Content available Mechanical Properties and Corrosion Resistance of HVOF Sprayed Coatings Using Nanostructured Carbide Powders
Żórawski W., Makrenek M., Góral A.
Archives of Metallurgy and Materials
|
2016
|
Vol. 61, iss. 4
1839--1846
EN
Nanostructured and composite WC-12Co coatings were prepared by means of the supersonic spray process (HVOF). The microstructure and composition of WC-12Co nanostructured powder were analyzed by scanning electron microscope (SEM) and transmission electron microscope (TEM). Investigations revealed nano grains of WC with the size in the range of 50-500 nm. The nanostructured sprayed coating was analysed by SEM and phase composition was investigated by X-ray diffractometer (XRD). A denser coating structure with higher hardness was observed compared to conventional coating with a small amount of W2C, WC1−x, W and some amorphous phase. Young’s modulus and hardness were determined by depth sensing indentation in HVOF sprayed WC-12Co nanostructured coatings. Results were compared to conventional coatings and the relevance of the nanostructure was analyzed. An indentation size effect was observed on the polished surface and cross-section of both coatings. Data provided by indentation tests at maximum load allow to estimate hardness and elastic modulus. Enhanced nanomechanical properties of conventional coating in comparison to nanostructured one were observed. Nanostructured coatings WC-12Co (N) revealed significantly better corrosion resistance.
2
Content available remote Mikrostruktura i właściwości natryskiwanych naddźwiękowo powłok WC-12Co po obróbce elektroiskrowej
Żórawski W., Radek N.
Przegląd Spawalnictwa
|
2012
|
R. 84, nr 9
46-50
PL
W artykule przedstawiono wyniki badań natryskiwanych naddźwiękowo nanostrukturalnych i konwencjonalnych powłok WC-12Co po obróbce elektroiskrowej (ESD) elektrodą z węglika wolframu. Analiza zmian mikrostruktury i właściwości powłok została przeprowadzona przy użyciu mikroskopu skaningowego Joel JSM-5400. Do określenia zmian rozkładu pierwiastków zastosowano mikrosondę ISIS 300 Oxford Instruments, a zmiany składu fazowego zostały zbadane dyfraktometrem D8 Advance (Bruker). Stwierdzono, że na powierzchniach nałożonych powłok po obróbce ESD została utworzona homogeniczna powłoka z niską zawartością kobaltu o bardzo dobrej przyczepności, a wysoka temperatura procesu spowodowała zmiany fazowe w powłoce. Obydwie natryskiwane powłoki WC-12Co po obróbce elektroiskrowej miały podobną twardość, chropowatość oraz współczynnik tarcia, a powłoka nanostrukturalna WC-12Co wykazała większą odporność na zużycie ścierne.
EN
The paper concerns properties of HVOF sprayed two tungsten carbide coatings after applying electro-spark deposition process (ESD). After finishing microstructure of sprayed coatings were changed by applying tungsten carbide electrode. Analysis of changes in microstructure and properties of the coatings was performed using scanning electron microscope Joel JSM-5400. To determine the changes in the distribution of elements was used microprobe ISIS 300 Oxford Instruments and the changes of phase composition were examined by D8 Advance (Bruker) diffractometer. It was found that on the surfaces of sprayed coatings after ESD process was formed a homogeneous layer with a low content of cobalt and very good adhesion. The high temperature of the process caused changes in phase composition of sprayed coating. Both sprayed WC-12Co coating after ESD process have similar hardness, roughness and coefficient of friction. The nanostructured WC-12Co coating showed higher resistance to abrasive wear.
3
Content available remote Właściwości nanostrukturalnych powłok WC12Co natryskiwanych HVOLF
Żórawski W.
Przegląd Spawalnictwa
|
2009
|
R. 81, nr 9
33-36
PL
Nanostrukturalna cermetalowa powłoka była natryskiwana naddżwiękowo (HVOLF) z aglomerowanego nanostrukturalnego proszku WC12Co. Ziarna nanostrukturalnego proszku i natryskiwanej powłoki były analizowane za pomocą mikroskopu skaningowego (SEM), mikroskopu transmisyjnego (TEM) i dyfraktometru (XRD). Badania pokazały, że ziarna proszku składają się z nanocząstek. Na podstawie badań natryskiwanej nanostrukturalnej powłoki stwierdzono, że charakteryzowała się ona większą gęstością niż powłoka natryskiwana z proszku konwencjonalnego i zawierała również niewielką ilość faz W2C, WC1-x i W. Powłoki o strukturze nanokrystalicznej miały wyższą twardość oraz czterokrotnie niższy współczynnik tarcia od powłok natryskiwanych z proszku konwencjonalnego.
EN
Nano-structural cermet coating was sprayed with the supersonic method (HVOLF) from the WC12Co agglomerated nano-structural powder. Grains of a nano-structural powder and a coating sprayed were analysed by means of a scanning electron microscope (SEM), a transmission electron microscope (TEM) and a X-ray diffractometer (XRD). The investigations showed that grains of powder consist of nano-particles. On the grounds of investigations of a nano-structural coating it was stated that it was characterized by higher density than a coating sprayed of a classical powder and it also contained a small amount of the W2C, WC1-x and W phases. The coatings of nano-crystallic structure had higher hardness and four-time lower friction factor than coatings sprayed of a classical powder.