Microstructure and wear resistance of modified WC-Co coatings

Myalska H., Szymański K., Moskal G.

Problemy Eksploatacji

2014

no. 2

27--34

Results of investigations related to microstructure and wear resistance characterization of three types of WC-17Co coatings obtained by a high velocity process were showed in this article. The first type of coating was obtained by spraying standard powders of WC-17Co types. The second one was from “superfine powder” with the same chemical composition. The third type of coating consists of standard powders, as in first case, but with additions of sub-microcrystalline carbides of different types. The process of powder modifications rely on simple mechanical blending of standard WC-17Co powder with 5% wt. of carbide modifier. The presented investigations included the characterization of the microstructure of coatings. Evaluation of porosity, thickness, and especially the morphology of the matrix of coatings were made. The matrix microstructure description was an interesting problem, especially due to the localization and morphology of modifier particles in the Co base phase. Final investigations consisted of the characterization of the wear resistance of the analysed coatings.

W artykule przedstawiono wyniki badań dotyczących charakterystyki mikrostruktury oraz odporności na ścieranie dwóch typów powłok węglikowych WC-Co natryskanych metodą naddźwiękową. W pierwszym przypadku analizowano powłoki otrzymane ze standardowych proszków WC-Co. Drugi rodzaj powłok to powłoki modyfikowane za pomocą submikrokrystalicznych cząstek węglików różnego typu. Zmodyfikowane proszki uzyskano w wyniku prostego mieszania proszku bazowego z dodatkiem 5% wagowych modyfikatora. Wykonano badania obejmujące ocenę mikrostruktury powłok, ich grubość oraz porowatość. Szczególny nacisk położono na analizę osnowy metalicznej powłok celem określenia lokalizacji i morfologii cząstek modyfikatorów. W badaniach końcowych dokonano oceny odporności na ścierania analizowanych powłok.

The deposition of WC-Co coatings by EBPVD technique

Richert M. W., Mazurkiewicz A., Smolik J. A.

Archives of Metallurgy and Materials

2012

Vol. 57, iss. 2

511-515

The WC-Co carbides are widely used to deposit protective coatings on engineering surfaces against abrasion, erosion and other forms of wear existence. The nanostructure coatings offer high strength, a low friction coefficient and chemical and thermal stability. WCo coatings were deposited using EBPVD technique realized in original technological process implemented in the hybrid multisource device, produced in the Institute for Sustainable Technologies - National Research Institute in Radom (Poland). The different kind of precursor sources was used. Depending on the source of precursors nanostructure of coatings forms continuous film or consist from nano-carbides. Nanocrystalline WC-Co coatings show hardness in the range of 510-1266 HV. The microstructure of coatings were observed by transmission electron microscopy (TEM). The phase consistence were determined byBrucker D8 Discover-Advance Diffractometer. The paper presents the original technological equipment, methodology, and technological parameters for the creation of the nanocomposite coatings WC.

Węgliki WC-Co są szeroko używane do osadzania na powierzchniach inżynierskich jako ochrona przeciwko tarciu, erozji i innym formom zużycia. Powłoki nanostrukturalne wykazują wysoka wytrzymałość, niski współczynnik tarcia oraz chemiczną i termiczną stabiność. Powłoki WC-Co zostały osadzane techniką EBPVD przy użyciu oryginalnego technologicznego procesu z hybrydowym źródłem prekursorów, w Instytucie Technologii Eksploatacji w Radomiu (Polska). Użyto różnego rodzaju źródeł prekursorów. W zależności od rodzaju użytego źródła prekursorów nanostrukturalne powłoki były zbudowane z ciągłych warstw lub z nano-weglików. Mikrotwardość nanokrystalicznych powłok mieściła się w zakresie 510-1266 μHV. Mikrostruktura powłok była obserwowana transmisyjnym mikroskopem elektronowym (TEM). Skład fazowy powłok określono za pomocą aparatu rentgenowskiego Brucker D8 Discover-Advance Diffractometer. Artykuł prezentuje oryginalne technologiczne urządzenie, metodologię i technologiczne parametry pozwalające na wytworzenie nanokompozytowej powłoki WC.