Comparison of numerical and experimental study of armour system based on alumina and silicon carbide ceramics

Chabera P., Boczkowska A., Morka A., Kędzierski P., Niezgoda T., Oziębło A., Witek A.

Bulletin of the Polish Academy of Sciences. Technical Sciences

|

2015

|

Vol. 63, nr 2

363--367

EN

The main goal of this numerical and experimental study of composite armour systems was to investigate their ballistic behaviour. Numerical simulations were employed to determine the initial dimensions of panel layers before the actual ballistic test. In order to achieve this aim, multivariate computations with different thicknesses of panel layers were conducted. Numerical calculations were performed with the finite element method in the LS-DYNA software, which is a commonly used tool for solving problems associated with shock wave propagation, blasts and impacts. An axisymmetric model was built in order to ensure sufficient discretization. Results of a simulation study allowed thicknesses of layers ensuring assumed level of protection to be determined. According to the simulation results two armour configurations with different ceramics have been fabricated. The composite armour systems consisted of the front layer made of Al2O3 or SiC ceramic and high strength steel as the backing material. The ballistic performance of the proposed protective structures were tested with the use of 7.62 mm Armour Piercing (AP) projectile. A comparison of impact resistance of two defence systems with different ceramic has been carried out. Application of silicon carbide ceramic improved ballistic performance, as evidenced by smaller deformations of the second layer. In addition, one of armour systems was complemented with an intermediate ceramic-elastomer layer. A ceramic-elastomer component was obtained using pressure infiltration of gradient porous ceramic by elastomer. Upon ballistic impact, the ceramic body dissipated kinetic energy of the projectile. The residual energy was absorbed by the intermediate composite layer. It was found, that application of composite plates as a support of a ceramic body provided a decrease of the bullet penetration depth.

2

Wytwarzanie ceramiki tlenkowej z zastosowaniem spiekania mikrofalowego

Putyra P.

Mechanik

|

2014

|

R. 87, nr 4

284--287

PL

Przedstawiono rezultaty spiekania mikrofalowego materiałów o osnowie Al2O3. Materiały spiekano w piecu mikrofalowym MKH 4,8 LINN, zgodnie z parametrami: temperatura spiekania - 1620 st. C, czas spiekania - 5 minut, prędkość nagrzewania - 9 st. C/min oraz 17 st. C/min. za pomocą krążków pirometrycznych przeprowadzono pomiar rozkładu temperatury w komorze pieca. Gęstość względna materiałów po procesie spiekania mikrofalowego przekraczała 98%, a ich moduł Younga mieścił się w zakresie 377 do 395 GPa. Zastosowanie nagrzewania mikrofalowego pozwoliło na znaczne skrócenie procesu w porównaniu ze spiekaniem konwencjonalnycm.

EN

Presented are the results of alumina microwave sintering process. The ceramic materials were sintered using microwave furnace MKH 4,8 LINN in accordance with the process parameters: sintering temperature –1620 degree Celsjus, sintering time – 5 minutes, heating rate – 9 C/min. and 17 C/min. The temperature distribution in the microwave furnace chamber was measured using process temperature control rings. The relative density of materials after microwave sintering exceeded 98% and the values of the Young’s modulus were in the range from 377 to 395 GPa. Using process time compared to conventional sintering process.

3

Wpływ procesu Hot Isostatic Pressing (HIP) na wybrane właściwości ceramiki z tlenku glinu

Perkowski K., Osuchowski M., Witosławska I., Witek A.

Prace Instytutu Ceramiki i Materiałów Budowlanych

|

2010

|

R. 3, nr 6

56-66

PL

Przedstawiono wstępne prace mające na celu określenie wpływu procesu Hot Isostatic Pressing (HIP) na wybrane właściwości ceramiki z tlenku glinu. Próbki spieczonego swobodnie tlenku glinu o znanych parametrach gęstości pozornej i wytrzymałości mechanicznej poddano procesowi hipowania, czyli powtórnego wypalenia w warunkach wysokiego ciśnienia izostatycznego działającego bezpośrednio na próbki. Proces prowadzono w temperaturze 1600°C przy ciśnieniu izostatycznym argonu równym 300 MPa. W wyniku przeprowadzonego eksperymentu uzyskano gęstą ceramikę korundową, o gęstości bliskiej 100% wartości gęstości teoretycznej. Wartości wytrzymałości mechanicznej na zginanie próbek poddanych procesowi HIP uległy nieznacznie pogorszeniu w stosunku do próbek, które były tylko spiekane swobodnie.

EN

We presence introductions works which main target is term Hot Isostatic Pressing (HIP) process on select properties alumina ceramic. Freely sintered alumina samples about known parameter such as apparently density and mechanical durability submit (HIP) process the other hand samples submit again sinter in other condition such as temperature 1600°C and isostatic argon pressure equally 300 MPa. In our experiment we obtain very density alumina ceramic. Density obtained ceramic was relative 100% theoretical density. Values mechanical durability on bend samples after HIP process were a bit worse than samples which were sinter freely.