Effect of surface modification of LaNi4.5Co0.5 active material on electrochemical parameters of hydride electrode in conditions of long-lasting cycling

Stefaniak A., Bordolińska K., Sozańska M.

Ochrona przed Korozją

|

2016

|

nr 9

330--333

EN

The analysis of galvanostatic charge/discharge curves for the hydrogen powder electrode in long-term cycling conditions (N = 40 cycles) is presented. The surface of active powder (LaNi4.5Co0.5; fraction 20÷50 μm) has been modified by 8-hours magnetron sputtering using Fe-Si target. The effect of deposition of thin Fe-Si layers on functional parameters of modified electrode has been characterized. It has been shown that magnetron sputtering scarcely affects electrode discharge capacity, but it decreases a little the slope of rectilinear segment of logQdisch = f(N) relationship, thus, inhibits the corrosion degradation of the electrode. For N > 22 cycles hydride capacity of modified electrode reaches practically constant level, close to 270 mAh/g, which testifies to disappearance of corrosion degradation. The sputtered layers improve the kinetics of hydrogen electrosorption because their presence increases exchange current density of H2O/H2 system.

PL

Dokonano analizy krzywych galwanostatycznego ładowania/rozładowania dla wodorkowej elektrody proszkowej w warunkach długotrwałego cyklowania (N = 40 cykli). Powierzchnię proszku aktywnego (LaNi4.5Co0.5; frakcja 20÷50 μm) modyfikowano poprzez 8-godzinne rozpylanie jonowe stopu Fe-Si stanowiącego target. Scharakteryzowano wpływ osadzania cienkich warstw Fe-Si w zależności od parametrów użytkowych zmodyfikowanej elektrody. Pokazano, że proces rozpylania ma niewielki wpływ na pojemność rozładowania, jednak zmniejsza nieco nachylenie odcinka prostoliniowego zależności logQrozł = f(N), tym samym hamuje degradację korozyjną elektrody. Dla N > 22 cykli pojemność wodorkowa elektrody modyfikowanej osiąga praktycznie stały poziom, ok. 270 mAh/g, co świadczy o zaniku degradacji korozyjnej. Warstwy napylone poprawiają również kinetykę elektrosorpcji wodoru, gdyż w ich obecności zwiększa się gęstość prądu wymiany układu H2O/H2.

2

Effect of magnetron sputtering of active powder with Fe-Cr-Ni layers on electrochemical parameters of metal hydride electrode

Bordolińska K., Stefaniak A., Bala H.

Ochrona przed Korozją

|

2016

|

nr 2

43--45

EN

Particles of hydrogen storage, LaNi4.5Co0.5 powdered material have been encapsulated with thin (about 40 nm) Fe-Cr-Ni layers using magnetron sputtering method. The acid resistant, 1.4301 (EN 10088) stainless steel has been applied as a target. The effect of powder encapsulation on galvanostatic charge/discharge characteristics (hydride capacity, exchange current density of the H2O/H2 system, susceptibility to oxidation) for the modified hydride electrodes has been evaluated. The plots of discharge curves testify to limitation of active material tendency to working surface development. The material modified reveals comparatively high discharge capacities which should be attributed to inhibition of oxidation processes of active material by the surface layers formed. The powder sputtering does not worsen the kinetics of charge/discharge processes for modified electrode.

PL

Cząstki proszku materiału wodorochłonnego LaNi4,5Co0,5 enkapsulowano cienkimi (ok. 40 nm) warstwami Fe-Cr-Ni poprzez napylanie magnetronowe, z użyciem stali kwasoodpornej 1,4301 (EN 10088) jako targetu. Oceniono wpływ enkapsulacji proszku na parametry galwanostatycznego procesu ładowania/rozładowania (pojemność wodorkowa, gęstość prądu wymiany układu H2O/H2, podatność na utlenianie) dla zmodyfikowanej w ten sposób elektrody wodorkowej. Przebieg krzywych rozładowania wskazuje, iż po procesie enkapsulacji zmniejsza się podatność materiału aktywnego na rozwijanie powierzchni roboczej. Materiał enkapsulowany wykazuje stosunkowo wysokie pojemności rozładowania, co jest konsekwencją hamowania procesów utleniania materiału aktywnego przez wytworzone warstwy. Napylanie proszku nie pogarsza kinetyki procesów ładowania/rozładowania zmodyfikowanej elektrody.

