1
Content available Prediction of concrete life under coupled dry and wet-sulfate erosion based on damage evolution equation
Nie Nan
Archives of Civil Engineering
|
2023
|
Vol. 69, nr 4
679--692
EN
In a corrosive environment with coupled dry-wet-sulfate action, concrete structures are susceptible to erosion by sulfate ions, which seriously affects the safe operating life. To forecast the operational lifetime of concrete below the influence of the dry-wet cycle and sulfate erosion environment, four different admixtures of polypropylene fiber: 0, 0.6, 0.9, and 1.2 kg/m3, were incorporated into concrete specimens, and indoor accelerated tests were designed to observe the macroscopic and microscopic deterioration law analysis of concrete specimens; using the precept of damage mechanics, the damage of concrete under solubility cycle was established. The damage evolution equation of concrete under freeze-thaw cycles was established and the operational life of concrete was predicted. The results showed that the overall mass loss rate of concrete specimens increased with the number of tests, and the relative energetic modulo decreased with the number of tests; the pore change pattern, microstructure, and internal material composition of specimens under different working conditions were obtained by using NMR scanning technique, SEM electron microscope scanning technique and XRD physical phase analysis technique. The damage evolution equation shows that adding a certain amount of polypropylene fiber to concrete can improve the working life of concrete under dry and wet connected sulfate assault.
2
Content available An approach in determining the critical level of degradation based on results of accelerated test
Hoang Anh D., Vintr Zdenek, Valis David, Mazurkiewicz Dariusz
Eksploatacja i Niezawodność
|
2022
|
Vol. 24, no. 2
330--337
EN
Nowadays, systems are more complex and require high reliability for their components, especially critical system components. Therefore, to avoid serious damage, system are often replaced before the actual failure. The replaced parts are considered to have “soft failure”, and the limit in which the parts are replaced is known as the critical level of the degradation process. Determining the appropriate value of the critical level for a product is an important problem in their exploitation, as well as for predicting the Mean Time to Failure (MTTF) or Remaining Useful Lifetime (RUL) of this product based on the degradation data by the mathematical models. In this article, an approach in determining the critical levels based on failure data from an accelerated test is introduced. This approach is applied with the degradation process of Light-Emitting Diodes (LED) in an accelerated test and a type of Wiener process-based model is used to predict the MTTF or RUL of LED based on their degradation data and the found critical level.
3
Content available remote Odporność na korozję metalowych blach perforowanych
Strąk A.
Materiały Budowlane
|
2017
|
nr 8
77--79
PL
W artykule przedstawiono podstawowe rodzaje blach perforowanych, stosowane w budownictwie. Zinterpretowano wyniki testów przyspieszonej korozji blach perforowanych stalowych i stalowych ocynkowanych spełniających wymagania PN-EN 10346:2011. W badaniach wykorzystano blachy perforowane zabezpieczone antykorozyjnie metodą lakierowania proszkowego. Wyniki odporności na działanie mgły solnej i wilgotnej atmosfery zawierającej SO2 dowodzą, że lakierowanie proszkowe może stanowić skuteczne zabezpieczenie przed działaniem agresywnego środowiska korozyjnego. Szczególnie nanoszenie powłoki lakierowej w dwóch warstwach pozwala na pokrycie zaostrzonych krawędzi powstałych podczas procesu perforacji.
EN
The paper presents basic types of metal sheets perforated used in constructions. The results of accelerated corrosion tests of galvanized steel and steel perforated sheets meeting the requirements of EN 10346:2011 have been interpreted. In the tests perforated sheets coated with anticorrosive powder coating method were used. Based on the resistance to salt spray and humid atmosphere containing SO2, it has been found that powder coating can provide effective protection against the aggressive corrosive environment. In particular, application of the coating varnish in two layers allows to cover the sharpened edge formed during the perforation process.
4
Content available Potencjał sekwestracyjny CO2 w betonach kruszywowych
Łaskawiec K., Piotrowicz M., Romanowski P., Woyciechowski P.
Prace Instytutu Ceramiki i Materiałów Budowlanych
|
2015
|
R. 8, nr 21
22--30
PL
Oddziaływania dwutlenku węgla na efekt cieplarniany są jednym z głównych zagadnień związanych z ochroną środowiska. Dwutlenek węgla występuje w atmosferze ziemskiej przy standardowej temperaturze i ciśnieniu. Spalanie paliw kopalnych i wycinki lasów to główne działania człowieka, które przyczyniają się do wzrostu stężenia dwutlenku węgla na ziemi. Emitery dwutlenku węgla to naturalne gorące źródła, wulkany, gejzery i rośliny. Ponieważ globalne ocieplenie stało się jednym z najważniejszych problemów, podejmuje się prace badawcze mające na celu rozwój technologii, które będą wspierać redukcję stężenia CO2 w atmosferze. Większość badań związanych z karbonatyzacją ograniczają się do jego wpływu na korozję stali zbrojeniowej i przewidywania żywotności konstrukcji żelbetowych. W artykule przedstawiono badania mające na celu określenie potencjału sekwestracji CO2 dla różnych odmian betonów wraz ze szczegółową analizą tego procesu.
EN
The carbon dioxide impact on the greenhouse effect is one of the major topics related to environmental protection. Carbon dioxide occurs in the Earthatmosphere at standard temperature and pressure. Combustion of fossil fuels and forest felling are the major human activities which contribute to concentration of carbon dioxide in the Earth atmosphere. The natural carbon dioxide emitters include volcanoes, hot springs, geysers and plants. Since the global warming became one of the most important issues, it calls for development of technologies which will support the reduction of the CO2 concentration in the atmosphere. Most of studies related to the carbonation are limited to its effects on corrosion of steel reinforcements and service life prediction of reinforced concrete structures. The article objective consists on determining the CO2 sequestration potential for different varieties of concrete together with a detailed analysis of this process.
5
Content available Porównawcze badania właściwości ochronnych powłok metalicznych na blachach stalowych
Strąk A., Bobryk H., Piwowarczyk W.
Przegląd Budowlany
|
2012
|
R. 83, nr 6
57-59
PL
W pracy przedstawiono podstawowe rodzaje blach z powłokami metalicznymi, stosowanych w budownictwie. Zinterpretowano wyniki testów porównawczych przyspieszonej korozji blach stalowych z powłoką cynkowo-magnezową ZMg oraz innymi powłokami metalicznych, które spełniają wymagania PN-EN 10346:2011. Opisano korzystne aspekty zastosowania powłok cynkowo-magnezowych ZMg na pokrycia dachowe i okładziny elewacyjne.
EN
This article describes the basic types of sheet steel with metallic coatings as used in the construction industry. An interpretation is made of the results of comparative tests of accelerated corrosion of sheet steel with the zinc-magnesium coating ZMg and other metallic coatings complying with the requirements of the PN-EN 10346:2011 standard. The favourable aspects of the use of ZMg coatings on roof coverings and elevation facing are presented.