Leaching of vanadium(V) from the mixture after potassium metavanadate synthesis based on KCl and spent vanadium catalyst

Kiełkowska U., Białowicz K., Drużyński S.

Polish Journal of Chemical Technology

2013

Vol. 15, nr 4

33-35

The results of the leaching of vanadium(V) from the mixture after potassium metavanadate synthesis from KCl and spent vanadium catalyst in the presence of steam were presented. Spent vanadium catalyst was obtained from the waste storage of a chemical plant producing sulfuric acid(VI) by the contact method. The reaction mixture was leached using different solutions: 1 M Na2CO3, 20% CO(NH2)2, 15% NaOH, 15% KOH, 2 M H2SO4. The effect of time and temperature was studied. The results showed that for reaction mixture leached for 4 h at 303 K in the presence of 15% sodium hydroxide solution at a liquid:solid ratio of 10:1, the extent of leaching of vanadium(V) was 95.43%.

Eksperymentalne wyznaczenie optymalnych parametrów syntezy KVO3 z V2O5 i KCl w obecności tlenu z powietrza

Trypuć M., Białowicz K., Mazurek K., Kiełkowska U.

Przemysł Chemiczny

2005

T. 84, nr 2

97-100

Podjęto badania nad ustaleniem wpływu parametrów syntezy KVO3 z KCl i V2O5 w obecności tlenu z powietrza. Zbadano wpływ takich parametrów jak temperatura, czas syntezy, szybkość przepływu powietrza przez reaktor, nadmiar chlorku potasu oraz obecność piasku kwarcowego jako nośnika mieszaniny reakcyjnej, na wydajność badanej syntezy KVO3.

At 873 K, the reaction 4KCl + 2 V2O5 + O2 = 4 KVO3 + 2Cl2 gave KVO3 in 59.44% yield in 4 h at air flow rate 181.5 cm3/ min and KCl used in 50% excess over V2O5. Quartz sand, 0.25–0.355 mm, added as a reaction mixt. carrier, 100% of the overall reaction mass, raised the yield to 89.08%.