Oxide scale formation on in 792 at early stages of high temperature exposure

Nowak W. J., Wierzba P., Wierzba B., Sieniawski J.

Advances in Manufacturing Science and Technology

2017

Vol. 41, nr 1

65--74

In the present work a commercially available Ni-base superalloy IN 792 was exposed at 1050°C up to 50 hours in Ar+O2 (20%) for investigation of its oxidation kinetics as well as oxide scale formation. It was observed that the alloy formed chromium rich oxide scale. However, detailed analysis, including glow discharge optical emission spectroscopy (GD-OES) and scanning electron microscopy (SEM) showed that the alloy forms multiphase oxide scale consisting of TiO2, Cr2O3, TiTaO4 and Al2O3. The latter caused Al-depletion from the bulk material, which resulted in dissolution of the γ’ phase and local weakening of the IN 792.

W pracy przedstawiono analizę wyników próby utleniania wysokotemperaturowego nadstopu niklu IN 792 w temperaturze 1050°C, w czasie 50 h w atmosferze Ar+O2 (20%). Określono kinetykę procesu utleniania oraz scharakteryzowano wytworzoną warstwę tlenków. Analizę składu chemicznego prowadzono metodami emisyjnej spektroskopii optycznej z wyładowaniem jarzeniowym (GD-OES) i elektronowej mikroskopii skaningowej (SEM). Stwierdzono, że na podłożu nadstopu niklu IN 792 tworzy się wielowarstwowa zgorzelina złożona z tlenków TiO2, Cr2O3, TiTaO4 i Al2O3. Wykazano również, że tworzenie się wydzieleń Al2O3 powoduje lokalne zubożenie ziarn osnowy stopu w aluminium – składnika fazy umacniającej (Ni3Al). Prowadzi więc do degradacji tego składnika fazowego mikrostruktury i obniżenia stopnia umocnienia nadstopu IN 792.