Ni-P/Graphene composite layers produced by chemical reduction method

Trzaska M., Cieślak G.

Composites Theory and Practice

|

2015

|

R. 15, nr 3

137--140

EN

The paper presents the results of studies of nickel-phosphorus/graphene (Ni-P/G) composite layers and, for comparative purposes, Ni-P layers produced by the electroless deposition method. The layers were prepared in multi-component solutions. The used graphene was in the form of flakes of different sizes. The characteristics of the grapheme were determined by means of Raman spectroscopy and scanning electron microscopy. The diffraction analysis of the material, morphology and surface topography of the Ni-P and Ni-P/G layers are presented. The micro-hardness of the material of the produced layers was examined by Vickers measurements. The conducted studies have shown that the Ni-P/G layers prepared by the chemical reduction process are characterized by a higher degree of surface roughness and three times higher hardness in comparison with the Ni-P composite layers.

PL

Przedstawione w niniejszej pracy wyniki zrealizowanych badań odniesione są do powierzchniowych warstw kompozytowych nikiel-fosfor/grafen (Ni-P/G) oraz, w celach porównawczych, do warstw Ni-P, wytworzonych metodą redukcji chemicznej. Warstwy wytwarzano w wieloskładnikowej kąpieli, a w przypadku warstw kompozytowych jako fazę dyspersyjną stosowano grafen w postaci płatków o zróżnicowanych wymiarach. Charakterystykę grafenu wyznaczano za pomocą spektroskopii Ramana oraz skaningowej mikroskopii elektronowej. Przedstawiono wyniki analizy dyfrakcyjnej materiału warstw Ni-P, Ni-P/G oraz morfologię i topografię ich powierzchni. Mikrotwardość materiału wytworzonych warstw określono metodą Vickersa. Zrealizowane badania wykazały, że warstwy kompozytowe Ni-P/G wytworzone metodą redukcji chemicznej charakteryzują się znacznie większym stopniem rozwinięcia powierzchni oraz trzykrotnie większą twardością w porównaniu z warstwami Ni-P.

2

Wpływ enkapsulacji cząstek proszku Nd-M-B powłoką Ni-P na szybkość korozji wiązanych magnesów w zakwaszonych roztworach siarczanowych

Klimecka-Tatar D., Pawłowska G., Bala H.

Ochrona przed Korozją

|

2011

|

nr 7

387-390

PL

W pracy zbadano wpływ enkapsulacji cząstek proszku ze stopu Nd-(Fe,Co)-B powłoką Ni-P na korozyjne zachowanie się magnesów kompozytowych spajanych żywicą epoksydową. Aby ocenić odporność korozyjną tych wiązanych magnesów wykonano pomiary potencjokinetyczne krzywych polaryzacji w zakwaszonych roztworach siarczanowych (pH = 1 i 3). Badania korozyjne wykazały, że pokrycie cząstek proszku warstwą Ni-P przed procesem spajania skutecznie spowalnia szybkość korozji magnesów, o ile środowisko nie jest zbytnio zakwaszone (pH = 1).

EN

The effect of encapsulation of Nd-(Fe,Co)-B powder particles with Ni-P coating on the corrosion behaviour of the final composite magnetic material, consolidated with epoxy-resin, has been examined. To evaluate the corrosion resistance of these bonded magnets, the potentiokinetic polarization measurements in acidified (pH = 1 and 3) sulphate solutions have been carried out. Corrosion tests showed that the coating of powder particles with Ni-P layers before bonding effectively inhibit the corrosion rate of the final magnets, unless the environment is too acidified (pH = 1).

3

Wpływ enkapsulacji cząstek proszków Nd-M-B powłokami Ni-P na szybkość korozji atmosferycznej magnesów wiązanych

Klimecka-Tatar D., Bala H., Pawłowska G.

Ochrona przed Korozją

|

2011

|

nr 4-5

147-149

PL

Przeprowadzono badania nad wpływem enkapsulacji cząstek proszku MQP-B (Nd12Fe77Co5B6) powłokami Ni-P na korozyjne zachowanie w atmosferze mgły solnej magnesów wiązanych żywicą epoksydową. Powłoki Ni-P na cząstkach proszku wytwarzano bezprądowo w wodnym roztworze soli Ni(II) i podfosforynu sodu. Dowiedziono, że wytworzenie warstwy Ni-P na powierzchni cząstek proszku przed procesem spajania korzystnie wpływa na szybkość korozji atmosferycznej magnesów wiązanych.

EN

Investigations under effect of MQP-B (Nd12Fe77Co5B6) powder particles encapsulation with Ni-P layer on corrosion behaviour of epoxy-bonded magnets in salt spray atmosphere have been carried out. The layers of Ni-P were prepared by electroless plating in aqueous solution of Ni(II) and sodium hypophosphite. It was established that powder particles encapsulation with Ni-P layer before consolidation has its beneficial effect on atmospheric corrosion rate of bonded magnets.

4

Bezprądowe niklowanie włókien węglowych - stabilizatory roztworów

Broda A., Kozera R., Boczkowska A., Kurzydłowski K. J., Bieliński J., Bielińska A., Strzała A.

Ochrona przed Korozją

|

2009

|

nr 11

476-478

PL

Wykonano badania bezprądowej metalizacji włókien węglowych z zastosowaniem osadzania Ni-P. Metalizowano wiązki włókien Tenax po ich wstępnym wygrzewaniu na powietrzu. Powierzchnię włókien aktywowano katalitycznie w roztworach Sn(II) i Pd(II). Powłoka Ni-P (2-5% mas.P) o grubości 0,3-2 žm osadzana była z roztworu zawierającego siarczan(VI) niklu(II), podfosforyn i glicynę (pH = 8,5; 70oC; 5-30 min). Dla zapobieżenia samorozkładowi roztworu dodawano stabilizatory i zwilżacze, m.in. tiomocznik, azotan(III), arsenian(III), molibdenian(VI), sole alkiloamoniowe. W roztworach z dodatkami uzyskano znaczne wydłużenie czasu metalizacji włókien.

EN

Electroless metallization of carbon fibers was investigated with use of Ni-P deposition. Tenax roving of carbon fibers was metallized after preliminary heat treatment on air. The surface of fibers was then catalytically activated in Sn(II) and Pd(II) baths. The Ni-P coating (2-5% mas.P; thickness 0,3-2 žm) was deposited in bath contained nickel(II) sulfate(VI), hypophosphite and glycine (pH = 8,5; 70oC; 5-30 min). In aim to prevent the bath self-decomposition, the stabilizers and wetting agents were added, e.g. thiourea, nitrate(III), arsenate(III), molybdate(VI) and alkylammonium salts. In stabilized baths the time of Ni-P deposition on carbon fiber was considerably prolonged.