PL
 |
EN
Preferencje help
Polish version English version Język
Widoczny [Schowaj] Abstrakt
Liczba wyników
Powiadomienia systemowe
  • Sesja wygasła!

Znaleziono wyników: 8

Liczba wyników na stronie
first rewind previous Strona / 1 next fast forward last
Wyniki wyszukiwania
Wyszukiwano:
w słowach kluczowych:  alloy structure
help Sortuj według:

help Ogranicz wyniki do:
first rewind previous Strona / 1 next fast forward last
1
Content available Influence of Al5FeSi Phases on the Cracking of Castings at Al-Si Alloys
Hren I., Svobodova J., Michna Š.
Archives of Foundry Engineering
|
2018
|
Vol. 18, iss. 4
120--124
EN
The research described in this contribution is focused on fractographic analysis of the fracture area of newly developed eutectic silumin type AlSi9NiCuMg0.5 (AA 4032), which was developed and patented by a team of staff of the Faculty of Mechanical Engineering. The paper presents determination of the cause of casting cracks in operating conditions. Fractographic analysis of the fracture area, identification of the structure of the casting, identification of structural components on the surface of the fracture surface and chemical analysis of the material in the area of refraction were performed within the experiment. Al-Si alloys with high specific strength, low density, and good castability are widely used in pressure-molded components for the automotive and aerospace industries. The results shown that the inter-media phases Fe-Al and Fe-Si in aluminium alloys lead to breakage across the entire casting section and a crack that crossed the entire cross section, which was confirmed by EDS analysis.
2
Content available Kształtowanie struktury i właściwości wolframowych stopów ciężkich o przeznaczeniu specjalnym
Kaczorowski M., Skoczylas P.
Problemy Mechatroniki : uzbrojenie, lotnictwo, inżynieria bezpieczeństwa
|
2015
|
Vol. 6, Nr 1 (19)
27-40
PL
W artykule zamieszczono wyniki badań doświadczalnych, których celem było opracowanie metody wytwarzania wolframowych stopów ciężkich (WSC), przeznaczonych na rdzenie pocisków podkalibrowych stabilizowanych brzechwowo typu APFSDS (ang. Armor Piercing Fin Stabilized Discarding Sabot). Stwierdzono, że najbardziej skuteczną metodą zwiększania właściwości wytrzymałościowych WSC jest obróbka plastyczna na zimno, prowadząca do umocnienia odkształceniowego zarówno ziaren wolframu, jak i osnowy na bazie Ni. Obróbka ta powinna być jednak prowadzona w sposób kontrolowany, ponieważ nadmierny zgniot, powodujący bardzo duże zwiększenie wytrzymałości na rozciąganie i twardości, dokonuje się kosztem znaczącego zmniejszenia wydłużenia, w szczególności odporności na obciążenia udarowe. Obróbka cieplna obejmująca wyżarzanie pod obniżonym ciśnieniem oraz szybkie chłodzenie (przesycanie) połączone z późniejszym wyżarzaniem w temperaturze w zakresie 500-800°C umożliwia dalsze zwiększenie wytrzymałości WSC, lecz efekt obróbki cieplnej jest znacznie mniej efektywny niż obróbki plastycznej na zimno.
EN
The paper presents the results of experimental studies aimed at elaboration of the manufacturing technology of tungsten heavy alloys (WSC) with high mechanical properties, dedicated for kinetic energy penetrators of armour piercing fin stabilized discarding sabot (APFSDS) ammunition. Especially, the results of mechanical properties’ investigations and structure observations of the materials strengthened by cold work and heat treatment involving supersaturation and aging are described. It was concluded that the best method of WSC strengthening is cold working, involving strain hardening both tungsten grain and Ni-based matrix. The cold working should be carried out under control because it excesses deformation causing very high strength and hardness increase is accomplished by the cost of substantial ductility, especially impact strength decrease. The solution heat treatment in vacuum furnace followed by water quenching and then isothermal aging at temperature range of 500-800°C enable further strength and hardness increase of WSC but its effectiveness is substantially less than cold work strengthening.
3
Content available remote The study of precipitation hardening of weight heavy alloys matrix
Kaczorowski M., Skoczylas P., Nowak W.
Archives of Foundry Engineering
|
2008
|
Vol. 8, iss. 1 spec.
169--174
EN
The study of model weight heavy alloy (WHA) W-Ni-Co-Fe, with some excess of tungsten with respect to its maximum nickel based solid State solubility are presented. The alloy was melted at the temperature 1570 °C in hydrogen atmosphere. After removing the bottom part of the casting where excess grains of tungsten sediment, the ingot was solution heat treatment for 2h at the temperature 900 °C followed by water quenching. Finally, the specimens were aged at the temperature 250, 300 and 350 °C for time up to 48, 36 and 24 respectively. After heat treatment the specimens were studied using hardness measurements and structure investigations. The last one included X-ray diffractometry (XRD), optical metallography, scanning electron microscopy (SEM) and transmission electron microscopy (TEM). It was concluded that two phase microstructure was not substantially changed during aging, especially the aging lead not to ultra-fine precipitate formation, which would caused remarkable precipitation strengthening of matrix. The results analysis prompt us to conclude that the main reason of minimal strengthening only was the specific output structure after solution heat treatment, resulted from to low temperature of solution heat treatment.
