The microstructure and properties of titanium carbide reinforced stainless steel matrix composites prepared by powder metallurgy

Szewczyk-Nykiel A.

Technical Transactions

|

2018

|

Vol. 115, iss. 7

191--206

EN

TiC particle-reinforced AISI 316L stainless-steel matrix composites were prepared using conventional powder metallurgy technology. The effect of TiC content on the microstructure and properties of these composites has been investigated with a particular emphasis upon hardness, wear resistance and corrosion resistance in sea water environments. The results showed that TiC particle reinforcement improved the hardness, wear resistance and corrosion resistance of AISI 316L stainless steel. The higher TiC content in the studied composites resulted in a higher hardness of the wear surface and a lower wear rate. The best corrosion resistance in sea water was achieved for sintered AISI 316L – 5% TiC composite.

PL

Konwencjonalną technologią metalurgii proszków wytworzono umacniane cząstkami TiC kompozyty o osnowie austenitycznej stali AISI 316L. Dokonano oceny wpływu udziału cząstek TiC na mikrostrukturę i właściwości tych kompozytów, w szczególności twardość, odporność na zużycie ścierne i odporność na korozję w środowisku wody morskiej. Stwierdzono, że umocnienie cząstkami TiC doprowadziło do poprawy twardości, odporności na zużycie ścierne i odporności na korozję stali AISI 316L. Wraz ze wzrostem udziału TiC w badanych kompozytach wzrastała twardość powierzchni zużycia, a malała jej szybkość. Natomiast najlepszą odporność na korozję w wodzie morskiej wykazał spiekany kompozyt AISI 316L – 5% TiC.

2

Microstructure and mechanical behaviour of in situ fabricated AA6061–TiC metal matrix composites

Kumar G. S. P., Koppad P. G., Keshavamurthy R., Alipour M.

Archives of Civil and Mechanical Engineering

|

2017

|

Vol. 17, no. 3

535--544

EN

AA6061–TiC composites were developed by in situ reaction of molten AA6061 alloy with potassium hexafluorotitanate salt and pure graphite at a temperature of 900 °C. The in situ composites were subjected to hot forging at 500 °C and uniform strain rate of 0.0115 mm s−1 with degree of deformation of 65%. Both cast and forged in situ composites were subjected to grain size analysis and scanning electron microscopy studies to study the dispersion of TiC particles. Mechanical properties like Brinell hardness and tensile properties were evaluated to measure the effect of TiC particles on the AA6061 matrix. Microstructure of forged composites revealed uniform dispersion of TiC particles without forming any lumps at any particular regions. Brinell hardness and tensile strength of cast and forged in situ composites increased with increasing TiC particle content. The improved mechanical properties were attributed to good dispersion of TiC particles, grain refinement of the matrix and dislocation strengthening. Every fracture developed in cast ones was due to inter-dendritic cracking while in the case of forged ones it had mixed mode of fracture with dominating ductile nature.

3

Obróbka elektroerozyjna kompozytów Ni₃Al-TiC

Biało D, Perończyk J, Daniels R.., Duszczyk J.

Mechanik

|

2015

|

R. 88 nr 4CD

17--21

PL

Obróbce elektroerozyjnej WEDM poddano materiały kompozytowe z intermetaliczną osnową Ni₃Al i fazą zbrojącą TiC w ilości 0, 10, 20, 30% obj. wytworzone w procesie metalurgii proszków. Jako parametry obróbki przyjęto czas impulsu ti i napięcie w impulsie U. W funkcji tych parametrów oceniano wydajność obróbki Vw, topografię i chropowatość powierzchni oraz stan tzw. warstwy białej.

EN

Composites with intermetallic matrix Ni₃Al reinforced with 0, 10, 20, 30% vol. TiC were wire electro discharge machined (WEDM). Materials were manufactured by powder metallurgy (P/M) using hot isostatic pressing (HIP).Material remove rate Vw, surface topography and roughness, white layer were investigated as a function of machining parameters (pulse time ti and load voltage U).