Density profile and hardness of thermo-mechanically modified beech, oak and pine wood

Laskowska Agnieszka

Drewno : prace naukowe, doniesienia, komunikaty

2020

vol. 63, nr 205

25--41

Beech (Fagus sylvatica L.), oak (Quercus robur L.) and pine (Pinus sylvestris L.) wood were volume-densified by means of thermo-mechanical modification. At first stage the wood was heated in a hydraulic press at temperature 100°C for 720 s, and then one-step densified in order to obtain the target thickness. The wood was cooled in a hydraulic press with unheated plates. Density profiles parallel and perpendicular to the grain were examined. The analysis of the density profiles was carried out on the basis of the following parameters: mean density, minimum to mean density ratio, maximum density, and the distance between the maximum density area and the wood surface. Wood hardness was determined according to the Brinell method. Volume-densified pine wood was characterized by considerably lower susceptibility to densification than beech or oak wood. Densified beech wood had the highest mean density 921 ±7 kg/m3, and the highest maximum density 968 ±12 kg/m3. The Brinell hardness of densified beech, oak and pine wood was twice as high as before the densification. The greatest hardness after the densification 78.60 ±10.56 N/mm2 was observed in beech wood.

Assessment of compressive strength and compressive modulus parallel to the grain of oak and tauari wood after thermo-mechanical modification

Laskowska A.

Annals of Warsaw University of Life Sciences - SGGW. Forestry and Wood Technology

2018

No. 103

70--76

European oak and tauari wood were subjected to thermomechanical modification. One treatment cycle consisted of three stages: heating the wood in a hydraulic press; wood densification; and cooling the wood samples in unheated hydraulic press without exerting pressure. The treatment temperature was 100 °C or 150 °C. The modification temperature significantly affected the compressive strength parallel to the grain of oak and tauari wood. Such dependencies were not found in the case of compressive modulus of elasticity parallel to the grain of tested wood species. The compressive strength of tauari wood modified at 100 oC and 150 oC was, respectively, 16% and 20% greater than the compressive strength of oak wood modified at the same temperatures. The compressive strength parallel to the grain of the oak and tauari wood depended linearly on wood density and load.

Drewno dębu i tauari poddano obróbce termo-mechanicznej. W pierwszym etapie drewno ogrzewano kontaktowo w prasie hydraulicznej, następnie zagęszczano, po czym poddawano chłodzeniu w nieogrzewanej prasie hydraulicznej bez użycia ciśnienia. Temperatura półek prasy, przy której prowadzono proces zagęszczania drewna wynosiła 100°C lub 150°C. Temperatura obróbki wykazała istotny wpływ na wytrzymałość na ściskanie wzdłuż włókien drewna dębu i tauari. Zależności tych nie stwierdzono w przypadku modułu przy ściskaniu wzdłuż włókien badanych gatunków drewna. Wytrzymałość na ściskanie drewna tauari zagęszczanego w temperaturze 100°C i 150°C była odpowiednio o 16% i 20% wyższa niż wytrzymałość na ściskanie drewna dębu modyfikowanego w tych samych temperaturach. Wytrzymałość na ściskanie wzdłuż włókien drewna dębu i tauari zależała liniowo od gęstości drewna i obciążenia wywieranego na próbkę.