Cavitation erosion resistance of Ni-Co based coatings

Szala M., Hejwowski T., Lenart I

Advances in Science and Technology. Research Journal

2014

Vol. 8, nr 21

36--42

The Ni-Co based coatings were performed by means of PTA method from Ni-based and Co-based powders. The cavitation erosion resistance of Ni-Co specimens and reference sample in deionized water was determined by the ultrasonic vibration system. The microstructure, as well as mechanism of cavitation erosion of coating was examined by using SEM and LOM. The main mechanism of erosion is cracking and spalling at the boundary of dendrites and eutectics. Coatings exhibit higher cavitation erosion resistance than the reference sample. Therefore, they could be applied to repair and protect pump elements from cavitation wear.

Alloys for PTA deposition onto seatings of exhaust valves

Hejwowski T., Szewczyk S., Nastaj T.

Journal of KONES

2008

Vol. 15, No. 4

171-178

The paper presents results of corrosion investigations of alloys used for PTA deposition and three experimental Ni-Co based alloys for plasma deposition containing 37.7-60.5% Ni, 22.8-38% Co and 10.8-18% Cr. Results were compared with experimental data obtained in the similar experiment on currently applied valve steels and H23N18 heat resistant steel. Experimental alloys containing 15-18% of chromium revealed higher heat resistance compared to valve steels and H23N18 heat resistant steel. Experimental alloys Nos 1 and 2 demonstrated lower linear loss in corrosion test carried out in molten salts compared to satellite grade 6. The chemistry of molten salts used in crucible tests resembled that of deposits formed on exhaust system elements of engines burning heavy fuels. Experimental alloys in corrosion research tests in the air atmosphere proved the smaller increase of mass in the temperatures of tests 1073 K and 1173 K, in comparison to Stellite grade 6 alloy, currently used to weld deposition on valve sealing surface. Considering of the contents of hard phases assuring good wear resistance and the their high corrosion resistance, coatings welded on with the powder mixtures based on nickel and cobalt can be poised for the application on sealing surfaces of exhaust valves of diesel engines instead of currently applied expensive Stellite grade 6 alloy.

W pracy przedstawiono wyniki badań korozyjnych stopów stosowanych do napawania metodą plazmową oraz TIG a także trzech stopów eksperymentalnych na osnowie Ni-Co, o zawartości 37,7-60,5% Ni, 22,8-38% Co oraz 10,8-18% Cr i przewidywanych do napawania metodą plazmową. Rezultaty porównano z wynikami badań dla aktualnie stosowanych stali zaworowych i stali żaroodpornej H23N18. Stopy eksperymentalne o zawartości 15-18% Cr wykazały wyższą żaroodporność od stali zaworowych i stali żaroodpornej H23N18 i aktualnie stosowanego do napawania stopu stellite grade 6. Stopy eksperymentalne w badaniach korozyjnych w atmosferze powietrza wykazały, w porównaniu do aktualnie stosowanego do napawania przylgni zaworów stopu Stellite grade 6, mniejsze przyrosty masy w temperaturach testu 1073 K i 1173 K. Stopy Ni-Co nr 1 i 2 wykazały mniejszy ubytek liniowy w porównaniu do stellitu grade 6 w badaniach korozyjnych w stopionych solach, których skład chemiczny był zbliżony do składu osadów utworzonych na elementach układów wydechowych silników napędzanych ciężkimi paliwami. Z uwagi na zawartość twardych faz zapewniających dobrą odporność na zużycie oraz wysoką odporność na korozję powłoki napawane mieszaninami proszków na osnowie niklu oraz na osnowie kobaltu mogą być rozważane do zastosowania na przylgniach zaworów wylotowych silników Diesla zamiast aktualnie stosowanego kosztownego stellitu grade6.