Effect of Al and Ir additions on FeCrNi coating's surface morphology and topography

Kucharska B.

Inżynieria Materiałowa

2010

Vol. 31, nr 3

358-361

The morphology and roughness of FeCrNi coatings based on 310S heat-resisting steel enriched with Al and Ir. Coatings were deposited on a substrate of the same steel by the magnetron sputtering method. The investigation of surfaces was carried out using the scanning microscope and atomic force microscope. The roughness measurement along 12 ?m long sections and from areas up to 100 ?m2 was performed. It was found that the additions of Al and Ir had the effect of changing the morphology and reducing the size of crystallites. The addition of both 2.3% Al and 3.7% Ir reduces the coating roughness, respectively, by up to approx. 25 and 50% compared to the coating without additions. No relationship between roughness of coatings and their thicknesses was found.

W pracy przedstawiono wyniki badań morfologii i chropowatości powłok FeCrNi o składzie chemicznym stali żaroodpornej 310S, wzbogaconych dodatkami Al i Ir. Powłoki osadzono metodą magnetronowego rozpylania na stalowym podłożu. Powierzchnię powłok badano za pomocą elektronowego mikroskopu skaningowego oraz mikroskopu sił atomowych. Pomiar chropowatości wykonano na odcinku 12 um i na obszarach o powierzchni do 100 um2. Stwierdzono, że dodatki Al i Ir zmieniają morfologię powłoki i powodują rozdrobnienie krystalitów. Zarówno dodatek 2,3% Al, jak i 3,7% Ir zmniejszają chropowatość powłoki odpowiednio do ok. 25 i 50% chropowatości powłoki bez dodatków. Nie stwierdzono zależności pomiędzy chropowatością powłok a ich grubością.