Identification of the cause of the stem neck fracture in the hip joint endoprosthesis

Ryniewicz A. M., Bojko Ł., Ryniewicz A., Pałka P., Ryniewicz W.

International Journal of Applied Mechanics and Engineering

2018

Vol. 23, no. 1

223--234

Endoprosthesis stem fractures are among the rarest complications that occur after hip joint arthroplasty. The aim of this paper is to evaluate the causes of the fractures of the Aura II stem neck, which is an element of an endoprosthesis implanted in a patient. In order to achieve it, a radiogram was evaluated, the FEM analysis was carried out for the hip joint replaced using the Aura II prosthesis and scanning tests as well as a chemical analysis were performed for the focus of fatigue. The tests performed indicate that the most probable causes leading to the fatigue fracture of the Aura II stem under examination were material defects in the process of casting and forging (forging the material with delamination and the presence of brittle oxides and carbides) that resulted in a significant reduction of strength and resistance to corrosion. In the light of an unprecedented stem neck fracture, this information should be an indication for non-destructive tests of ready-made stems aiming to discover the material and technological defects that may arise in the process of casting and drop forging.

Tribological tests of the nanomaterials used to reconstruct molars and premolars with the application of the direct method

Ryniewicz W., Herman M., Ryniewicz A. M., Bojko Ł., Pałka P., Ryniewicz A., Madej T.

Tribologia

2017

nr 3

155--164

Physiological abrasion of teeth is a process of gradual loss of the hard tissue of opposite teeth resulting from age-related natural dental wear. In abrasion, the cusps and their slopes in the jaw and the mandible become flattened due to the mechanical load applied. The aim of this paper is to carry out a tribological and microstructural evaluation of modern composite materials used to reconstruct the teeth in the lateral part of the dental arch. Five light-cured composite materials were selected for tests. The tests involved the coefficient of friction and resistance to wear in a sliding contact in the presence of artificial saliva and the microstructure of the external surface of samples before the wear process and in the wear-related damaged area. The test method applied, which combines a biomechanical analysis of resistance to wear and the analysis of the microstructure before the wear process and in the wear-related damaged area, makes it possible to evaluate the tribological properties of composite materials used to reconstruct teeth in the lateral part of the dental arch.

Fizjologiczne starcie zębów jest to proces stopniowej utraty twardych tkanek zębów przeciwstawnych w wyniku naturalnego zużycia postępującego z wiekiem. Starcie to polega na jednoczesnym spłaszczaniu guzków i ich stoków w zębach szczęki i żuchwy w warunkach obciążeń biomechanicznych. Celem pracy jest ocena tribologiczna i mikrostrukturalna nowoczesnych materiałów kompozytowych stosowanych do odbudowy ubytków w bocznym odcinku łuku zębowego. Do badań wybrano 5 materiałów kompozytowych utwardzanych światłem. Przeprowadzono badania współczynnika tarcia i odporności na zużycie w kontakcie ślizgowym, w obecności sztucznej śliny oraz badania mikrostrukturalne warstwy wierzchniej próbek przed procesem zużycia oraz w strefie skazy zużyciowej. Zastosowana metoda badań łącząca biomechaniczną analizę odporności na zużycie z analizą mikrostruktury przed procesem zużycia oraz w skazie zużyciowej pozwala na ocenę właściwości tribologicznych materiałów kompozytowych do odbudowy zębów w bocznym odcinku łuku.