A method was developed to obtain a durable coating consisting of zinc and graphene oxide (Zn-GO) in order to reduce the mechanical wear and tear rate of oil and gas pipelines made of steel. Graphene oxide was obtained from graphite by wet chemical oxidation (unmodified and modified Hummers’ method) using potassium permanganate and sulfuric acid. The process was carried out at various temperatures. The steel was covered with an ultrathin layer of Zn-GO using the electrophoretic deposition method. The GO particle size (< 90 nm) was confirmed by XRD and laser analysis. For GO particles obtained by the modified Hummers’ method, a significant correlation was observed in the scratch (R2 = 0.87) and the Vickers microhardness tests (R2 = 0.93), which indicates a lower wear rate of Zn-GO-coated steel.
PL
Opracowano metodę otrzymywania trwałej powłoki składającej się z cynku i tlenku grafenu (Zn-GO) w celu zmniejszenia zużycia mechanicznego rurociągów naftowo-gazowych wykonanych ze stali. Tlenek grafenu pozyskano z grafitu metodą mokrego utleniania chemicznego (niezmodyfikowana i zmodyfikowana metoda Hummersa) z użyciem nadmanganianu potasu i kwasu siarkowego. Proces prowadzono w różnej temperaturze. Stal powlekano ultra cienką warstwą Zn-GO techniką osadzania elektroforetycznego. Metodą XRD i analizą laserową potwierdzono wielkość cząstek GO (≤ 90 nm). Dla cząstek GO otrzymanych zmodyfikowaną metoda Hummersa zaobserwowano znaczącą korelację w teście zarysowania (R2 = 0.87) i mikrotwardości Vickersa (R2 = 0.93), co świadczy o mniejszym stopniu zużycia stali pokrytej powłoką Zn-GO.
2
Dostęp do pełnego tekstu na zewnętrznej witrynie WWW
Graphene, a carbon allotrope, became a significant area of research with its superior electrical, mechanical, optical properties, etc. There are several methods to obtain graphene oxide from graphite, one of which is the Hummers method. In this study, several modifications and pre-treatments preceding the Hummers method have been employed. Three different graphene oxide fibers have been produced by three different procedures, i.e. fibers obtained by Hummers method with pre-oxidation step, modified Hummers method and modified Hummers method with pre-oxidation step. It has been observed that pre-oxidation has a significant effect on graphene oxide fiber properties produced by wet spinning process (coagulation). Modified Hummers method without pre-oxidation leads to the highest breaking strength and breaking elongation. Reduced fiber linear density, breaking strength and breaking elongation together with increased crimp were observed in graphene fiber due to the addition of pre-oxidation step.
JavaScript jest wyłączony w Twojej przeglądarce internetowej. Włącz go, a następnie odśwież stronę, aby móc w pełni z niej korzystać.