Corrosion and corrosion fatigue behaviour of Al-bronze in LiBr solutions

Youssef G. I., Shehata M. F., Meleigy A. E., Warraky A. A., Aziz A. M. A.

Ochrona przed Korozją

2013

nr 2

34--38

The corrosion behaviour of Al-bronze in LiBr solution was investigated by means of solution analysis, potentiodynamic cyclic polarization, and surface examination. It was found that the dissolution of the alloy at lower concentrations of LiBr (0.25 M) was mainly general due to the formation of CuBr and/or Cu2O. By increasing the concentration of LiBr (≥ 0.5 M) the predominant species were CuO, Cu(OH)2 and CuBr2 • 3Cu(OH)2, CuLiO phase in addition to Al2O3, which is more passive, while the corrosion form was mainly pitting. The corrosion fatigue results proved that both the fatigue life and fatigue strength deteriorated as the LiBr concentration increased. Phractographic examinations revealed a shift of fracture mode from transgranular in air to a mixed mode of transgranular and intergranular with an increasing percentage of intergranular as the LiBr concentration increased. The above results indicate that the failure was due to the action of a mechanochemical mechanism.

Właściwości korozyjne brązu aluminiowego w roztworze LiBr badano za pomocą analizy roztworu, cyklicznej polaryzacji potencjodynamicznej i analizy powierzchni. Stwierdzono, że przy mniejszym stężeniu roztworu LiBr (0,25 M) roztwarzanie stopu zachodzi z wytworzeniem głównie CuBr i/lub Cu2O. Zwiększenie stężenia Libr (≥ 0,5 M) powoduje korozję wżerową na skutek utworzenia się pasywnej warstwy składającej się przede wszystkim z CuO, Cu(OH)2, CuBr2 • 3Cu(OH)2 i fazy CuLiO. Badania zmęczeniowe wykazały, że zarówno trwałość, jak i wytrzymałość zmęczeniowa zmniejszają się ze wzrostem stężenia LiBr. Badania fraktograficzne ujawniły zmianę rodzaju pęknięć z śródkrystalicznych w powietrzu na mieszane śródkrystaliczne i międzykrystaliczne, aż do międzykrystalicznych, w miarę wzrostu stężenia LiBr. Wyniki badań wskazują na mechanochemiczny mechanizm powstawania pęknięć.

Potentiometric determination of molybdate ions

Youseff G. I.

Ochrona przed Korozją

2012

nr 7

298-301

Molybdates are one of the recently developed corrosion inhibitors for cooling systems. This paper present a simple and accurate metohod for molybdate analysis with these systems, based on the potentiometric titration of molybdate with lead acetate, using molybdenum, lead and molybdenum-containing alloys as indicator electrodes. At the equivalnet poin, a rapid jump of the potential of the indicator electrode relative to the reference calomel electrode takes place indicatin complete precitipation of the present molybdate in the form of lead molybdate. The results show a linear relationship beteen volumes of molybdate and the consumed acetate with equimolat concentrations. Bimetallic electrodes have been also used in following the titration reaction, wit no need to aplly a reference electrode. The method is applicable in the presence of the constituents of cooling water and the corrosion products of the main materials used in the contruction of cooling systems. It is also aplicable in LiBr containing cooling system.

Molibdeniany należą do jednych z najnowszych inhibitorów korozji stosowanych w układach chłodzenia. Zaprezentowano prostą i dokładną metodę analizy molibdenianów w takich układach, opartą na miareczkowaniu potencjometrycznym molibdenianu za pomocą octanu ołowiu z użyciem, jako elektrod wskaźnikowych, molibdenu, ołowiu i stopów zawierających molibden. W punkcie równoważnikowym następuje gwałtowny skok potencjału elektrody wskaźnikowej względem kalomelowej elektrody odniesienia wskazujący całkowite osadzenie się molibdenianu w postaci molibdenianu ołowiu. Wyniki wskazują na liniową zależność między ilością molibdenianu a zużytym octanem o stężeniach równomolarnych. Do miareczkowania zastosowano również elektrody bimetaliczne, co wyeliminowało konieczność użycia elektrody odniesienia. Metoda nadaje się do stosowania w obecności składników wody chłodzącej i produktów korozji podstawowych materiałów stosowanych w układach chłodzenia. Można ją również stosować w układach chłodzenia zawierających LiBr.