Microstructure and corrosion resistance of Ti oxidized at high potentials

Jakubowicz J., Koper J. K.

Inżynieria Materiałowa

2013

Vol. 34, nr 4

273--276

In this work high-potentials anodic oxidation of titanium was studied. The treatment can be applied for modiﬁcation of Ti-based hard tissue implants. The potential in the range of 120÷180 V was applied for 30 min. Samples were immersed in 1 M H3PO4 electrolyte consisting 0.2+2% HF addition. The treatment results in signiﬁcant surface morphology changes. The roughness, porosity and corrosion resistance increases, which is related with TiO2 formation. At high-potentials, the oxidation process follows under sparking conditions. Taking into account structure, morphology and corrosion resistance, the most promising in hard tissue implant applications, was anodic oxidation at 180 V in 1 M H3PO4 + 0.2% HF and 1 M H3PO4 + 1% HF electrolytes.

W pracy przedstawiono zagadnienie wysokopotencjałowego utleniania anodowego tytanu. Obróbka ta może być stosowana do modyﬁkacji powierzchni tytanowych implantów tkanek kostnych. Próbki zanurzano w elektrolicie 1 M H3PO4 z dodatkiem 0,2÷2% HF, przykładając potencjał 120÷180 V przez 30 minut. W wyniku obróbki stwierdzono istotne zmiany morfologii powierzchni próbek. Zwiększa się chropowatość, porowatość i odporność na korozję, co jest związane z pojawieniem się tlenków TiO2. W wysokich potencjałach proces utleniania przebiega w warunkach iskrzenia. Biorąc pod uwagę strukturę, morfologię i odporność na korozję, najbardziej obiecujące w zastosowaniach implantologicznych tkanek kostnych są warunki utleniania anodowego w potencjale 180 V w elektrolitach 1 M H3PO4 + 0,2% HF oraz 1 M H3PO4 + 1%HF.