Characterization of weld fusion zone for TIG welded P91and P92 steels

Pandey C., Mahapatra M. M., Kumar P., Kumar P., Thakare J. G.

Archives of Metallurgy and Materials

2018

Vol. 63, iss. 4

1755--1761

The welding of nuclear grade P91 and P92 steel plate of thickness 5.2 mm were performed using the autogenous tungsten inert gas (TIG) welding process. The welded joint of P91 and P92 steel plate were subjected to the varying post weld heat-treatment (PWHT) including the post weld heat treatment (PWHT) and re-austenitizing based tempering (PWNT). A comparative study was performed related to the microstructure evolution in fusion zone (FZ) of both the welded joint using the scanning electron microscope and optical microscope in a different condition of heat treatment. The hardness test of the FZ for both joints was also conducted in a different condition of heat treatment. P92 steel welded joint have observed the higher tendency of the δ ferrite formation that led to the great variation in hardness of the P92 FZ. The homogeneous microstructure (absence of δ ferrite) and acceptable hardness was observed after the PWNT treatment for both the welded joint.

Changes In Properties and Microstructure of High-Chromium 9-12%Cr Steels Due to Long-Term Exposure at Elevated Temperature

Zieliński A., Dobrzański J., Purzyńska H., Golański G.

Archives of Metallurgy and Materials

2016

Vol. 61, iss. 2B

957--964

This paper presents the characteristics of the performance of P91 (X10CrMoVNb9-1), P92 (X10CrWMoVNb9-2) and VM12 (X12CrCoWVNb12-2-2) steels used for condition assessment of the pressure components of boilers with supercritical steam parameters. Studies on the mechanical properties, microstructure tests using scanning and transmission electron microscopy, and X-ray analysis of the phase composition of precipitates were performed for selected steels in the as-received condition and after long-term annealing. These steel characteristics are used for the evaluation of the microstructural changes and mechanical properties of the material of components after long-term service. The result of this study is the database of material characteristics representing the mechanical properties related to the microstructure analysis and it can be used for diagnosis of the components of pressure parts of power boilers.