Annealing and hot deformation of Al-based composite hardened with niobium oxide dispersions.

Blaz L., Kaneko J., Sugamata M., Sierpiński Z., Tumidajewicz M.

Archives of Materials Science

|

2005

|

Vol. 26, nr 1-2

73-78

EN

A brief review of structural investigation and results of mechanical tests for mechanically alloyed Al-based composites is presented. As an example, the effect of annealing temperature on the structure and properties of Al-Nb2O5 composite was discussed. It was found that chemical reaction between components during aging at 873 K resulted in an increase of material porosity. Opposite effect of the local volume increase due to intermetallic grain growth was not efficient enough to eliminate the porosity of the annealed material. Annealing of the composite at 873 K was found to result in material hardening. The hardness maximum was observed for samples annealed for 12 h at 873 K. Following softening at prolonged annealing time was ascribed to the grain coarsening and increased porosity of the composite. High strength of the composite, suspected from highly refined structure of the material, was proved by hot deformation tests at 623-903 K.

2

Odkształcalność kompozytów na osnowie stopów aluminium wzmacnianych cząstkami węglika krzemu. Cz. I. Kompozyty - klasyfikacja, metody wytwarzania, własności mechaniczne, zastosowanie.

Kurtyka P., Płonka B., Wierzbiński S.

Rudy i Metale Nieżelazne

|

2000

|

R. 45, nr 1

23-28

PL

Na podstawie studiów literaturowych w artykule przedstawiono kryteria klasyfikacji kompozytów, rodzaje i formy faz zbrojących kompozyty z uwzględnieniem reakcji na granicy osnowa-faza zbrojąca. Omówiono także podstawowe zagadnienia związane z wytwarzaniem kompozytów, w tym głównie kompozytów na osnowie metalowej wzmacnianych cząstkami węglika krzemu, jak również metody oceny ich własności mechanicznych w aspekcie zastosowań przemysłowych.

EN

Criterions of composites' classification, the kinds and forms of the phases reinforcing composites, taking into account the reactions on the matrix-reinforcing phase are presented, grounded on literary studies. The principal problems bound with generation of composites, especially of metal-matrix ones, reinforced with particles of silicon-carbide, and the methods of evaluation of their mechanical properties for industrial applications are talked over.

3

Odkształcalność kompozytów na osnowie stopów aluminium wzmacnianych cząstkami węglika krzemu. Cz. III Wpływ warunków odkształcania na zdolność do odkształceń plastycznych w kompozytach AA2024/SiC(p).

Płonka B., Wierzbiński S.

Rudy i Metale Nieżelazne

|

2000

|

R. 45, nr 4

225-232

PL

Przedstawiono wybrane własności mechaniczne kompozytu AA2024/SiC(p) w aspekcie możliwości kształtowania plastycznego w warunkach wysokotemperaturowego odkształcania. Ponieważ osnowa kompozytu wykonana została ze stopu ulegającego przemianie fazowej, analizowano współdziałanie mechanizmów umocnienia odkształceniowego i wydzieleniowego w kontekście procesów odnowy strukturalnej - zdrowienia i rekrystalizacji dynamicznej. Ustalono optymalne warunki temperaturowo-prędkościowe kształtowania plastycznego kompozytu w szerokim zakresie temperatur i prędkości odkształcania oraz wzajemną relację pomiędzy mechanizmami umocnienia odkształceniowego i wydzieleniowego a procesami odnowy strukturalnej.

EN

Selected mechanical properties of the composite AA2024/SiC(p), are presented, in relation to its plastic formability, in conditions of high temperature deformation. The cooperation of the mechanism of deformation and precipitation strengthenings were analysed contextual with structural reconditioning-recovery and dynamic recrystallization, as the composite-matrix was an alloy being subject to phase change. The optimum conditions for thermal and velocity plastic formation of the composite within broad temperature and velocity ranges, die reciprocal relation between the mechanisms of deformation and precipitation strengthening and the processes of structural reconditioning were determined.

4

Odkształcalność kompozytów na osnowie stopów aluminium wzmacnianych cząstkami węglika krzemu. Cz. II Charakterystyki mechaniczne wysokotemperaturowego odkształcania kompozytu AA6061/SiC(p).

Kurtyka P.

Rudy i Metale Nieżelazne

|

2000

|

R. 45, nr 3

178-186

PL

Przedstawiono wyniki analizy charakterystyk mechanicznych wysokotemperaturowego odkształcania (sigma-epsilon) kompozytu na osnowie stopu aluminium AA6061 (PA45) zbrojonego cząsteczkami SiC o wielkości 1 i 8 mikrometrów. Na podstawie wyników badań ustalono zakresy temperatur i prędkości odkształcania, w których istnieje możliwość plastycznego kształtowania kompozytu, a także określono wybrane własności wytrzymałościowe kompozytu w podwyższonych temperaturach. Analizowano również współdziałanie mechanizmu umocnienia odkształceniowego i wydzieleniowego z procesami odnowy strukturalnej, w tym głównie zdrowienia i rekrystalizacji dynamicznej.

EN

The authors present the results of the analysis of mechanical characteristics of high-temperature strain (sigma-epsilon) of the aluminium alloy based composite AA6061(PA45), reinforced with 1 and 8 micrometres particles of SiC. The range of temperature, the deformation-velocities at which exists the ability of plastic formation of the composite and some selected thermal strength-qualities of the composite, at elevated temperatures, have been defined. The cooperation of the mechanism of deformation-reinforcement and structural restoration, chiefly that of recovery, and dynamic recrystallization have been analysed too.

5

Kompozyty z wiórów aluminium i jego stopów utwardzane żelazochromem.

Gronostajski J., Marciniak H., Matuszak A.

Mechanik

|

2000

|

R. 73, nr 12

862-865

PL

Przeprowadzono analizę wpływu fazy utwardzającej wprowadzonej do wiórów Al, PA2 i PA6 tworzących osnowę oraz parametrów technologicznych wytwarzania kompozytów na ich właściwości mechaniczne. Stwierdzono, że nagrzewanie w powietrzu nie powoduje istotnego utleniania powierzchni cząstek wiórów pogarszającego procesu ich spajania. Stosowanie atmosfery ochronnej lub próżni jest wiec niecelowe. Krzywe umcnienia kompozytów w temperaturze 20, 150, 300 i 450 stopni C charakteryzują sie stale rosnącymi wartościami naprężenia w funkcji odkształcenia zarówno w niskiej, jak i w wysokiej teperaturze. Badania metalograficzne wykazały, że w wyniku dużych odkształceń plastycznych, niszczących warstwę tlenków na powierzchni wiórów i umożliwiających dyfuzyjny transport materii orzymano materiał niemal całkowicie pozbawiony nieciągłości. Gęstości względne kompozytów po wciskaniu na gorąco osiągają wartości powyżej 98%.

EN

Analysis of the infuence of the hardening phase introduced into the chips Al, Pa2 and PA6 creating a matrix and parameters of composite producing process upon their mechanical properties.