3

Effect of cycling on oxidation/reduction time periods of hydride electrode active material

Bordolińska K., Bala H.

Ochrona przed Korozją

|

2014

|

nr 7

252--254

EN

The effects of cycling on LaNi4.5Co0.5 hydrogen storage material oxidation (during electrode discharge) and reduction of its corrosion products (during charge process) are discussed. The time periods of the Ni and Co oxidation considerably decrease, whereas corresponding oxide phases reduction somewhat increase with electrode cycling. As a result, material corrosion rate increases with cycling with apparent tendency to settle down for final cycles.

PL

Dyskutowany jest wpływ cyklowania materiału wodorochłonnego LaNi4.5Co0.5 na jego utlenianie (podczas rozładowywania elektrody) i redukcję powstałych (podczas procesu ładowania) produktów korozji. Przedziały czasu odpowiadające utlenianiu Ni i Co maleją wyraźnie, natomiast czasy redukcji odpowiednich faz tlenkowych wzrastają w niewielkim stopniu wskutek cyrklowania elektrody. W efekcie, szybkość korozji materiału wzrasta z numerem cyklu, z pewną tendencją do ustalenia na stałym poziomie dla cykli końcowych.

4

Wpływ warunków ładowania katodowego na efektywność pochłaniania wodoru przez kompozytową elektrodę proszkową LaNi5

Giza K., Bala H.

Ochrona przed Korozją

|

2011

|

nr 7

390-393

PL

Scharakteryzowano zdolność do pochłaniania wodoru przez kompozyt proszkowy LaNi5, przy dwu wybranych gęstościach prądu katodowego i zachowaniu tej samej gęstości ładunku. Galwanostatyczne pomiary ładowania/ rozładowania wskazują zarówno na wzrost gęstości prądu wymiany jak i na wzrost efektywności pochłaniania wodoru przez kompozyt proszkowy LaNi5 jako skutek cyklowania. Największa pojemność rozładowania kompozytowej elektrody proszkowej LaNi5 wynosi około 39 mAźh/g dla prądu ładowania 0,5C, co stanowi 10% wartości teoretycznej.

EN

The hydrogen absorption ability of LaNi5 powder composite at two cathodic current densities with the same amount of total charge density have been investigated. The galvanostatic charge/ discharge measurements indicate both on the increase of the exchange current density and on the increase of the hydrogen absorption efficiency of LaNi5 powder composite with cycling. The highest discharge capacity of LaNi5 powder composite is about 39 mAźh/g at 0.5C charge current, which is 10% of the theoretical value.

5

Ocena stopnia degradacji korozyjnej ujemnej elektrody ogniwa NiMH w oparciu o galwanostatyczne krzywe ładowania/rozładowania

Kukuła I., Bala H.

Ochrona przed Korozją

|

2011

|

nr 7

494-496

PL

W pracy wykonano cykliczne galwanostatyczne krzywe ładowania/rozładowania dla kompozytowej elektrody proszkowej LaNi5 + Ni spajanej żywicą termoutwardzalną. Przebieg chronopotencjometrycznych krzywych katodowych umożliwił ocenę stopnia rozwinięcia powierzchni wywołanego wodorowanie i umożliwił wskazanie kolejnych etapów redukcji faz tlenkowych materiału elektrody. Pokazano, że w cyklu rozładowania utlenieniu ulega ok. 1% materiału elektrody.

EN

Cyclic galvanostatic charge/discharge curves for LaNi5 + Ni - powder, thermo-setting epoxy-resin bonded composite electrode have been measured in the present paper. Plots of the cathodic chronoammetric curves allowed evaluation of electrode surface development as a result of hydrogenation and indicated consecutive stages of reduction of electrode material oxide phases. It has been shown that ca 1% of electrode material undergo oxidation during discharge cycle.