1
Content available Effect of Nb and Mo Addition on the Microstructure and Wear Behavior of Fe-Cr-B Based Metamorphic Alloy Coating Layer Manufactured by Plasma Spray Process
Cho Yong-Hoon, Ham Gi-Su, Park So-Yeon, Kim Choongnyun Paul, Lee Kee-Ahn
Archives of Metallurgy and Materials
|
2022
|
Vol. 67, iss. 4
1521--1524
EN
Fe-Cr-B-based metamorphic alloy coating layers were manufactured by plasma spray with a Fe-Cr-B-Mo-Nb composition (hereinafter, M+) powder. The microstructure and wear properties of the coating layers were investigated and compared with a metamorphic alloy coating layer fabricated with commercial m material. XRD analysis revealed that the M and M+ coating layers were composed of α-Fe, (Cr, Fe)2B, and some metallic glass phases. Wear test results showed that M+ coating layers had a superior wear resistance which had 1.48 times lower wear volume than M coating layers. Observations of the worn-out surfaces and cross-sections of the coating layers showed that M+ coating layer had relatively low oxides along the particle boundaries and it suppress a delamination behavior by the oxides.
2
Content available remote Wpływ dodatków stopowych na temperaturę krzepnięcia staliwa austenitycznego
Garbiak M.
Archiwum Technologii Maszyn i Automatyzacji
|
2008
|
Vol. 28, nr 3
35-40
PL
W artykule przedstawiono wyniki badań, których celem była ocena wpływu niobu, tytanu i krzemu na wartość temperatury początku i końca krzepnięcia staliwa austenitycznego typu 0,3 C--30Ni-18Cr. Metodą ATD rejestrowano krzywe krzepnięcia 15 stopów zawierających 0,03÷3% Nb, 0,03÷5-1,4% Ti oraz 1,6÷4,3% Si. Wykazano, że badane składniki stopowe zwiększają zakres temperaturowy i wydłużają czas krzepnięcia. W stopach z górną zawartością wprowadzonych pierwiastków rejestrowano dwa przystanki temperaturowe i tworzenie się dodatkowego składnika fazowego w mikrostrukturze stopów.
EN
The paper presents the results of research on TDA cooling curves of austenitic cast steel 30Ni-18Cr with niobium, titanium and silicon. The liquidus and the end of solidification temperature were determined for 15 experimental alloys in which the content of alloying elements varied in a range of 0.03-3% Nb, 0.03-1.4% Ti and 1.6÷4.3% Si. It has been found that all the alloying additions decrease the liquidus and end of solidification temperature and they cause an enlargement of the solidification interval. For alloys of the highest total content of Nb, Ti and Si the second temperature arrest on TDA curve was recorded and simultaneously G phase precipitates have been observed in the microstructure.
3
Content available remote Fracture toughness of stabilised 0.3%C-30%Ni-18%Cr cast steel
Garbiak M.
Archiwum Technologii Maszyn i Automatyzacji
|
2007
|
Vol. 27, nr 1
27-32
EN
The effect of niobium, titanium and silicon additions on fracture behaviour of 0.3%C-30%Ni--18%Cr cast steel after annealing for 300 hrs at a temperature of 900°C has been investigated. The Charpy test results showed that the presence of Nb/Ti in chemical composition in combination with silicon reduces the fracture toughness of cast steel at room temperature and at 900°C.
PL
W artykule omówiono badania wpływu dodatków niobu, tytanu i krzemu na udarność staliwa 0,3%C-30%Ni-18% Cr po wyżarzaniu w temperaturze 900°C w czasie 300 godzin. Wyniki pomiaru udarności wykazały, że badane pierwiastki zmniejszają udarność staliwa zarówno w temperaturze pokojowej, jak i w temperaturze 900°C.
4
Content available remote Elektrochemiczne roztwarzanie stabilizowanego staliwa austenitycznego
Chylińska R., Piekarski B.
Archiwum Technologii Maszyn i Automatyzacji
|
2007
|
Vol. 27, nr 1
113-120
PL
W artykule przedstawiono wyniki pomiarów, których celem było wyizolowanie faz międzymetalicznych ze stabilizowanego staliwa typu 0,3C-30Ni-18Cr za pomocą ekstrakcji elektrolitycznej. Jakość prowadzonych procesów oceniono na podstawie ilości otrzymywanego izolatu, jego składu fazowego oraz bilansu masowego produktów ekstrakcji.
EN
The paper presents the results of measurement aimed at isolating the phases of stabilised cast steel 0.3C-30Ni-18Cr during electrolytical extraction. The quality of the conducted process was evaluated on the base of the quantity of received residues, his phase constitution and mass balance of the extraction products.