The inﬂuence of ageing process on microstructure of GP91 cast steel

Opydo M., Golański G., Dudek A., Jasak J., Mroziński S.

Inżynieria Materiałowa

2013

Vol. 34, nr 4

336--340

The study aim is to determine the effect of ageing at 550°C and time up to 6000 h on the changes in microstructure of GX12CrMoVNbN9-1 (GP91) cast steel. A detailed microstructural study and analysis of the secondary phases was carried out using scanning and transmition electron microscopy technique. The microstructural observations showed that the lath martensite microstructure was retained after 6000 h. The coarsening of M23C6 carbides and precipitates of Laves phase was observed. In addition, in the dislocation microstructure of the tested cast steel after ageing, the process of matrix recovery was observed, which appeared as an increase in the mean diameter of subgrains and a decrease in the density of dislocations. Moreover, the privileged precipitation of M23C6 carbides on grain boundaries as well as precipitation of the Laves phase was noted.

W pracy określono wpływ starzenia w temperaturze 550°C przez 6000 godzin na zmiany mikrostruktury staliwa GX12CrMoVNbN9-1 (GP91). Badania mikrostrukturalne oraz analiza faz wtórnych zostały przeprowadzone za pomocą skaningowego i transmisyjnego mikroskopu elektronowego. Przeprowadzone badania wykazały, że w stanie wyjściowym badane staliwo charakteryzuje się listwową mikrostrukturą martenzytu wysokodpuszczonego z licznymi wydzieleniami węglików M23C6 i MX. Po procesie starzenia mikrostruktura staliwa GP91 nadal charakteryzowała się listwową budową, chociaż obserwowano procesy zdrowienia i poligonizacji dyslokacyjnej osnowy, objawiające się wzrostem średniej średnicy podziaren i spadkiem gęstości dyslokacji. Stwierdzono ponadto uprzywilejowane wydzielanie węglików M23C6 po granicach ziaren oraz wydzielanie fazy Lavesa.

Effect of different heat treatments on microstructure and mechanical properties of the martensitic Gx12CrMoVNbN9-1 cast steel

Golański G., Słania J.

Archives of Metallurgy and Materials

2013

Vol. 58, iss. 1

25-30

The paper presents a research on the influence of multistage heat treatment with the assumed parameters of temperature and time on the microstructure and mechanical properties of high-chromium martensitic GX12CrMoVNbN9-1 (GP91) cast steel. In the as-cast state GP91 cast steel was characterized by a microstructure of lath martensite with numerous precipitations of carbides of the M23C6, M3C and NbC type, with its properties higher than the required minimum. Hardening of the examined cast steel contributes to obtaining a microstructure of partly auto-tempered martensite of very high strength properties and impact strength KV on the level of 9-15 J. Quenching and tempering with subsequent stress relief annealing of GP91 cast steel contributed to obtaining the microstructure of high-tempered lath martensite with numerous precipitations of the M23C6 and MX type of diverse size. The microstructure of GP91 cast steel received after heat treatment was characterized by strength properties (yield strength, tensile strength) higher than the required minimum and a very high impact energy KV. It has been proved that GP91 cast steel subject to heat treatment No. 2 as a result of two-time heating above the Ac3 temperature is characterized by the highest impact energy.

W pracy przedstawiono badania wpływu wieloetapowej obróbki cieplnej przy założonych parametrach temperaturowo - czasowych na mikrostrukturę i właściwości mechaniczne wysokochromowego, martenzytycznego staliwa GX12CrMoVNbN9-1(GP91). W stanie lanym staliwo GP91 charakteryzowało się mikrostruktura martenzytu listwowego z licznymi wydzieleniami węglików typu M23C6, M3C i NbC o właściwościach wyższych od wymaganego minimum. Hartowanie badanego staliwa przyczynia sie do uzyskania mikrostruktury częściowo samoodpuszczonego martenzytu, o bardzo wysokich właściwościach wytrzymałościowych i udarności KV na poziomie 9_15 J. Ulepszanie cieplne z następnym wyżarzaniem odprężającym staliwa GP91 przyczyniła się do uzyskania mikrostruktury listwowego martenzytu wysokoodpuszczonego, z licznymi, o zróżnicowanej wielkości wydzieleniami typu M23C6 i MX . Uzyskana droga obróbki cieplnej mikrostruktura staliwa GP91 charakteryzowała sie właściwościami wytrzymałościowymi (granica plastyczności, wytrzymałością na rozciąganie) wyższymi od wymaganego minimum i bardzo wysoka udarnoącią KV. Wykazano, ze staliwo GP91 poddane obróbce No. 2 w wyniku dwukrotnego nagrzewania powyżej temperatury Ac3 charakteryzuje się najwyższą udarnością.