Difference of Microstructures and Mechanical Properties between 9Cr-1W Ferritic/martensitic Steel and ODS Steel

Kim Ga Eon, Kim Tae Kyu, Noh Sanghoon

Archives of Metallurgy and Materials

|

2020

|

Vol. 65, iss. 1

337--341

EN

Ferrtic/martensitic and ODS steels were fabricated by the mechanical alloying process, and their microstructures and mechanical properties were investigated. The 9Cr-1W and 9Cr-1W-0.3Ti-0.35Y2 O3 (in wt.%) steels were prepared by the same fabrication process such as mechanical alloying, hot isostatic pressing, and hot rolling processes. A microstructural observation of these steels indicated that the Ti and Y2 O3 additions to 9Cr-1W steel were significantly effective to refine the grain size and form nano-sized Y-Ti-O oxide particles. As a result, the tensile strengths at room and elevated temperatures were considerably enhanced. Considerable improvement of the creep resistances at 700°C was also evaluated. It is thus concluded that 9Cr-1W ODS steel with Ti and Y2 O3 additions would be very effective in improving the mechanical properties especially at elevated temperatures.

2

Understanding the Oxide Dispersion Behavior of Yttria in Metal Matrix of MA956 Alloy through High-Energy Milling and Hot Press Sintering

Swain B., Han D., Kim G.-H., Kong M.-S., Ahn B.

Archives of Metallurgy and Materials

|

2017

|

Vol. 62, iss. 2B

1377--1381

EN

MA956 (Fe-Cr-Al) alloy powder was high-energy ball milled with various amount of yttria contents (1,2,3, and 4 wt.%) to fabricate an oxide dispersion strengthened alloy. The milled powders were then consolidated using hot press sintering at 1150°C. The surface morphology and crystal structure of MA956 powder during the high-energy milling depending on the yttria contents was investigated using particle size analysis, X-ray diffraction, and scanning electron microscopy. The microstructural analysis of sintered alloy was performed using transmission electron microscopy and energy dispersive spectroscopy to evaluate the dispersion behavior of yttrium oxide. The results showed that, as yttria contents increased, the oxide particles became finer and are uniformly distributed during the high-energy milling. However, after the sintering, the oxide particles were coarsened with more than 3 wt.% of yttria addition.

3

Identification of ods and dynamics characteristics of chain saws

Kromulski J., Pawłowski T., Zembrowski K.

Drewno : prace naukowe, doniesienia, komunikaty

|

2010

|

vol. 53, nr 183

113-125

EN

This article presents methods of identification of dynamics characteristics of chain saws. These methods can be successfully used in the process of identification of resonant frequencies and visualisation of ODS of chain saws. Vibration measurements were done using Laser Doppler Vibrometry. Some examples of identification of dynamics characteristics of chain saws and their operational deflection shapes are presented below.

PL

Przedstawiono wyniki badań charakterystyki dynamicznej pilarki łańcuchowej. Pomiarów wibracji dokonano z wykorzystaniem techniki laserowej. Przeprowadzono analizę modalną układu. Zaprezentowano przykłady ODS (Operational Deflection Shapers) prowadnicy pilarki łańcuchowej.

4

Substancje zubożające warstwę ozonową w ZSEE - aspekty prawne i praktyczne

Olszaniecki P.

Recykling

|

2009

|

nr 11

46-47

PL

W latach siedemdziesiątych ubiegłego wieku naukowcy udowodnili, że za niszczenie warstwy ozonowej odpowiadają emitowane do atmosfery niektóre gazy chlorowcopochodne. Zaczęto określać je mianem substancji zubażających warstwę ozonową SZWO (ang. ODS - ozone depleting substances).

5

Badania właściwości spieków ODS o osnowie Fe40Al

Durejko T., Zarański Z., Sulej S.

