The article presents research on the development of technology and mechanical properties of a 16Mo3 steel tube overlaid with Inconel 625 nickel superalloy using robotized Plasma Powder Transferred Arc Welding (PPTAW) process. Based on the results of non-destructive, metallographic and microscopic observations, chemical composition, thickness and hardness measurements of overlays optimal technological parameters for working in elevated temperature environment were selected. The performed test has shown the correct structure of the overlay weld without welding imperfections. The examined padding weld was characterized by a dendritic structure with primary crystals growing in the direction of heat removal. It has been stated that in the range of heat input to base material 277÷514 J/mm, the iron content in the surface zone of 1,5 mm padding weld ranges from 4 to 5,5%.
PL
W artykule przedstawiono wyniki badań dotyczących opracowania technologii napawania i właściwości mechanicznych rury ze stali kotłowej gatunku 16Mo3 pokrytej zewnętrzną warstwą plateru z nadstopu niklu Inconel 625 nanoszonego w procesie zrobotyzowanego napawania plazmowego proszkowego (PPTAW). W oparciu o wyniki badań nieniszczących, metalograficznych makro- imikroskopowych, składu chemicznego oraz pomiarów grubości i twardości warstwy plateru, wytypowano optymalne parametry technologiczne wykonywania tego typu zabezpieczeń na elementach rurowych konstrukcji energetycznych pracujących w podwyższonej temperaturze. Przeprowadzone badania wykazały prawidłową budowę warstwy plateru bez niezgodności spawalniczych. Badana warstwa charakteryzowała się budową dendrytyczną o kryształach pierwotnych narastających w kierunku odprowadzania ciepła. Wykazano, że przy ilości ciepła wprowadzonego do materiału rodzimego z zakresu 277÷514 J/mm, zawartość żelaza w strefie przypowierzchniowej plateru o grubości ok. 1,5 mm mieściła się w przedziale od 4 do 5,5%.
2
Content available remote Mikrostruktura kompozytowych powłok Ni-ZrC napawanych plazmowo
PL
W artykule przedstawiono wyniki badań kompozytowych napoin o osnowie stopu Ni umacnianych cząstkami ZrC. Warstwy te uzyskano poprzez napawanie plazmowe mieszaniny proszków – osnowy i fazy umacniającej na podłoża ze stali S355J0. Wykonano napoiny dla zmiennych wartości natężenia prądu łuku głównego. Przeprowadzono badania makro i mikroskopowe powłok kompozytowych stosując mikroskopię optyczną i skaningową. Określono objętościowy udział cząstek fazy umacniającej osnowę oraz stopień rozcieńczania napoiny metalem podłoża. Analizowano rozkład mikrotwardości osnowy. Wykazano, iż zachodzi dezintegracja cząstek proszku ZrC w skutek oddziaływania z ciekłą osnową metaliczną.
EN
The results of investigations of nickel base composite coatings reinforced by ZrC particles are presented in the paper. The layers were obtained by deposition of Ni-alloy and ZrC powders’ mixture onto S355J0 low alloy steel by Plasma Powder Transferred Arc Welding method. Variable values of main welding current were applied. Macroscopic and microscope examinations of composite coatings were evaluated using optical and scanning microscopes. Volume fraction of reinforcing phase and dilution coefficient were evaluated. Microhardness of the matrix of composite coatings was also analyzed. It was evidenced that disintegration of ZrC particles occurred due to the action with liquid metal base.
3
Content available remote The structure of Ni-TiC composite coatings deposited by PPTAW method
EN
In this paper, the structure investigations of Ni-TiC composite coatings deposited on low carbon steel (S355J0) using plasma powder transferred arc welding (PPTAW) are presented. A blend of nickel alloy powder with 40 vol% TiC was selected as the precursor material for fabricating Ni-TiC composite coatings. The obtained composite layers were characterized by macro and microstructural examination. The distribution of carbide grains in the nickel matrix was characterized by fractal analysis. In addition, the volume fraction of TiC inclusion in the nickel matrix and coating dilution as a function hardfacing parameters were calculated. Metallographic examination revealed that the coatings obtained within the range of a 60÷80 A welding current have discontinuities in the interface layer - substrate and a number of large air bubbles. The composite coatings obtained with a welding current higher than 80 A were correctly formed. The microstructure of the composite coatings contains large and small irregular titanium carbide particles. As a result of the interaction between the nickel alloy matrix and high energy plasma arc with titanium carbide during the surfacing process, small particles are formed. Both the dilution coefficient and volume fraction of TiC increase with an increase in welding current. The last part of the paper includes the results of the fractal dimension measurements of coating cross-sections. For the analyzed structures, the percentage of TiC and linear fractal dimension were determined using the line counting dimension method (LCD), which is a modification of the box counting dimension method (BCD).
PL
W artykule przedstawiono wyniki badań struktury kompozytowych powłok Ni-TiC otrzymanych metodą napawania plazmowego (ang. PPTAW - Plasma Powder Transferred Arc Welding) w zależności od natężenia prądu napawania. Napoiny te uzyskano w wyniku topienia mieszaniny proszków, w której osnową był proszek na bazie niklu, natomiast fazę umacniającą stanowił proszek TiC. Proszek osnowy mieszano z proszkiem węglika tytanu o tej samej ziarnistości w stosunku objętościowym 60:40. Kompozytowe powłoki napawano na podłoża ze stali niskowęglowej S355J0. Przeprowadzono badania makro- i mikroskopowe otrzymanych napoin kompozytowych Ni-TiC. Zaadaptowano program do analizy obrazów mikroskopowych MultiScanBase do określenia udziału cząstek fazy umacniającej osnowę oraz obliczenia udziału metalu podłoża w napoinie. Do określenia rozmieszczenia cząstek TiC w osnowie napoin kompozytowych zastosowano analizę fraktalną. Kompozytowe napoiny Ni-TiC formowały się poprawnie, gdy natężenie prądu łuku głównego wynosiło co najmniej 80 A. Warstwy uzyskane dla niższych wartości natężenia prądu nie wykazywały metalurgicznego połączenia ze stalowym podłożem, a ponadto występowały w nich niezgodności spawalnicze w postaci dużych pęcherzy gazowych. Badania metalograficzne ujawniły obecność dużych i małych cząstek TiC w niklowej osnowie. Wraz ze wzrostem natężenia prądu liczba małych cząstek wzrastała. Było to powodowane rozpadem dużych cząstek TiC pod wpływem oddziaływania ciekłej osnowy w trakcie napawania. Udział metalu podłoża w napoinie zwiększa się wraz ze wzrostem natężenia prądu, ponieważ zwiększa się także energia liniowa procesu. Również udział objętościowy cząstek TiC w osnowie rośnie, gdy zwiększa się prąd napawania. Dla badanych powłok określono liniowy wymiar fraktalny, stosując zmodyfikowaną metodę box counting dimension (BCD).