Effect of Ag on Sn-Cu and Sn-Zn lead free solders

Alam S. N., Mishra P., Kumar R.

Materials Science Poland

|

2015

|

Vol. 33, No. 2

317--330

EN

Lead and lead-containing compounds are considered as toxic substances due to their detrimental effect on the environment. Sn-based soldering systems, like Sn-Cu and Sn-Zn are considered as the most promising candidates to replace the eutectic Sn-Pb solder compared to other solders because of their low melting temperature and favorable properties. Eutectic Sn-0.7 wt.% Cu and near eutectic composition Sn-8 wt.% Zn solders have been considered here for study. For the Sn-Cu system, besides the eutectic Sn-0.7 wt.% Cu composition, Sn-1Cu and Sn-2Cu were studied. Three compositions containing Ag: Sn-2Ag-0.7Cu, Sn-2.5Ag-0.7Cu and Sn-4.5Ag-0.7Cu were also developed. Ag was added to the eutectic Sn-0.7 wt.% Cu composition in order to reduce the melting temperature of the eutectic alloy and to enhance the mechanical properties. For the Sn-Zn system, besides the Sn-8 wt.% Zn near eutectic composition, Sn-8Zn-0.05Ag, Sn-8Zn-0.1Ag and Sn-8Zn-0.2Ag solder alloys were developed. The structure and morphology of the solder alloys were analyzed using a scanning electron microscope (SEM), filed emission scanning electron microscope (FESEM), electron diffraction X-ray spectroscopy (EDX) and X-ray diffraction (XRD). Thermal analysis of the alloys was also done using a differential scanning calorimeter (DSC). Trace additions of Ag have been found to significantly reduce the melting temperature of the Sn-0.7 wt.% Cu and Sn-8 wt.% Zn alloys.

2

Wpływ zawartości cynku oraz temperatury na lutowność niklu stopami Sn-xZn (x=4,5; 90; 95% wag.)

Kudyba A., Siewiorek A., Sobczak N.

Prace Instytutu Odlewnictwa

|

2012

|

T. 52, z. 4

25-39

PL

Celem badań było określenie wpływu temperatury oraz zawartości Zn na lutowność podłoży Ni ciekłymi stopami Sn-Zn o zawartości cynku 4,5; 90; 95% wag. Badania lutowności przeprowadzono metodą zanurzeniową (wetting balance test) pozwalającą na pomiar siły i czasu zwilżania oraz wyznaczenie wartości kąta zwilżania. Badania wykonano w dwóch różnych temperaturach dla każdego z badanych stopów, odpowiednio dla Sn-4,5Zn w 230 i 250°C, Sn-90Zn w 400 i 450°C, Sn-95Zn w 410 i 450°C. Po badaniach lutowności przeprowadzono analizę strukturalną poprzecznych przekrojów próbek metodami mikroskopii optycznej i skaningowej mikroskopii elektronowej w połączeniu z lokalną analizą składu chemicznego. Stwierdzono, że wzrost temperatury poprawia lutowność każdego z badanych układów Sn-xZn/Ni. W przypadku podwyższenia temperatury procesu do 450°C dla stopów o zawartości 90 i 95% wag. Zn, zaobserwowano całkowitą zwilżalność Ni (wartość kąta zwilżania θ = 0°).

EN

The aim of this study was to determine the effect of temperature and zinc content on the solderability of nickel substrates with liquid Sn-xZn alloys (4.5, 90, 95 wt% Zn). Solderability tests were carried out by the wetting balance method which allows the measurement of wetting force and wetting time and determination of the contact angle size. The study was performed at two different temperatures applied to each of the examined alloys, i.e. for Sn-4.5Zn at 230 and 250°C, for Sn-90Zn at 400 and 450°C, and for Sn-95Zn at 410 and 450°C. After the solderability tests, structural analysis was performed on sample cross-sections using optical microscopy and scanning electron microscopy coupled with energy dispersive spectroscopy for chemical analysis. It was found that temperature increase improves the solderability in each of the systems investigated. With process temperature raised to 450°C for alloys with 90 and 95 wt% Zn, a complete wetting of the tested nickel substrates was obtained (the value of contact angle θ = 0°).

3

Wpływ zawartości cynku oraz temperatury na lutowność miedzi stopami Sn-xZn (x=4,5; 90; 95% wag.)

Kudyba A., Siewiorek A., Sobczak N.

Prace Instytutu Odlewnictwa

|

2012

|

T. 52, z. 3

45-61

PL

Celem badań było określenie wpływu temperatury oraz zawartości Zn na lutowność podłoży Cu ciekłymi stopami Sn-Zn o zawartości cynku 4,5; 90; 95% wag. Badania lutowności przeprowadzono metodą zanurzeniową (wetting balance test) pozwalającą na pomiar siły i czasu zwilżania oraz wyznaczenie wartości kąta zwilżania. Badania wykonano w dwóch różnych temperaturach dla każdego z badanych stopów, odpowiednio dla Sn-4,5Zn w 230 i 250°C, Sn-90Zn w 400 i 450°C, Sn-95Zn w 410 i 450°C. Po badaniach lutowności przeprowadzono analizę strukturalną poprzecznych przekrojów próbek metodami mikroskopii optycznej i skaningowej mikroskopii elektronowej w połączeniu z lokalną analizą składu chemicznego. Stwierdzono, że wzrost temperatury poprawia lutowność każdego z badanych układów Sn-xZn/Cu. W przypadku podwyższenia temperatury procesu do 450°C dla stopów o zawartości 90 i 95% wag. Zn, zaobserwowano całkowitą zwilżalność Cu (wartość kąta zwilżania θ = 0°).

EN

The aim of this study was to determine the effect of temperature and Zn content on the solderability of Cu substrates with liquid Sn-xZn alloys (4.5; 90; 95 wt.% Zn). Solderability tests were carried out by the wetting balance test which allows the measurement of wetting force and wetting time and determination of the size of contact angle. The study was performed at two different temperatures applied to each of the examined alloys, i.e. for Sn-4.5Zn at 230 and 250°C, for Sn-90Zn at 400 and 450°C, and for Sn-95Zn at 410 and 450°C. After the solderability tests, structural analysis was performed on sample cross-sections using optical microscopy and scanning electron microscopy coupled with energy dispersive spectroscopy for chemical analysis. It was found that the temperature increase improves the solderability of each of the systems investigated. With process temperature increased to 450°C for alloys with 90 and 95 wt%. Zn, a complete wetting of the tested Cu substrates was obtained (the value of contact angle θ = 0°).