inulinowych wynikały z cech strukturalnych cząstek proszków inulinowych oraz zależały od temperatury przygotowania próbek. Wzrost temperatury powodował istotny (p ? 0,05) spadek wartości modułów zachowawczego i stratności a także lepkości pozornej żeli powstałych z inuliny o amorficznej budowie cząstek. Inulina o budowie krystalicznej tworzyła stabilne żele dopiero w wysokiej temperaturze.
Amorphous hydrogenated carbon-silicon (a-SixCy:H) films were produ- \ ced by plasma enhanced chemical vapor deposition (PECVD) in the audio-frequency (a.f.) three-electrode reactor using tetramethylsilane as a source compound. The negative amplitude of a.f. voltage, V, •., measured on a small electrode, on which the films were deposited, was tnę only operational parameter of the deposition process. Investigations of electrical conductivity, UV VIS optical absorption and Raman scattering were carried out for the films deposited at various V^. It was found that these films are composed of amorphous insulator (a-I) and amorphous semiconductor (a-S) fractions with different electronic structures. On the basis of Raman spectroscopy, it was shown that both sp2 C-C and Si Si bonds are created in the a-S fraction in contrast to the a-I fraction in which C-H groups dominate. A shift of the Si-C band position for a-I and a-S is also observed. Probably, it is connected with a transformation from polymer-like to tetra-hedral glasses structure.
PL
Amorficzne wodorowane cienkie warstwy węgiel-krzem (a-SixCY:H) otrzymywano przez plazmowe osadzane chemiczne z fazy lotnej w zakresie częstości akustycznych (cz.a.) w trój elektrodowym reaktorze z tetra-metylosylanu jako związku wyjściowego. Amplituda ujemna napięcia cz.a. V/j mierzona na małej elektrodzie, na której warstwy były osadzane, była jedynym parametrem zmiennym procesu osadzania. Badania przewodnictwa elektrycznego, absorpcja UV-VIS oraz rozpraszanie Ramana były przeprowadzone dla warstw otrzymanych przy różnych wartościach V,v Stwierdzono, że warstwy te złożone są z części amorficznego izolatora (a-I) i amorficznego półprzewodnika (a-S) o różnych strukturach elektronicznej. W oparciu o spektroskopię Ramana wykazano, że oba wiązania sp2 dla C-C oraz Si-Si powstają w strukturze a-S w przeciwieństwie do struktury a-I, w której dominujągrupy C-H. Obserwuje się także przesunięcie pasma od Si-C przy przejściu od a-I do a-S. Przypuszczalnie jest to wynikiem transformacji struktury szkłopodobnej.
W pracy przedstawiono możliwości zastosowania ceramiki hydroksyapatytowej jako cementu kostnego. Przedstawiono możliwości zwiększenia odporności korozyjnej stopów tytanu poprzez modyfikację składu chemicznego oraz zmianę stanu fizykochemicznego ich powierzchni. Przedstawiono wyniki badań strukturalnych warstw hydoksyapatytowych wytworzonych metodą zol-żel na powierzchni tytanu technicznego. Badaniom poddano warstwy o strukturze krystalicznej i amorficznej, z podwarstwą oraz bez podwarstwy SiO2. Wykazano, że badane warstwy są warstwami o charakterze dyfuzyjnym. Najlepszymi właściwościami charakteryzowały się warstwy o strukturze amorficznej. Obecność podwarstwy SiO2 wpływała na zahamowanie dyfuzji składników warstwy w głąb tytanu.
EN
In this work possibility of use of hydroksyapatite ceramic as osseous cement was introduced. Possibilities of increase of corrosive resistance of alloys of titanium were introduced across modification of chemical constitution as well as change of physicochemical state of them surface. Results of structural investigations of hydroksyapatite layers made by sol-gel method on technical titanium were introduced. Investigations layers were surrendered about crystalline structure and amorphous, with and without SiO2 underlayer. It was shown, that studied layers are layers about diffusive character. Best properties characterized amorphous layers. Presence of SiO2 underlayer influenced onto of titanium onto set - back of diffussion of components of layer.
The structural tranformations in FeAl-NbC, FeAl-Al2O3 and NiAl-Al2O3 composite powders obtained by mechanical alloying were studied. The milling process of a mixture of Fe, Al, Nb and graphite powders led to the formation of an amorphous structure. The crystallisation processes resulted in two-phase structure consisting of ordered FeAl intermetallic compound and NbC. Composite powders containing Al2O3 were formed due to the reduction reaction of hematite or nickel oxide by Al, during the ball milling process. All obtained composite powders revealed a nanocrystalline structure of both phases (intermetallic and alumina).
PL
W pracy przedstawiono wyniki badań strukturalnych proszków kompozytowych FeAl-NbC, FeAl-Al2O3 i NiAl-Al2O3 otrzymanych metodą syntezy mechanicznej. W przypadku kompozytu FeAl-NbC mieszaninę wyjściową stanowiły proszki Fe, Al, Nb i grafitu. Efektem procesu ich mielenia było utworzenie stopu o strukturze amorficznej. Jego krystalizacja prowadziła do uzyskania dwufazowej struktury FeAl-NbC. Proszki kompozytowe z Al2O3 formowały się w wyniku reakcji redukcji hematytu lub tlenku niklu za pomocą Al, w procesie mielenia odpowiednich mieszanin proszkowych. Uzyskane proszki kompozytowe charakteryzowały się nanokrystaliczną strukturą.
Composite ribbons with amorphous matrix and ceramic (SiC, WC, MoB) particles were produced by modified planar melt flow casting methods. Weldability, abrasive wear and wood sanding examinations were carried out in order to find optimal material and technology for elevated wear resistance and sanding durability. The correlation between structure and composite properties is discussed.