Microstructure, castability, microstructural stability and mechanical properties of ZRE1 magnesium alloy

Rzychoń T., Szala J., Kiełbus A.

Archives of Metallurgy and Materials

|

2012

|

Vol. 57, iss. 1

245-252

EN

The influence of pouring temperature on the microstructure, fluidity and mechanical properties of ZRE1 magnesium alloy was investigated in this paper. The pouring temperature influences on the fluidity, mean area of grain plane section and mechanical properties. The dependence between pouring temperature and volume fraction of the (Mg, Zn)12RE intermetallic phase was not observed. The investigations enabled to determine the optimal pouring temperature of ZRE1 alloy. Moreover, the microstructural stability of ZRE1 alloy during long-term annealing at 150°C, 200°C and 400°C was investigated. ZRE1 magnesium alloy possesses a high microstructural stability up to 200°C, whereas at 400°C magnesium oxides and rare earth metals oxides are observed in the microstructure.

PL

W pracy przedstawiono wyniki badań wpływu temperatury odlewania na mikrostrukturę, lejność i właściwości mechaniczne stopu magnezu ZRE1. Stwierdzono, że temperatura odlewania wpływa na lejność, średnie pole powierzchni płaskiego przekroju ziarna i właściwości mechaniczne stopu ZRE1. Nie zaobserwowano zależności pomiędzy temperaturą odlewania a udziałem objętościowym wydzieleń fazy miedzymetalicznej (Mg, Zn)12RE. Przeprowadzone badania umożliwiły określenie najkorzystniejszej temperatury odlewania do form piaskowych dla stopu ZRE1. Przeprowadzono także badania stabilności strukturalnej podczas długotrwałego wygrzewania w temperaturze 150°C, 200°C i 400°C. Stwierdzono, że do temperatury 200°C mikrostruktura jest stabilna, natomiast w temperaturze 400°C stop ZRE1 charakteryzuje się niską stabilnością i skłonnością do tworzenia tlenków magnezu i metali ziem rzadkich.

2

Evaluation of susceptibility of the ZRE1 alloy to hot cracking in conditions of forced strain

Adamiec J.

Archives of Foundry Engineering

|

2010

|

Vol. 10, iss. 1 spec.

345--350

EN

Nowadays, magnesium alloys are used for casting into sand moulds of huge dimensional castings, high-pressure castings and precise casings. In castings of magnesium alloys defects or inconsistencies often appear (like casting misrun, porosities and cracks) particularly in the huge dimensional castings. Such defects are mended with the use of padding and welding. The welding techniques can be applied by using weld material consisting of magnesium alloy, as well as for regeneration of alloys after excessive wear. Nevertheless, the number of the repaired castings, which were permitted for use, is not satisfactory for a profitable production. The main reasons for wear are the cracks appearing during welding in brittleness high-temperature range. This work in combination with industrial tests of casting welding show that the causes of high-temperature brittleness are the partial tears of the structure and the hot cracks of both the castings and the welded and padded joints. Such phenomena should be treated as irreversible failures caused by the process of crystallisation that is in the area of co-existence of the solid and liquid structural constituent. The assessment of the resistance to hot fractures was conducted on the basis of the transvarestriant trial. The transvarestriant trial consists in changing of strain during welding It was stated that the range of the high-temperature brittleness is very broad, which significantly limits the application of the welding techniques to join or mend the elements made of alloy ZRE-1. The brittleness is caused mainly by metallurgical factors, i.e., precipitation of inter-metal phases from the solid solution.

3

Struktura właściwości złączy spawanych ze stopu magnezu ZRE1

Adamiec J.

Spajanie Materiałów Konstrukcyjnych

|

2009

|

Nr 4 (6) 2009 - Nr 1 (7) 2010

12--16

PL

W ostatnich latach można zauważyć wzrost zainteresowania technologiami wytwarzania elementów z nowych stopów magnezu, a przede wszystkim metodami ich odlewania i spawania. Stop ZRE1 z dodatkiem Zn, Zr i pierwiastków ziem rzadkich odlewany jest grawitacyjnie do form piaskowych. W odlewach tych często występują wady i niezgodności odlewnicze, a naprawia się je z zastosowaniem technik napawania i spawania. Celem pracy było zbadanie wpływu obróbki cieplnej na spawalność stopu ZRE1 oraz opracowanie wytycznych technologicznych dla napawania naprawczego odlewów. Zakres badań obejmował próby napawania i spawania, badania metalograficzne i ocenę własności mechanicznych. Opracowano technologię naprawy odlewów grawitacyjnych wykonanych ze stopu ZRE1.

EN

Magnesium based alloy, ZRE1, is sand molded cast. After this process appear defects (misruns, micro-shrinkage, cracks) in materials, especially in large-size castings. Welding process are methods for the removal and repair of casting defects. In this paper evaluation the possibility of welding ZRE1 magnesium alloy was presented. Alloy in the initial state and alloy in the annealed state were researched. Because the possibility to hot cracks, causes stress in largesize castings ZRE1 magnesium alloy, welding should be after annealing process.