The influence of interrupting the brazing process of Hastelloy X superalloy on the properties of the joint

Krystek Kamil

Zeszyty Naukowe Politechniki Rzeszowskiej. Mechanika

|

2021

|

z. 93 [302]

31--40

EN

In this paper, disruption of brazing process impact on behavior of filler metal and properties of the joint was investigated. Hastelloy X sheet samples were brazed using Ni-13Cr-4Fe-4Si-2,7B filler alloy. Two identical sets of samples were heated in high vacuum, once load reached specified temperature process was interrupted. Subsequently, one set of samples was tested and second set was subjected to rebrazing in proper time and temperature, dedicated for used filler material. Disruption of the process in following temperature was analyzed: 930, 960, 1050, 1127, 1145, 1170°C. After both processes macroscopic observations of joint, peel test, static tensile test and spreadability analysis were carried out.

2

Influence of vacuum brazing temperature on the microstructure of an Inconel 783 superalloy joint with a honeycomb sealing made of Hastelloy X superalloy

Krystek Kamil, Dul Irena, Motyka Maciej

Welding Technology Review

|

2019

|

R. 91, nr 9

27--37

EN

The purpose of this work was to assess the influence of brazing temperature on microstructure of the cobalt-based Inconel 783 superalloy joint with nickel-based Hastelloy X superalloy ‒ seal shaped in honeycomb structure. Brazing process was combined with solution heat treatment of Inconel 783 in one operation. Nickel based brazing filler metal from BNi-2 group was used. Tests were conducted in 1121 °C (solutionizing temperature), 1075 °C and 1030 °C in 1 hour. Subsequently, metallographic investigations were made using optical and scanning electron microscopes, mainly focused on changes in a seal made of Hastelloy X, where joint erosion in higher temperature was observed.

PL

Celem niniejszej pracy była ocena wpływu temperatury lutowania na mikrostrukturę złącza obudowy turbiny z nadstopu kobaltu Inconel 783 z uszczelnieniem o strukturze plastra miodu z nadstopu niklu Hastelloy X. Procesy lutowania i przesycania nadstopu Inconel 783 prowadzono łącznie - w jednej operacji technologicznej. Zastosowano lutowie niklowe z grupy BNi-2. Złącza wykonano w temperaturze 1121°C (przesycania), 1075 °C, 1030 °C w czasie 1 godziny. Następnie przeprowadzono obserwacje mikrostruktury złącza metodami mikroskopii świetlnej i elektronowej skaningowej, ze szczególnym uwzględnieniem zmian zachodzących w materiale uszczelnienia ze stopu Hastelloy X, w którym obserwowano zjawisko erozji złącza w górnym przedziale stosowanej temperatury lutowania.

3

Microstructure and Properties of a Repair Weld in a Nickel Based Superalloy Gas Turbine Component

Rakoczy Ł., Grudzień M., Tuz L., Pańcikiewicz K., Zielińska-Lipiec A.

Advances in Materials Science

|

2017

|

Vol. 17, nr 2(52)

57--63

EN

The aim of the present study was to characterize the repair weld of serviced (aged) solid-solution Ni-Cr-Fe-Mo alloy: Hastelloy X. The repair welding of a gas turbine part was carried out using Gas Tungsten Arc Welding (GTAW), the same process as for new parts. Light microscopy, scanning electron microscopy, transmission electron microscopy, microhardness measurements were the techniques used to determine the post repair condition of the alloy. Compared to the solution state, an increased amount of M6C carbide was detected, but M23C6 carbides, sigma and mu phases were not. The aged condition corresponds to higher hardness, but without brittle regions that could initiate cracking.

4

Mikrostruktura i własności złączy naprawczych wykonanych na stopie Hastelloy X przed i po eksploatacji w turbinie gazowej

Rakoczy Ł., Zielińska-Lipiec A., Tuz L.

Przegląd Spawalnictwa

|

2016

|

R. 88, nr 4

54--56

PL

Przedmiotem badań były złącza spawane ze stopu niklu umacnianego roztworowo o nazwie handlowej Hastelloy X. Proces spawania przeprowadzono metodą GTAW (z ang. Gas Tungsten Arc Welding) na materiale w stanie dostawy oraz po eksploatacji tj. pochodzącym z turbiny gazowej. W celu porównania zmian mikrostrukturalnych i własności wykonano badania za pomocą mikroskopii świetlnej, skaningowej oraz pomiary mikrotwardości. Dodatkowo przeprowadzono badania za pomocą transmisyjnej mikroskopii elektronowej (TEM) w obszarze materiału rodzimego po eksploatacji. Wykonane badania TEM były podstawą do stwierdzenia, iż temperatura eksploatacji wpłynęła jedynie na zwiększenie ilości i średnicy wydzieleń węglików typu M6C, natomiast temperatura eksploatacji leżała poza zakresem wydzielania faz wtórnych węglików typu M23C6 i faz topologicznie zwarcie wypełnione σ lub μ. Hastelloy X w stanie przesyconym charakteryzuje się bardzo dobrą spawalnością, jednakże może ona ulec obniżeniu w wyniku obecności kruchych i niskotopliwych faz powstałych w trakcie eksploatacji.

EN

The aim of the present study was to characterize repair welds performed on solid solution strengthened nickel-based superalloy also known Hastelloy X. The welding process was performed using GTAW. Process was carried out on materials in solid solution condition (unaged state) and after long term service in gas turbine. In order to compare microstructural changes and properties of welds light microscopy, scanning electron microscopy and microhardness measurements were performed. Additionally, transmission electron microscopy (TEM) of the base material after long term service was carried out. TEM study was the basis for the conclusion that the operating temperature had an impact on increase the amount and diameter of M6C-type carbides. Operating temperature of the turbine part was too low to contribute to the precipitation of M23C6- type carbides and topologically closed packed phases σ and μ. Alloy in solid solution condition has excellent weldability but precipitation of brittle and low melting temperature constituents during service may affect the tendency to cracking.