The degradation process of La2Zr2O7 + 8YSZ composite thermal barrier coatings (TBC) was presented in this paper. These systems were deposited by air plasma spraying (APS) on AMS 5599 alloy and on a NiCrAlY bond-coat. A scope of tests consisting of isothermal oxidation in air atmosphere at 1100°C for 500 h was performed. Detailed microstructural tests were carried out after 2, 10, 48, 175 and 500 hours of exposure. These tests included microstructure evaluation of a ceramic layer in all coating types, while particularly taking into account phenomena, which occur in a TGO (thermally growth oxide) zone. Evaluation of TGO zone growth was worked out and obtained results were compared with data for conventional TBC layers, which were deposited from 8YSZ powders and La2Zr2O7 respectively.
PL
W artykule przedstawiono proces degradacji kompozytowych powłokowych barier cieplnych typu La2Zr2O7 + 8YSZ. Powłoki zostały wykonane metoda natrysku cieplnego w powietrzu na stopie niklu typu AMS 5599 z międzywarstwą typu NiCrAlY. Powłoki poddano badaniom w postaci testu odporności na utlenianie izotermiczne w temperaturze 1100°C przez czas 500 h. Szczegółowe badania mikrostrukturalne wykonano po 2, 10, 48, 175 and 500 godzinach testu. Zakres zastosowanych badan obejmował ocenę mikrostrukturalną wszystkich powłok ze szczególnym uwzględnieniem zjawisk zachodzących w strefie TGO. Rozwój i morfologia strefy TGO została porównane do wyników uzyskanych dla standardowych powłok jednowarstwowych bazujących na ceramice typy 8YSZ i La2Zr2O7 .
2
Dostęp do pełnego tekstu na zewnętrznej witrynie WWW
The degradation process of La2Zr2O7 thermal barrier coatings (TBC) was presented in this paper. This system was deposited by air plasma spraying (APS) on AMS5599 alloy and on a NiCrAlY bond-coat. A scope of tests consisting of isothermal oxidation in air atmosphere at 1100°C for 500 h was performed. Detailed microstructural tests were carried out after 2, 10, 48, 175 and 500 hours of exposure. These tests included microstructure evaluation of a ceramic layer in both coating types, while particularly taking into account phenomena, which occur in a TGO (thermally growth oxide) zone. Evaluation of TGO zone growth was worked out and obtained results were compared with data for conventional TBC layers, which were deposited from 8YSZ powders.
PL
W prezentowanym artykule przedstawiono proces degradacji powłok termoizolacyjnych TBC typu La2Zr2O7 Układ ten został wytworzony metodą natrysku plazmowego (APS) na stopie AMS5599 z międzywarstwą NiCrAlY. Zakres badań obejmował statyczne utlenianie próbek w atmosferze powietrza o temperaturze 1100° C przez 500 godzin. Szczegółowe badania mikrostruktury przeprowadzono po 2, 10, 48, 175 i 500 godzinach ekspozycji. Testy te obejmowały ocenę mikrostruktury warstwy ceramicznej obu typów, ze szczególnym uwzględnieniem zjawisk zachodzących w strefie TGO. Dokonano oceny wzrostu strefy TGO, a uzyskane wyniki porównano z danymi dla konwencjonalnych warstw TBC, które zostały osadzone z proszków 8YSZ.
JavaScript jest wyłączony w Twojej przeglądarce internetowej. Włącz go, a następnie odśwież stronę, aby móc w pełni z niej korzystać.