Electrodeposition of nickel coatings in choline chloride: ethylene glycol deep eutectic solvent

Winiarski J., Cieślikowska B., Szczygieł B.

Ochrona przed Korozją

2018

nr 4

93--95

The electrodeposition and morphology of nickel coatings deposited potentiostatically in (2-hydroxyethyl)trimethylammonium chloride : ethylene glycol (1:2 molar ratio) eutectic solvent on copper substrate were investigated. In the presence of 1 mol dm−3 NiCl2·6H2O the reduction of nickel at 25 °C takes place at potentials more negative than −0.4 V vs. Ag quasi-reference electrode. It was found that the morphology and structure of nickel coatings are strongly affected by deposition potential. In the investigated system, electrodeposition at ambient temperature and at the potentials between −0.6 and −0.8 V vs. Ag results in compact nickel coatings devoid of visible defects.

Zbadano proces osadzania i morfologię powłok niklowych otrzymanych potencjostatycznie na podłożu miedzianym w kąpieli bezwodnej bazującej na mieszaninie eutektycznej chlorku 2-hydroksyetylotrimetyloamoniowego i glikolu etylenowego (1:2 molowo). W tej mieszaninie zawierającej 1 mol dm−3 NiCl2·6H2O redukcja niklu zachodzi przy potencjałach bardziej ujemnych od −0,4 V względem pseudoelekrody srebrnej (drut Ag). Zauważono, że morfologia i struktura powłok niklowych silnie zależy od potencjału osadzania. Powłoki homogeniczne i pozbawione widocznych wad można otrzymać w temperaturze otoczenia przy potencjale w zakresie od −0,6 do −0,8 V wzgl. Ag.

Microstructure and Properties of Ni and Ni/Al2O3 Coatings Electrodeposited at Various Current Densities

Góral A., Berent K., Nowak M., Kania B.

Archives of Metallurgy and Materials

2016

Vol. 61, iss. 1

55--60

The study presents investigations of an influence of various direct current densities on microstructure, residual stresses, texture, microhardness and corrosion resistance of the nickel coatings electrodeposited from modified Watt’s baths. The properties of obtained coatings were compared to the nano-crystalline composite Ni/Al2O3 coatings prepared under the same plating conditions. The similarities and differences of the obtained coatings microstructures visible on both their surfaces and cross sections and determined properties were presented. The differences in the growth character of the Ni matrix and in the microstructural properties were observed. All electrodeposited Ni and Ni/Al2O3 coatings were compact and well adhering to the steel substrates. The thickness and the microhardness of the Ni and Ni/Al2O3 deposits increased significantly with the current density in the range 2 - 6 A/dm2. Residual stresses are tensile and they reduced as the current density increased. The composite coatings revealed better protection from the corrosion of steel substrate than pure nickel in solution 1 M NaCl.