4
Content available remote The structure and mechanical properties of heat treated Al-Zn-Cu-Mg type alloy
Kaczorowski M., Krzyńska A.
Archives of Foundry Engineering
|
2008
|
Vol. 8, iss. 1 spec.
163--168
EN
The results of precipitation hardening 7075 type cold worked alloy are presented. The aim of the study was to elaborate an Al-Zn-Cu-Mg type light alloy for special application. The most important was to propose the heat treatment parameters which would allow reach the extremely high tensile properties with good ductility. These properties was as follow: tensile strength > 640MPa, Rp, 02 > 600MPa and A5 no less than 8%. To meet these properties we propose the solution heat treatment at the temperature 520 °C with cooling in cold water. The temperature 125°C was chosen for aging. The different aging time was applied for the specimen after solution heat treatment followed with quenching in cold water. The mechanical properties of heat treated specimens were tested in tension and using hardness measurement. Besides the conventional Metallography, scanning (SEM) and transmission electron microscopy (TEM) were applied for structure observations. In case of the last one we used either microscopy observations where tilting experiment was used and selected area electron diffraction (SAD).
5
Content available remote Węgliki w stabilizowanym staliwie austenitycznym
Piekarski B.
Krzepnięcie Metali i Stopów
|
2000
|
R. 2, nr 42
95--103
PL
W pracy przedstawiono wyniki badań mikrostruktury trzech austenitycznych staliw typu 18/30 z dodatkami Nb i Ti poddanych procesowi wyżarzania - 900ºC/300 godz. Stopy zawierały kolejno (% mas.): 1.75% Nb i 0.83% Ti, 1% Ti oraz 1.71% Nb. W badaniach zastosowano mikroskopię świetlną i skaningową, mikroanalizę i dyfrakcję rentgenowską. W strukturze stopów, w zależności od składu chemicznego, identyfikowano wydzielenia węglików NbC, TiC lub (Nb, Ti)C, M23C6, oraz fazę bogatą w Ni i Si, prawdopodobnie fazę G.
EN
The microstructure of three austenitic cast steels type 18/30 with additions of Nb and Ti after annealing at 900ºC/300h has been presented in this paper. The contents of Nb and Ti in tested alloys have been changed as follows (wt-%): 1.75% Nb and 0.83 % Ti, 1% Ti and 1.71% Nb. Microstructural studies were conducted using optical and scanning microscopy, X-ray diffraction and quantitative microprobe analysis. In the microstructure of tested alloys, depending on their chemical composition, the following phases have been identified: NbC, TiC or (Nb,Ti)C, M23C6 and Ni, Si -rich precipitates probably G-phase.
6
Content available remote Struktura stopu AK 7 modyfikowanego tytanem i borem oraz gwałtowną krystalizacją
Orłowicz W., Mróz M.
Krzepnięcie Metali i Stopów
|
2000
|
R. 2, nr 42
51--57
PL
W pracy przedstawiono wyniki pomiaru parametru λ (odległości między osiami głównymi dendrytów) fazy α(Al) stopu AK7 modyfikowanego tytanem i borem oraz drogą gwałtownej krystalizacji.
EN
The paper presents the results of the measurement of λ parameter (the distance between main axes of dendrites of the α phase) in the AK7 alloy modified with AITi5B l and through sudden crystallisation.
7
Content available remote Struktura stopów na osnowie faz międzymetalicznych z układu Ni-Al po przetapianiu laserowym
Czujko T., Zasada D., Bojar Z.
Krzepnięcie Metali i Stopów
|
2000
|
R. 2, nr 42
233--243
PL
W pracy przedstawiono wpływ wiązki lasera CO2 średniej mocy, pracującego w sposób ciągły, na strukturę stopów międzymetalicznych z układu Ni3Al o zróżnicowanym składzie chemicznym. Przedstawiono także zmiany umocnienia materiału w strefie wpływu ciepła i przetopie w stosunku do materiału rodzimego.
8
Content available remote Kształtowanie struktury i właściwości wysokowytrzymałych stopów Al-Zn-Mg
Rzadkosz S., Staszczak L.
Krzepnięcie Metali i Stopów
|
1998
|
nr 36
121--128
PL
Właściwości wytrzymałościowe stopów są uzależnione od struktury pierwotnej odlewów i efektywności procesu utwardzenia dyspersyjnego. Kształtowanie struktury i właściwości wysokowytrzymałych stopów Al-Zn-Mg jest możliwe poprzez zapewnienie odpowiednich warunków odlewania i stygnięcia odlewów, wprowadzenie do stopów odpowiednich aktywnych mikrododatków wpływających na proces zarodkowania i krzepnięcia stopów oraz na efektywność procesów przesycania i starzenia. W pracy poddano analizie wpływ modyfikatorów (Ti, B, Zr) na efekty utwardzania dyspersyjnego stopów Al-Zn-Mg odlanych do form metalowych oraz do form piaskowych wilgotnych i suszonych.
first rewind previous Strona / 1 next fast forward last
JavaScript jest wyłączony w Twojej przeglądarce internetowej. Włącz go, a następnie odśwież stronę, aby móc w pełni z niej korzystać.