The Effect of Mn Content on the Structure and Properties of PM Mn Steels

Tenerowicz M., Sułkowski M.

Archives of Metallurgy and Materials

2017

Vol. 62, iss. 4

2153--2163

The aim of the study was to examine how a reduction of Mn content in PM steels will affect their plastic and strength properties. The results of mechanical, metallographic and fractography tests of sintered (PM) steels containing 1% and 2% Mn are reported and compared with those for 3% Mn PM steel. Höganäs iron powder grade NC 100.24, low-carbon ferromanganese Elkem and graphite powder grade C-UF were used as the starting powders. Powder mixes Fe-(1-2)%Mn-0.8%C were prepared in a Turbula mixer for 30 minutes. Following mixing, “dog bone” compacts were single pressed at 660 MPa, according to PN-EN ISO 2740 standard. Sintering of compacts was carried out in a laboratory tube furnace at 1120°C and 1250°C for 60 minutes in a mixture of 95%N2 – 5%H2 in a semi-closed container. Three types of heat treatment were then used: sinterhardening (cooling rate – 66°C/min), slow furnace cooling (cooling rate 3.5°C/min) and tempering at 200°C. The studies have shown a beneficial effect of the reduction of manganese on plastic properties (up to 7.96%), while maintaining fracture strengths (UTSs) comparable to those of steel with higher contents of manganese. Currently detailed studies of steel containing 1%Mn are conducted.

The Microstructure and Properties of Low-Carbon PM Mn-Cr-Mo Steels Sintered under Different Conditions

Sułowski M., Ciaś A., Pieczonka T.

Archives of Metallurgy and Materials

2014

Vol. 59, iss. 2

575--580

The paper presents the effect of sintering conditions on the microstructure and mechanical properties of low-carbon Mn-Cr-Mo PM steels. It was proved there is no effect of tempering temperature on the properties of Astaloy CrL-base steels, sintered at 1250°C in 5%H2-95%N2 mixture as compared with the properties of those sintered at 1120°C. The properties of Astaloy CrM-based steels, sintered at 1250°C in air were comparable or higher to Astaloy CrL-based steels. The addition of lump of ferromanganese was not sufficient for metal oxides reduction. The structure investigation confirmed the earlier observations that Mn-Cr-Mo PM steels have predominantly martensitic or martensitic/bainitic microstructure.

W artykule przedstawiono wpływ parametrów spiekania na mikrostrukturę i własności mechaniczne spiekanych, niskowęglowych stali manganowo-chromowo-molibdenowych. W pracy wykazano, że własności mechaniczne stali wykonanej na bazie proszku stopowego Astaloy CrL (l,5%Cr, 0,2%Mo, reszta Fe) spiekanej w temperaturze 1250°C w atmosferze 5%H2-95%N2 nie zależą od temperatury odpuszczania, czego nie stwierdzono podczas badań własności wytrzymałościowych tych stali wy- twarzanych w niższej temperaturze spiekania (1120°C). Ponadto, prowadzone badania wykazały, że stale wytworzone na bazie proszku stopowego Astaloy CrM (3%Cr, 0,5%Mo. reszta Fe) po spiekaniu w temperaturze 1250°C w atmosferze powietrza charakteryzowały się porównywalnymi lub wyższymi własnościami mechanicznymi niż stale wykonane na bazie proszku stopowego Astaloy CrL, wytwarzane w tych samych warunkach. Podczas spiekania w powietrzu zastosowano odłamkowe cząstki żelazomanganu o łącznej masie 52 g, które umieszczano w bezpośrednim sąsiedztwie próbek (całkowita masa próbek 490 g) w stalowej łódce, w celu redukcji tlenków. Jak wykazały badania, dodatek żelazomanganu był niewystarczający, aby zapewnić kompletną redukcję tlenków.