Possibility of obtaining lanthanum doped nickel coatings from baths based on deep eutectic solvents

Niciejewska Anna, Tylus Włodzimierz, Marczewski Marek, Winiarska Katarzyna, Szczygieł Bogdan, Winiarski Juliusz

Ochrona przed Korozją

2022

nr 11

344--349

Lanthanum-doped nickel coatings were obtained from the bath based on a deep eutectic solvent: choline chloride and propylene glycol, mixed in a molar ratio of 1 : 2, and 0.2 mol dm−3 NiCl2 ∙ 6H2O and 0.5 mol dm−3 LaCl2 ∙ xH2O. The morphology, topography and chemical composition were examined. The lanthanum content in the coating was determined to be 1.7 wt. % using the ICP-MS method. Lanthanum on the surface was mainly in the form of lanthanum carbonate. The obtained coating was exposed to a 7-day exposure in 0.05 mol dm−3 NaCl solution. The coating showed the highest corrosion resistance (Rp ~ 30 kΩ cm2) after 15 hours of exposure to the NaCl solution.

Powłoki niklowe domieszkowane lantanem zostały otrzymane z kąpieli na bazie rozpuszczalnika eutektycznego chlorku choliny i glikolu propylenowego zmieszanych w proporcjach molowych 1 : 2 oraz 0,2 mol dm−3 NiCl2 ∙ 6H2O i 0,5 mol dm−3 LaCl2 ∙ xH2O. Zbadano morfologię, topografię oraz skład chemiczny. Zawartość lantanu w powłoce została określona na 1,7% mas. techniką ICP-MS. Na powierzchni powłoki lantan występował głównie w postaci węglanu lantanu. Otrzymana powłoka została poddana 7-dniowej ekspozycji w 0,05 mol dm−3 roztworze NaCl. Największą odporność na korozję powłoki stwierdzono po 15-godzinnej ekspozycji w roztworze NaCl.