Optimization of hydrogen volumetric storage capacity for microporous carbon materials

Buczek B., Czepirski L., Ziętkiewicz J.

Chemical and Process Engineering

2007

Vol. 28, z. 1

47-55

The concept of adsorptive of hydrogen storage at reduced pressure was analyzed. The method of improving hydrogen storage capacity has been proposed. Active carbons seem to be a suitable medium for the storage of hydrogen. The volumetric hydrogen uptake, the bulk and particle densities of adsorbent, as well as the operating conditions become important factors influencing the storage density. The results show that the adsorption technique could provide a viable method for hydrogen storage.

Zanalizowano koncepcję wykorzystania adsorbentów węglowych jako czynnika zwiększającego gęstość magazynową wodoru. O przydatności węgla aktywnego do adsorpcyjnego magazynowania decydują charakterystyki adsorpcyjne, strukturalne i densymetryczne. Optymalizacja adsorpcyjnych układów magazynowania jest głównie związana z doborem adsorbentu zapewniającego maksymalną pojemność magazynową. Przedstawiono wyniki badań nad usprawnieniem sposobu upakowania węgla aktywnego w zbiornikach do adsorpcyjnego magazynowania wodoru.

Zmiany powierzchniowych i strukturalnych właściwości węgli aktywnych wywołane ich utlenianiem

Choma J., Jaroniec M., Burakiewicz-Mortka W., Klinik J., Tybel A.

Ochrona Środowiska

1998

nr 3

13-20

The objective of the study was to investgate how liquid-phase oxidation with H2O2, HClO4 or HNO3 affects the surface and structural properties of active carbons. To evaluate structural prperties use was made of low-temperature-(-196oC)experimental adsorption isotherms of nitrogen measured on unimodified and oxidized carbons.Experimental adsorption isotherms of water vapor ( measured on unimodified and oxidized active carbons at 25o C )were used to determine surface properties.The oxidation process was fuond to influence the parameters the porous structure.This influence was particularly distinct when the samples were oxidized with HNO3at its boiling temperature.The oxidation process also changed the surface properties of the carbons,thus increasing the amount of adsorbed water vapor.In strongly oxidized active carbons samples a change in the adsorption mechanism was observed ( as compared to unmodified or weakly oxidized samples).This observation was confirmed quantitatively by the parameters of the adsorption equations which were used to describe the experimental isotherms.The oxygen groups that form in the course of the oxidation process were fund to alter the mechanism governing water phase formation on the carbon surface.This is reflected by the substantial changes in the adsorption potential distributions due to progressive oxidation of the carbon surface.