Kompozyty

|

2005

|

R. 5, nr 2

39-42

PL

Materiał do badań uzyskano, wykorzystując autorski proces technologiczny, nawiązujący do metalurgii proszków. Mieszaninę proszków żelaza i aluminium z jednoprocentowym wagowo dodatkiem nanometrycznego Al2O3 prasowano/spiekano wstępnie pod obciążeniem statycznym i cyklicznie zmiennym, a następnie spiekano swobodnie w celu uzyskania jednorodnej struktury FeAl. Wsad przed spiekaniem homogenizowano w młynie kulowym. W prezentowanym opracowaniu przeanalizowano wpływ granulacji wsadu wejściowego i rodzaju obciążenia (statyczne i cyklicznie zmienne) na właściwości wytrzymałościowe spieków. Wraz ze wzrastającą szerokością przedziału wymiarowego wsadu wzrasta granica wytrzymałości na ściskanie badanych spieków. Zmiany parametru Rc wynikające ze zmiany rodzaju ciśnienia prasowania są w tym przypadku statystycznie nieistotne. Obserwuje się natomiast jego wyraźny wpływ na wartość odkształcenia względnego Ac. Odkształcenie próbek, wykonanych z proszków o tej samej granulacji, spiekanych z udziałem obciążenia statycznego jest około 10% wyższe niż dla dogęszczanych ciśnieniem cyklicznie zmiennym. Poszerzenie przedziału wymiarowego - wsad poniżej 38 žm - umożliwia odkształcanie spieków do poziomu 42% przy wartości 37% dla frakcji 40+/-38 žm. Dla próbek wykonanych z proszków z przedziału 53+/-38 žm zaobserwowano spadek plastyczności do wartości 34%. Optimum wytrzymałościowe uzyskano dla spieków wykonanych z proszków o frakcji poniżej 38 žm spiekanych z udziałem obciążenia statycznego. Dla tego przypadku zarejestrowano poziom naprężeń niszczących równy 2482 MPa przy odkształceniu względnym 42%.

EN

The iron aluminides FeAl have been among the most widely investigated intermetallics. For example, they have relatively Iow density, high stiffness, and excellent resistance to oxidation and corrosion at elevated temperature. Their major disadvantages is the susceptibility to environmental embrittlement at room temperature, very poor strength and creep resistance above 600°C. This problem can be partially solved by microalloying and oxide dispersion strengthening (ODS). Oxide dispersion strengthening (ODS) iron aluminides alloys based on FeAl have been formed by two stages sintering process. The elemental iron and aluminum powders with addition of nanometer size Al2O3 (1 wt.%) were mixed together to give a composition of Fe-40 at.% Al by ball milling. Three variants of powders mixture size: 40+/38, 53+/-38, < 38 žm were used. The initial stage of manufacturing was mechanical forming of prepared mixture by pressing at elevated temperature. Two value of cyclic pressure frcquency was used - static version (0 Hz) and 40 Hz. Second stage of manufacturing led to change of chemically and structurally heterogencous pre-sintered materials into homogeneous Fe40Al-based intermetallics. Changes in mechanical properties of sintered materials were studied. The essential strength parameters of intermetallic sinters were calculated on the base of stress-strain compression curves. Influence of mixture powders size on compression strength and equivalent strain was analysed. It was stated that size of powders influence on sinters compression strength. With increase powders dimensionally range increase value of Rc too. Samples obtained from < 38 žm powders, Consolidated by static pressure have the highest strength of the order of 2482 MPa at 42% strain. Kind of used loading has a negligible effect on sinter strength. However, cyclic loading decrease in plastic deformation. Decrcase about ten percent in equivalent strain was observed for all variants.

6

Metody badania odkształceń dynamicznych konstrukcji mechanicznych (ODS)

Kromulski J.

Journal of Research and Applications in Agricultural Engineering

|

2001

|

Vol. 46, nr 3

11-15

PL

Przedstawiono trzy metody badania odkształceń dynamicznych konstrukcji (ODS). Pierwsza z nich pozwala na wyznaczenie ODS z bezpośredniego pomiaru funkcji transmitancji widmowej w warunkach eksploatacyjnych. Druga bazuje na obliczeniu ODS, na podstawie znajomości modelu modalnego układu i sił wymuszających. Trzecia z metod oparta jest na analizie rozkładu na wartości szczególne wzajemnego widma mocy odpowiedzi układu. Zamieszczono przykłady identyfikacji eksploatacyjnych postaci drgań dla wybranych maszyn rolniczych.

EN

Three methods are presented of the determination of operational deflection shapes (ODS). The first method allows one to determine the ODSs by direct measuring of responses (transmissibility junction) of the operating machine. The second method is based on the simulation with assumed operating forces and using a previously derived modal model. The third method allows to determine the ODS using singular value decomposition of crosspower spectrum matrix. Examples of identification of operational deflection shapes of selected agricultural machines were presented.

7

Żarowytrzymałe stopy umocnione dyspersyjnie cząstkami tlenków (stopy ODS)

Dubiel B., Czyrska-Filemonowicz A.

