1

Fatigue life prediction for acid-resistant steel plate under operating loads

Tomaszewski T., Strzelecki P., Wachowski M., Stopel M.

Bulletin of the Polish Academy of Sciences. Technical Sciences

|

2020

|

Vol. 68, nr 4

913--921

EN

The paper evaluates the causes related to the fatigue damage in a conveyor slide plate, exposed to high-frequency cyclic loads. The plate was made of 1.4301 acid-resistant steel. The fractography showed that the plate failure was caused by fatigue crack. A nonlinear analysis of plate deformation was conducted using the finite element method (FEA) in LS-Dyna software. The maximum normal stresses in the plate fracture were used in further analysis. A “fatigue limit” calculated initially using a FITNET procedure was above the maximum stress calculated using FEA. It indicates that the structural features of the plate were selected correctly. The experimental test results for 1.4301 acid-resistant steel were described using a probabilistic Weibull distribution model. Reliability was determined for the obtained S-N curve at 50% and 5% failure probability allowing for the selected coefficients (cycle asymmetry, roughness, variable load) and the history of cyclic loading. Cumulative damage was determined using the Palmgren-Miner hypothesis. The estimated fatigue life was similar to the actual value determined in the operating conditions for the S-N curve at 5% failure probability. For engineering calculations, the S-N curve at max. 5% failure probability is recommended.

2

Laboratory tests of the use of belt conveyor elements for moulding sands

Romek D., Selech J., Berdychowski M., Kęska W.

Tribologia

|

2018

|

nr 5

95--100

EN

The article presents the results of research on the wear of belt conveyors’ elements made of various materials. For the purpose of the experiment, a test stand was built, reflecting the real working conditions of the conveyor belt, on which abrasive tests of samples made of appropriately selected materials and a control sample of steel were carried out. Obtained wear values indicated the most wear-resistant material.

PL

W artykule zaprezentowano wyniki badań dotyczące zużywania się elementów podajnika taśmowego wykonanych z różnych materiałów. Na potrzeby eksperymentu zbudowano stanowisko badawcze, odzwierciedlające rzeczywiste warunki pracy taśmociągu, na którym przeprowadzono testy ścierne próbek wykonanych z odpowiednio dobranych materiałów oraz ze stali kontrolnej. Uzyskane wartości zużycia wskazały najbardziej odporny na zużywanie ścierne materiał.

3

Corrosion resistance of austenitic stainless steel joints in chlorine ion environments

Brzozowski A.

Archives of Mechanical Technology and Automation

|

2013

|

Vol. 33, no. 1

15--25

EN

The paper presents the results of testing acid-resistant steel welded joints corrosion resistance in the environment containing chlorine ions. The author manipulated corrosion resistance by differentiating the samples cutting and the quality of their surface finishing. Tests were performed in various kinds and concentrations of chlorine compounds, in order to verify the steels susceptibility to pitting and crevice corrosion. The authors attempted to classify welded joints by their corrosion resistance.

PL

W artykule przedstawiono wyniki badań odporności na korozję w środowisku z jonami chloru złączy spawanych z różnych gatunków stali kwasoodpornych. Podjęto próbę zróżnicowania odporności korozyjnej połączeń ze względu na sposób wycięcia próbek oraz jakość wykończenia ich powierzchni. Próby prowadzono z różnymi rodzajami i stężeniami procentowymi związków chloru w celu zbadania podatności omawianych stali na powstawanie i rozwój korozji wżerowej i szczelinowej. Podjęto próbę ogólnej klasyfikacji złączy spawanych ze względu na odporność korozyjną.

4

Możliwości zastosowania nagniatania zewnętrznych powierzchni kulistych w seryjnej produkcji przedmiotów ze stali kwasoodpornej

Kaczmarek J., Lange S., Święcik R., Żurawski A.

Mechanik

|

2012

|

R. 85, nr 8-9CD (SOS)

487--494