Influence of vacuum brazing temperature on the microstructure of an Inconel 783 superalloy joint with a honeycomb sealing made of Hastelloy X superalloy

Krystek Kamil, Dul Irena, Motyka Maciej

Welding Technology Review

2019

R. 91, nr 9

27--37

The purpose of this work was to assess the influence of brazing temperature on microstructure of the cobalt-based Inconel 783 superalloy joint with nickel-based Hastelloy X superalloy ‒ seal shaped in honeycomb structure. Brazing process was combined with solution heat treatment of Inconel 783 in one operation. Nickel based brazing filler metal from BNi-2 group was used. Tests were conducted in 1121 °C (solutionizing temperature), 1075 °C and 1030 °C in 1 hour. Subsequently, metallographic investigations were made using optical and scanning electron microscopes, mainly focused on changes in a seal made of Hastelloy X, where joint erosion in higher temperature was observed.

Celem niniejszej pracy była ocena wpływu temperatury lutowania na mikrostrukturę złącza obudowy turbiny z nadstopu kobaltu Inconel 783 z uszczelnieniem o strukturze plastra miodu z nadstopu niklu Hastelloy X. Procesy lutowania i przesycania nadstopu Inconel 783 prowadzono łącznie - w jednej operacji technologicznej. Zastosowano lutowie niklowe z grupy BNi-2. Złącza wykonano w temperaturze 1121°C (przesycania), 1075 °C, 1030 °C w czasie 1 godziny. Następnie przeprowadzono obserwacje mikrostruktury złącza metodami mikroskopii świetlnej i elektronowej skaningowej, ze szczególnym uwzględnieniem zmian zachodzących w materiale uszczelnienia ze stopu Hastelloy X, w którym obserwowano zjawisko erozji złącza w górnym przedziale stosowanej temperatury lutowania.