Inżynieria Materiałowa

|

2000

|

R. XXI, nr 1

20-28

PL

Stopy umocnione dyspersyjnie tlenkami (ang. Oxide Dispersion Strengthened, ODS) są nowoczesnymi materiałami konstrukcyjnymi pracującymi w wysokich temperaturach homologicznych. Koncepcja umocnienia stopów ODS zakłada stabilność termodynamiczną cząstek tlenków, które nie wydzielają się z osnowy metalicznej, lecz wprowadzane są do niej mechaniczną syntezą. W pracy przedstawiono charakterystykę własności i mikrostruktury stopów ODS na osnowie niklu, żelaza i aluminium. Szczególną uwagę poświęcono stopom żelaza, ze względu na ich wysoką odporność na korozję gazową i w związku z tym możliwość zastosowania w lotnictwie i astronautyce, do wyrobu elementów pieców przemysłowych, komór spalania silników Diesla i turbin gazowych. Najszersze zastosowanie znajdują stopy INCOLOY MA956 oraz PM2000, w których dodanie do ferrytycznej osnowy Fe-20Cr-4,5Al około 0,5% wagowych tlenku Y2O3 umożliwia uzyskanie dobrych własności wytrzymałościowych i odporności na utlenianie do temperatury 1 100 stopni Celsjusza. W pracy wykazano, że przyczyną spadku wytrzymałości stopów ODS po długotrwałym wyżarzaniu w temperaturach powyżej 1 100 stopni Celsjusza jest koagulacja cząstek tlenków. Stwierdzono, że już w trakcie zagęszczania mechanicznie syntezowanej mieszaniny proszków metodą wyciskania na gorąco, cząstki tlenku Y2O3 reagują z glinem z osnowy, tworząc złożone tlenki itrowo-glinowe. Wykazano, że w ferrytycznych stopach ODS występują cztery rodzaje tlenków itrowo-glinowych: 3Y2O3*5Al2O3 o strukturze tetragonalnej (YAT), Y2O3*Al2O3 o strukturze rombowej typu perowskitu (YAP), 2Y2O3*Al2O3 o strukturze jednoskośnej (YAM) oraz Y2O3*Al2O3 o strukturze heksagonalnej (YAH). Zaobserwowano, że od temperatury 1 100 stopni Celsjusza cząstki tlenków itrowo-glinowych zaczynają rosnąć, przyjmując kształt wydłużonych wielościanów. Proces wzrostu tlenków jest jednak wolniejszy, niż w przypadku węglików, czy też faz międzymetalicznych (na przykład fazy gamma'). Różnorodność tlenków itrowo-glinowych sprawia, że podczas koagulacji cząstek w osnowie ferrytycznych stopów ODS zachodzą jednocześnie przemiany kilku faz tlenkowych. Ponadto procesem towarzyszącym wzrostowi tlenków jest ubytek glinu z osnowy, związany z tworzeniem się na powierzchni stopu zgorzeliny Al2O3. Uniemożliwia to wytłumaczenie procesu wzrostu cząstek na gruncie klasycznych teorii koagulacji. Niestabilność cząstek tlenków itrowo-glinowych stanowi bardzo poważne ograniczenie w efektownym wykorzystaniu ferrytycznych stopów ODS do pracy w wysokich temperaturach.

EN

Oxide Dispersion Strengthened (ODS) alloys are advanced materials for high temperature components. Production of ODS alloys involves mechanical alloying process to create material with ductile matrix and hard oxide dispersoid. Strengthening oxides (e.g. yttria) are selected due to its extreme thermodynamic stability. The paper presents information concerning the properties and microstructure of Fe-, Ni- and Al-based ODS alloys. The Fe-base ODS alloys are of considerable interest because of its very good oxidation resistance and therefore are used for aircraft and aerospace applications, components of industrial furnaces, gas-turbine combustion chambers and Diesel engines. The Fe-Cr-Al ODS alloys INCOLOY MA956 and PM2000, containing 0.5 wt% of Y2O3 exhibit exceptional strength and oxidation resistance up to 1 100 degrees centigrade. The research carried out on the ferritic ODS alloys showed that the loss of strength at temperatures above 1 100 degrees centigrade is caused by the dispersoid growth. Systematic investigations on the chemical composition showed that the Y2O3 added could not be detected even in as-received material due to the uptake of aluminium into the oxides particles. Instead, mixed Y-Al oxides have been identified, which showed the phases: 3Y2O3*5Al2O3 (tetragonal, YAT), Y2O3*Al2O3 (Al-perovskite, YAP), 2Y2O3*Al2O3 (monoclinic, YAM) and Y2O3*Al2O3 (hexagonal YAH). The high temperature exposure above 1 100 degrees centigrade caused pronounced growth and facetting of particles. The growth of oxide dispersoid in ferriric matrix is not such pronounced as in case of carbides or intermetallic phases (e.g. gamma'). The coarsening occurs simultaneously in a number of different dispersoid phases and phase transformations take place. The additional uptake of Al is used for scale formation. Therefore the conventional theories of coarsening cannot be applied to describe the dispersoid growth in ODS alloys.